Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_150_2_17892_AJzVw4.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.07 T-atoms per nm^3
Material density = 2.302 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6185 Angstrom
T1  -- O2  = 1.6246 Angstrom
T1  -- O3  = 1.6189 Angstrom
T1  -- O4  = 1.6239 Angstrom
      mean = 1.6215 Angstrom
        t1 = 0.007788  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002993  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6225 Angstrom
T2  -- O4  = 1.6250 Angstrom
T2  -- O5  = 1.6185 Angstrom
T2  -- O3  = 1.6187 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.007154  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001562  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6185 A <--> 1.6250 A
          Mean   = 1.6213 A
          StdDev = 0.0028 A

       t1 Range  = 0.0072 <-- 0.0075 --> 0.0078
       t2 Range  = 0.0016 <-- 0.0023 --> 0.0030

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.843 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.178 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.091 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.867 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.887 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.953 deg; O3  -- O4  = 3 A
       108.953 deg <-- 109.470 deg --> 109.887 deg

O2  -- T2  -- O4  = 109.353 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.262 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.522 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.981 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.216 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.493 deg; O5  -- O3  = 3 A
       109.216 deg <-- 109.471 deg --> 109.981 deg

        O-T-O SUMMARY
          Range  = 108.9528 deg <--> 109.9807 deg
          Mean   = 109.4705 deg
          StdDev = 0.3381 deg

        O--O SUMMARY
          Range  = 2.6385 A <--> 2.6592 A
          Mean   = 2.6476 A
          StdDev = 0.0069 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 112.504 deg; T2  -- T2  = 5.0017 A
T2  - O1  - T1  - O3  - T2  = 101.007 deg; T2  -- T2  = 4.6944 A
T2  - O1  - T1  - O4  - T1  = 110.443 deg; T2  -- T1  = 5.0608 A
T2  - O2  - T1  - O3  - T2  = 112.141 deg; T2  -- T2  = 5.0028 A
T2  - O2  - T1  - O4  - T1  = 110.565 deg; T2  -- T1  = 5.0204 A
T2  - O3  - T1  - O4  - T1  = 109.824 deg; T2  -- T1  = 5.0532 A

T1  - O2  - T2  - O4  - T1  = 104.495 deg; T1  -- T1  = 4.7561 A
T1  - O2  - T2  - O5  - T1  = 116.209 deg; T1  -- T1  = 5.1649 A
T1  - O2  - T2  - O3  - T2  = 110.195 deg; T1  -- T2  = 5.0521 A
T1  - O4  - T2  - O5  - T1  = 104.980 deg; T1  -- T1  = 4.7828 A
T1  - O4  - T2  - O3  - T2  = 110.566 deg; T1  -- T2  = 5.0193 A
T1  - O5  - T2  - O3  - T2  = 110.074 deg; T1  -- T2  = 5.0597 A

        T-T-T SUMMARY
          Range  = 101.0067 deg <--> 116.2087 deg
          Mean   = 109.4170 deg
          StdDev = 3.9285 deg

        T--T SUMMARY
          Range  = 4.6944 A <--> 5.1649 A
          Mean   = 4.9724 A
          StdDev = 0.1399 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 149.976 deg ; T1  -- T1   3.1264 A

T1  -- O2  -- T2  = 138.329 deg ; T1  -- T2   3.0347 A

T1  -- O3  -- T2  = 140.668 deg ; T1  -- T2   3.0487 A

T1  -- O4  -- T2  = 133.097 deg ; T1  -- T2   2.9805 A

T2  -- O5  -- T2  = 149.780 deg ; T2  -- T2   3.1251 A


        T-O-T SUMMARY
          Range  = 133.0965° <--> 149.9756 deg
          Mean   = 142.3699 deg
          StdDev = 6.7156 deg

        T--T SUMMARY
          Range  = 2.9805 A <--> 3.1264 A
          Mean   = 3.0631 A
          StdDev = 0.0570 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

<TD10> = 1027.000
Average ring size = 6.0000