Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_47544_savJlW.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.46 T-atoms per nm^3
Material density = 1.941 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6155 Angstrom
T1  -- O2  = 1.6099 Angstrom
T1  -- O4  = 1.6099 Angstrom
T1  -- O3  = 1.6212 Angstrom
      mean = 1.6141 Angstrom
        t1 = 0.003137  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001396  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6099 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O4  = 1.6099 Angstrom
T2  -- O5  = 1.6155 Angstrom
      mean = 1.6141 Angstrom
        t1 = 0.003136  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002111  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6099 A <--> 1.6212 A
          Mean   = 1.6141 A
          StdDev = 0.0047 A

       t1 Range  = 0.0031 <-- 0.0031 --> 0.0031
       t2 Range  = 0.0014 <-- 0.0018 --> 0.0021

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.448 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.413 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.455 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.443 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.570 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.498 deg; O4  -- O3  = 3 A
       109.413 deg <-- 109.471 deg --> 109.570 deg

O2  -- T2  -- O3  = 109.572 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.441 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.456 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.490 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.455 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.413 deg; O4  -- O5  = 3 A
       109.413 deg <-- 109.471 deg --> 109.572 deg

        O-T-O SUMMARY
          Range  = 109.4129 deg <--> 109.5721 deg
          Mean   = 109.4712 deg
          StdDev = 0.0512 deg

        O--O SUMMARY
          Range  = 2.6284 A <--> 2.6424 A
          Mean   = 2.6358 A
          StdDev = 0.0049 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 108.957 deg; T2  -- T2  = 5.2406 A
T2  - O1  - T1  - O4  - T2  =  89.999 deg; T2  -- T2  = 4.4241 A
T2  - O1  - T1  - O3  - T1  = 108.885 deg; T2  -- T1  = 5.2475 A
T2  - O2  - T1  - O4  - T2  = 118.187 deg; T2  -- T2  = 5.3671 A
T2  - O2  - T1  - O3  - T1  = 109.784 deg; T2  -- T1  = 5.2771 A
T2  - O4  - T1  - O3  - T1  = 118.532 deg; T2  -- T1  = 5.3866 A

T1  - O2  - T2  - O3  - T1  = 108.957 deg; T1  -- T1  = 5.2406 A
T1  - O2  - T2  - O4  - T1  =  90.001 deg; T1  -- T1  = 4.4242 A
T1  - O2  - T2  - O5  - T2  = 108.892 deg; T1  -- T2  = 5.2477 A
T1  - O3  - T2  - O4  - T1  = 118.184 deg; T1  -- T1  = 5.3670 A
T1  - O3  - T2  - O5  - T2  = 109.783 deg; T1  -- T2  = 5.2771 A
T1  - O4  - T2  - O5  - T2  = 118.528 deg; T1  -- T2  = 5.3865 A

        T-T-T SUMMARY
          Range  = 89.9991 deg <--> 118.5316 deg
          Mean   = 109.0574 deg
          StdDev = 9.5588 deg

        T--T SUMMARY
          Range  = 4.4241 A <--> 5.3866 A
          Mean   = 5.1572 A
          StdDev = 0.3361 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2310 A

T1  -- O2  -- T2  = 177.913 deg ; T1  -- T2   3.2192 A

T1  -- O3  -- T2  = 138.773 deg ; T1  -- T2   3.0347 A

T1  -- O4  -- T2  = 179.152 deg ; T1  -- T2   3.2197 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2310 A


        T-O-T SUMMARY
          Range  = 138.7729° <--> 180.0000 deg
          Mean   = 171.1676 deg
          StdDev = 16.6366 deg

        T--T SUMMARY
          Range  = 3.0347 A <--> 3.2310 A
          Mean   = 3.1871 A
          StdDev = 0.0784 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000