Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_151_2_1439747_XgQerC.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 26.21 T-atoms per nm^3
Material density = 2.615 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5825 Angstrom
T1  -- O2  = 1.6156 Angstrom
T1  -- O3  = 1.6203 Angstrom
T1  -- O4  = 1.6550 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.042529  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046896  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6507 Angstrom
T2  -- O5  = 1.6267 Angstrom
T2  -- O6  = 1.5717 Angstrom
T2  -- O3  = 1.6410 Angstrom
      mean = 1.6225 Angstrom
        t1 = 0.038212  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029276  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5717 A <--> 1.6550 A
          Mean   = 1.6204 A
          StdDev = 0.0286 A

       t1 Range  = 0.0382 <-- 0.0404 --> 0.0425
       t2 Range  = 0.0293 <-- 0.0381 --> 0.0469

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 101.926 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 101.343 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 114.538 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.883 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.011 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.324 deg; O3  -- O4  = 3 A
       101.343 deg <-- 109.338 deg --> 114.538 deg

O4  -- T2  -- O5  = 113.731 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.977 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 114.770 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 103.550 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 111.761 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 105.881 deg; O6  -- O3  = 3 A
       103.550 deg <-- 109.278 deg --> 114.770 deg

        O-T-O SUMMARY
          Range  = 101.3429 deg <--> 114.7701 deg
          Mean   = 109.9052 deg
          StdDev = 4.7680 deg

        O--O SUMMARY
          Range  = 2.4775 A <--> 2.7726 A
          Mean   = 2.6549 A
          StdDev = 0.1012 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  95.844 deg; T1  -- T2  = 4.5677 A
T1  - O1  - T1  - O3  - T1  = 106.122 deg; T1  -- T1  = 4.9547 A
T1  - O1  - T1  - O4  - T2  = 139.600 deg; T1  -- T2  = 5.7183 A
T2  - O2  - T1  - O3  - T1  = 124.535 deg; T2  -- T1  = 5.4669 A
T2  - O2  - T1  - O4  - T2  = 109.410 deg; T2  -- T2  = 4.9547 A
T1  - O3  - T1  - O4  - T2  =  85.301 deg; T1  -- T2  = 4.1440 A

T1  - O4  - T2  - O5  - T2  =  85.307 deg; T1  -- T2  = 4.2061 A
T1  - O4  - T2  - O6  - T1  = 109.410 deg; T1  -- T1  = 4.9547 A
T1  - O4  - T2  - O3  - T2  = 139.254 deg; T1  -- T2  = 5.7919 A
T2  - O5  - T2  - O6  - T1  = 124.853 deg; T2  -- T1  = 5.4485 A
T2  - O5  - T2  - O3  - T2  = 104.788 deg; T2  -- T2  = 4.9547 A
T1  - O6  - T2  - O3  - T2  =  96.983 deg; T1  -- T2  = 4.5816 A

        T-T-T SUMMARY
          Range  = 85.3010 deg <--> 139.5997 deg
          Mean   = 110.0962 deg
          StdDev = 18.1932 deg

        T--T SUMMARY
          Range  = 4.1440 A <--> 5.7919 A
          Mean   = 4.9760 A
          StdDev = 0.5345 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.768 deg ; T1  -- T1   3.1107 A

T1  -- O2  -- T1  = 145.786 deg ; T1  -- T1   3.0883 A

T1  -- O3  -- T2  = 134.247 deg ; T1  -- T2   3.0047 A

T1  -- O4  -- T2  = 136.056 deg ; T1  -- T2   3.0657 A

T2  -- O5  -- T2  = 146.162 deg ; T2  -- T2   3.1127 A

T2  -- O6  -- T2  = 176.167 deg ; T2  -- T2   3.1415 A


        T-O-T SUMMARY
          Range  = 134.2469° <--> 176.1667 deg
          Mean   = 149.5308 deg
          StdDev = 14.5524 deg

        T--T SUMMARY
          Range  = 3.0047 A <--> 3.1415 A
          Mean   = 3.0872 A
          StdDev = 0.0442 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 30 52 80 116 156 204 258 318 384 458 536 622 714 812
TD10 = 1231
Circuit symbol = 6.6.6_{2}.6_{2}.8_{9}.8_{9}
Weight = 37
Vertex symbol  = 6.6.6_{2}.6_{2}.8_{7}.8_{7}
Weight = 37

<TD10> = 1231.000
Average ring size = 7.2727