Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_48351_F_2Ptk.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.43 T-atoms per nm^3
Material density = 2.238 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6211 Angstrom
T1  -- O3  = 1.6211 Angstrom
T1  -- O4  = 1.6205 Angstrom
T1  -- O2  = 1.6213 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.006862  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000553  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6209 Angstrom
T2  -- O4  = 1.6202 Angstrom
T2  -- O2  = 1.6214 Angstrom
T2  -- O3  = 1.6208 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.006748  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000257  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6202 A <--> 1.6214 A
          Mean   = 1.6209 A
          StdDev = 0.0004 A

       t1 Range  = 0.0067 <-- 0.0068 --> 0.0069
       t2 Range  = 0.0003 <-- 0.0004 --> 0.0006

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.499 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.366 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.448 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.586 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.441 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.487 deg; O4  -- O2  = 3 A
       109.366 deg <-- 109.471 deg --> 109.586 deg

O1  -- T2  -- O4  = 109.583 deg; O1  -- O4  = 3 A
O1  -- T2  -- O2  = 109.431 deg; O1  -- O2  = 3 A
O1  -- T2  -- O3  = 109.491 deg; O1  -- O3  = 3 A
O4  -- T2  -- O2  = 109.422 deg; O4  -- O2  = 3 A
O4  -- T2  -- O3  = 109.394 deg; O4  -- O3  = 3 A
O2  -- T2  -- O3  = 109.505 deg; O2  -- O3  = 3 A
       109.394 deg <-- 109.471 deg --> 109.583 deg

        O-T-O SUMMARY
          Range  = 109.3661 deg <--> 109.5863 deg
          Mean   = 109.4712 deg
          StdDev = 0.0657 deg

        O--O SUMMARY
          Range  = 2.6451 A <--> 2.6487 A
          Mean   = 2.6470 A
          StdDev = 0.0011 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 145.562 deg; T2  -- T2  = 5.7880 A
T2  - O1  - T1  - O4  - T2  =  96.814 deg; T2  -- T2  = 4.5191 A
T2  - O1  - T1  - O2  - T2  =  83.619 deg; T2  -- T2  = 4.0357 A
T2  - O3  - T1  - O4  - T2  = 116.852 deg; T2  -- T2  = 5.1598 A
T2  - O3  - T1  - O2  - T2  =  90.544 deg; T2  -- T2  = 4.3106 A
T2  - O4  - T1  - O2  - T2  = 110.791 deg; T2  -- T2  = 4.9801 A

T1  - O1  - T2  - O4  - T1  = 109.615 deg; T1  -- T1  = 4.9520 A
T1  - O1  - T2  - O2  - T1  =  83.186 deg; T1  -- T1  = 4.0113 A
T1  - O1  - T2  - O3  - T1  =  96.381 deg; T1  -- T1  = 4.5122 A
T1  - O4  - T2  - O2  - T1  = 106.584 deg; T1  -- T1  = 4.8554 A
T1  - O4  - T2  - O3  - T1  = 136.463 deg; T1  -- T1  = 5.6348 A
T1  - O2  - T2  - O3  - T1  = 110.791 deg; T1  -- T1  = 4.9801 A

        T-T-T SUMMARY
          Range  = 83.1859 deg <--> 145.5622 deg
          Mean   = 107.2668 deg
          StdDev = 18.6529 deg

        T--T SUMMARY
          Range  = 4.0113 A <--> 5.7880 A
          Mean   = 4.8116 A
          StdDev = 0.5457 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 137.628 deg ; T1  -- T2   3.0229 A

T1  -- O2  -- T2  = 137.250 deg ; T1  -- T2   3.0197 A

T1  -- O3  -- T2  = 138.409 deg ; T1  -- T2   3.0308 A

T1  -- O4  -- T2  = 139.115 deg ; T1  -- T2   3.0367 A


        T-O-T SUMMARY
          Range  = 137.2497° <--> 139.1147 deg
          Mean   = 138.1005 deg
          StdDev = 0.7431 deg

        T--T SUMMARY
          Range  = 3.0197 A <--> 3.0367 A
          Mean   = 3.0275 A
          StdDev = 0.0069 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000