Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_47724_MsUkw0.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 20.32 T-atoms per nm^3
Material density = 2.027 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6146 Angstrom
T1  -- O3  = 1.6228 Angstrom
T1  -- O4  = 1.6225 Angstrom
T1  -- O2  = 1.6214 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.028507  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019766  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6255 Angstrom
T2  -- O4  = 1.6198 Angstrom
T2  -- O5  = 1.5921 Angstrom
T2  -- O3  = 1.6259 Angstrom
      mean = 1.6158 Angstrom
        t1 = 0.019372  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021328  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5921 A <--> 1.6259 A
          Mean   = 1.6181 A
          StdDev = 0.0105 A

       t1 Range  = 0.0194 <-- 0.0239 --> 0.0285
       t2 Range  = 0.0198 <-- 0.0205 --> 0.0213

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 104.338 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.141 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 117.705 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 104.527 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 111.488 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 110.662 deg; O4  -- O2  = 3 A
       104.338 deg <-- 109.310 deg --> 117.705 deg

O2  -- T2  -- O4  = 112.741 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 105.678 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.841 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 106.836 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 111.177 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 110.379 deg; O5  -- O3  = 3 A
       105.678 deg <-- 109.442 deg --> 112.741 deg

        O-T-O SUMMARY
          Range  = 104.3381 deg <--> 117.7050 deg
          Mean   = 109.3762 deg
          StdDev = 3.7507 deg

        O--O SUMMARY
          Range  = 2.5570 A <--> 2.7695 A
          Mean   = 2.6394 A
          StdDev = 0.0639 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T1  = 101.543 deg; T2  -- T1  = 5.0108 A
T2  - O1  - T1  - O4  - T2  = 112.933 deg; T2  -- T2  = 5.3449 A
T2  - O1  - T1  - O2  - T2  =  90.794 deg; T2  -- T2  = 4.4064 A
T1  - O3  - T1  - O4  - T2  =  98.733 deg; T1  -- T2  = 4.8584 A
T1  - O3  - T1  - O2  - T2  = 128.002 deg; T1  -- T2  = 5.5487 A
T2  - O4  - T1  - O2  - T2  = 122.492 deg; T2  -- T2  = 5.3623 A

T1  - O2  - T2  - O4  - T1  = 122.656 deg; T1  -- T1  = 5.3665 A
T1  - O2  - T2  - O5  - T1  = 120.370 deg; T1  -- T1  = 5.5633 A
T1  - O2  - T2  - O3  - T2  =  99.902 deg; T1  -- T2  = 4.8660 A
T1  - O4  - T2  - O5  - T1  =  89.206 deg; T1  -- T1  = 4.3461 A
T1  - O4  - T2  - O3  - T2  = 116.644 deg; T1  -- T2  = 5.2155 A
T1  - O5  - T2  - O3  - T2  = 108.483 deg; T1  -- T2  = 5.2127 A

        T-T-T SUMMARY
          Range  = 89.2061 deg <--> 128.0022 deg
          Mean   = 109.3132 deg
          StdDev = 12.7127 deg

        T--T SUMMARY
          Range  = 4.3461 A <--> 5.5633 A
          Mean   = 5.0918 A
          StdDev = 0.3926 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2293 A

T1  -- O2  -- T2  = 129.993 deg ; T1  -- T2   2.9426 A

T1  -- O3  -- T2  = 171.325 deg ; T1  -- T2   3.2394 A

T1  -- O4  -- T2  = 156.192 deg ; T1  -- T2   3.1726 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.1841 A


        T-O-T SUMMARY
          Range  = 129.9928° <--> 180.0000 deg
          Mean   = 163.5020 deg
          StdDev = 19.3683 deg

        T--T SUMMARY
          Range  = 2.9426 A <--> 3.2394 A
          Mean   = 3.1536 A
          StdDev = 0.1113 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000