Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_2955416_7WdZPu.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 22.29 T-atoms per nm^3
Material density = 2.224 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O3  = 1.6792 Angstrom
T1  -- O4  = 1.6682 Angstrom
T1  -- O1  = 1.5341 Angstrom
T1  -- O2  = 1.6301 Angstrom
      mean = 1.6279 Angstrom
        t1 = 0.082412  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.079809  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6620 Angstrom
T2  -- O4  = 1.6727 Angstrom
T2  -- O5  = 1.6041 Angstrom
T2  -- O6  = 1.5488 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.067948  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044500  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5341 A <--> 1.6792 A
          Mean   = 1.6249 A
          StdDev = 0.0542 A

       t1 Range  = 0.0679 <-- 0.0752 --> 0.0824
       t2 Range  = 0.0445 <-- 0.0622 --> 0.0798

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O3  -- T1  -- O4  = 125.675 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  =  95.619 deg; O3  -- O1  = 2 A
O3  -- T1  -- O2  = 116.415 deg; O3  -- O2  = 3 A
O4  -- T1  -- O1  =  97.248 deg; O4  -- O1  = 2 A
O4  -- T1  -- O2  = 109.980 deg; O4  -- O2  = 3 A
O1  -- T1  -- O2  = 106.171 deg; O1  -- O2  = 3 A
       95.619 deg <-- 108.518 deg --> 125.675 deg

O3  -- T2  -- O4  = 126.469 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 104.766 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  97.364 deg; O3  -- O6  = 2 A
O4  -- T2  -- O5  = 111.916 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 102.317 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 113.071 deg; O5  -- O6  = 3 A
       97.364 deg <-- 109.317 deg --> 126.469 deg

        O-T-O SUMMARY
          Range  = 95.6190 deg <--> 126.4695 deg
          Mean   = 108.8536 deg
          StdDev = 10.4139 deg

        O--O SUMMARY
          Range  = 2.3828 A <--> 2.9782 A
          Mean   = 2.6422 A
          StdDev = 0.2075 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O3  - T1  - O4  - T1  =  99.749 deg; T2  -- T1  = 4.7939 A
T2  - O3  - T1  - O1  - T2  = 151.885 deg; T2  -- T2  = 6.0475 A
T2  - O3  - T1  - O2  - T1  = 102.143 deg; T2  -- T1  = 5.0367 A
T1  - O4  - T1  - O1  - T2  =  79.823 deg; T1  -- T2  = 3.8949 A
T1  - O4  - T1  - O2  - T1  = 108.789 deg; T1  -- T1  = 5.1324 A
T2  - O1  - T1  - O2  - T1  = 104.571 deg; T2  -- T1  = 4.9676 A

T1  - O3  - T2  - O4  - T2  = 115.556 deg; T1  -- T2  = 5.2673 A
T1  - O3  - T2  - O5  - T2  =  79.118 deg; T1  -- T2  = 3.8949 A
T1  - O3  - T2  - O6  - T1  = 152.807 deg; T1  -- T1  = 6.0594 A
T2  - O4  - T2  - O5  - T2  = 114.590 deg; T2  -- T2  = 5.3045 A
T2  - O4  - T2  - O6  - T1  =  89.760 deg; T2  -- T1  = 4.5320 A
T2  - O5  - T2  - O6  - T1  = 100.031 deg; T2  -- T1  = 4.8373 A

        T-T-T SUMMARY
          Range  = 79.1180 deg <--> 152.8067 deg
          Mean   = 108.7746 deg
          StdDev = 23.7853 deg

        T--T SUMMARY
          Range  = 3.8949 A <--> 6.0594 A
          Mean   = 4.9878 A
          StdDev = 0.6874 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 168.270 deg ; T1  -- T1   3.0522 A

T1  -- O2  -- T1  = 176.461 deg ; T1  -- T1   3.2586 A

T1  -- O3  -- T2  = 148.505 deg ; T1  -- T2   3.2158 A

T1  -- O4  -- T2  = 129.221 deg ; T1  -- T2   3.0182 A

T2  -- O5  -- T2  = 176.467 deg ; T2  -- T2   3.2069 A

T2  -- O6  -- T2  = 177.289 deg ; T2  -- T2   3.0967 A


        T-O-T SUMMARY
          Range  = 129.2213° <--> 177.2893 deg
          Mean   = 162.7023 deg
          StdDev = 18.2604 deg

        T--T SUMMARY
          Range  = 3.0182 A <--> 3.2586 A
          Mean   = 3.1414 A
          StdDev = 0.0914 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 11 23 46 76 113 163 212 273 347 427 510 596 703 813 925
TD10 = 1269
Circuit symbol = 4.5_{2}.5.8_{3}.5.8_{4}
Weight = 24
Vertex symbol  = 4.5_{2}.5.8.5.8_{2}
Weight = 24

<TD10> = 1269.000
Average ring size = 5.6140