Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_48335_ij0mrI.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 21.64 T-atoms per nm^3
Material density = 2.159 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6222 Angstrom
T1  -- O4  = 1.6202 Angstrom
T1  -- O3  = 1.6229 Angstrom
T1  -- O2  = 1.6215 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007368  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001344  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6234 Angstrom
T2  -- O3  = 1.6226 Angstrom
T2  -- O4  = 1.6207 Angstrom
T2  -- O2  = 1.6208 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.007513  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001038  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6202 A <--> 1.6234 A
          Mean   = 1.6218 A
          StdDev = 0.0011 A

       t1 Range  = 0.0074 <-- 0.0074 --> 0.0075
       t2 Range  = 0.0010 <-- 0.0012 --> 0.0013

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 109.444 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.103 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.571 deg; O1  -- O2  = 3 A
O4  -- T1  -- O3  = 109.621 deg; O4  -- O3  = 3 A
O4  -- T1  -- O2  = 109.391 deg; O4  -- O2  = 3 A
O3  -- T1  -- O2  = 109.697 deg; O3  -- O2  = 3 A
       109.103 deg <-- 109.471 deg --> 109.697 deg

O1  -- T2  -- O3  = 109.605 deg; O1  -- O3  = 3 A
O1  -- T2  -- O4  = 109.594 deg; O1  -- O4  = 3 A
O1  -- T2  -- O2  = 109.429 deg; O1  -- O2  = 3 A
O3  -- T2  -- O4  = 109.706 deg; O3  -- O4  = 3 A
O3  -- T2  -- O2  = 109.102 deg; O3  -- O2  = 3 A
O4  -- T2  -- O2  = 109.390 deg; O4  -- O2  = 3 A
       109.102 deg <-- 109.471 deg --> 109.706 deg

        O-T-O SUMMARY
          Range  = 109.1019 deg <--> 109.7059 deg
          Mean   = 109.4711 deg
          StdDev = 0.1977 deg

        O--O SUMMARY
          Range  = 2.6422 A <--> 2.6527 A
          Mean   = 2.6484 A
          StdDev = 0.0035 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O4  - T2  = 109.623 deg; T2  -- T2  = 4.9003 A
T2  - O1  - T1  - O3  - T2  =  81.192 deg; T2  -- T2  = 3.8851 A
T2  - O1  - T1  - O2  - T2  = 110.286 deg; T2  -- T2  = 4.9224 A
T2  - O4  - T1  - O3  - T2  = 151.275 deg; T2  -- T2  = 5.8206 A
T2  - O4  - T1  - O2  - T2  = 103.493 deg; T2  -- T2  = 4.7404 A
T2  - O3  - T1  - O2  - T2  =  96.944 deg; T2  -- T2  = 4.5002 A

T1  - O1  - T2  - O3  - T1  = 122.727 deg; T1  -- T1  = 5.2625 A
T1  - O1  - T2  - O4  - T1  = 110.286 deg; T1  -- T1  = 4.9224 A
T1  - O1  - T2  - O2  - T1  =  98.808 deg; T1  -- T1  = 4.5335 A
T1  - O3  - T2  - O4  - T1  = 115.809 deg; T1  -- T1  = 5.1140 A
T1  - O3  - T2  - O2  - T1  = 118.314 deg; T1  -- T1  = 5.1587 A
T1  - O4  - T2  - O2  - T1  =  83.056 deg; T1  -- T1  = 3.9853 A

        T-T-T SUMMARY
          Range  = 81.1918 deg <--> 151.2754 deg
          Mean   = 108.4845 deg
          StdDev = 18.0665 deg

        T--T SUMMARY
          Range  = 3.8851 A <--> 5.8206 A
          Mean   = 4.8121 A
          StdDev = 0.5207 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 133.228 deg ; T1  -- T2   2.9790 A

T1  -- O2  -- T2  = 137.282 deg ; T1  -- T2   3.0197 A

T1  -- O3  -- T2  = 134.357 deg ; T1  -- T2   2.9915 A

T1  -- O4  -- T2  = 137.148 deg ; T1  -- T2   3.0169 A


        T-O-T SUMMARY
          Range  = 133.2279° <--> 137.2818 deg
          Mean   = 135.5037 deg
          StdDev = 1.8156 deg

        T--T SUMMARY
          Range  = 2.9790 A <--> 3.0197 A
          Mean   = 3.0018 A
          StdDev = 0.0177 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000