Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_41517_3FK3uj.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 24.47 T-atoms per nm^3
Material density = 2.441 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5958 Angstrom
T1  -- O4  = 1.6252 Angstrom
T1  -- O2  = 1.6159 Angstrom
T1  -- O3  = 1.6296 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.054913  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.047231  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6326 Angstrom
T2  -- O4  = 1.6138 Angstrom
T2  -- O5  = 1.6382 Angstrom
T2  -- O3  = 1.5796 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.047501  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040142  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5796 A <--> 1.6382 A
          Mean   = 1.6163 A
          StdDev = 0.0189 A

       t1 Range  = 0.0475 <-- 0.0512 --> 0.0549
       t2 Range  = 0.0401 <-- 0.0437 --> 0.0472

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  =  98.223 deg; O1  -- O4  = 2 A
O1  -- T1  -- O2  = 119.164 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.302 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 107.973 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 123.359 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 102.140 deg; O2  -- O3  = 3 A
       98.223 deg <-- 109.693 deg --> 123.359 deg

O2  -- T2  -- O4  = 106.283 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 114.064 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 111.833 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 120.469 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 102.308 deg; O4  -- O3  = 2 A
O5  -- T2  -- O3  = 101.116 deg; O5  -- O3  = 2 A
       101.116 deg <-- 109.345 deg --> 120.469 deg

        O-T-O SUMMARY
          Range  = 98.2234 deg <--> 123.3592 deg
          Mean   = 109.5195 deg
          StdDev = 8.0048 deg

        O--O SUMMARY
          Range  = 2.4351 A <--> 2.8652 A
          Mean   = 2.6343 A
          StdDev = 0.1363 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T2  = 102.472 deg; T1  -- T2  = 4.9981 A
T1  - O1  - T1  - O2  - T2  = 138.472 deg; T1  -- T2  = 5.7617 A
T1  - O1  - T1  - O3  - T2  =  99.499 deg; T1  -- T2  = 4.8049 A
T2  - O4  - T1  - O2  - T2  =  88.589 deg; T2  -- T2  = 4.3251 A
T2  - O4  - T1  - O3  - T2  = 131.504 deg; T2  -- T2  = 5.7642 A
T2  - O2  - T1  - O3  - T2  = 102.484 deg; T2  -- T2  = 4.7366 A

T2  - O2  - T2  - O4  - T1  =  96.670 deg; T2  -- T1  = 4.6705 A
T2  - O2  - T2  - O5  - T1  = 115.615 deg; T2  -- T1  = 5.3998 A
T2  - O2  - T2  - O3  - T1  = 125.820 deg; T2  -- T1  = 5.7822 A
T1  - O4  - T2  - O5  - T1  = 102.484 deg; T1  -- T1  = 4.7366 A
T1  - O4  - T2  - O3  - T1  = 128.784 deg; T1  -- T1  = 5.5813 A
T1  - O5  - T2  - O3  - T1  =  85.019 deg; T1  -- T1  = 4.2725 A

        T-T-T SUMMARY
          Range  = 85.0187 deg <--> 138.4718 deg
          Mean   = 109.7841 deg
          StdDev = 17.1285 deg

        T--T SUMMARY
          Range  = 4.2725 A <--> 5.7822 A
          Mean   = 5.0695 A
          StdDev = 0.5447 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1916 A

T1  -- O2  -- T2  = 132.180 deg ; T1  -- T2   2.9697 A

T1  -- O3  -- T2  = 150.494 deg ; T1  -- T2   3.1034 A

T1  -- O4  -- T2  = 167.039 deg ; T1  -- T2   3.2184 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2763 A


        T-O-T SUMMARY
          Range  = 132.1804° <--> 180.0000 deg
          Mean   = 161.9427 deg
          StdDev = 18.8902 deg

        T--T SUMMARY
          Range  = 2.9697 A <--> 3.2763 A
          Mean   = 3.1519 A
          StdDev = 0.1096 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 110 151 200 251 310 375 446 520 592 648 699
TD10 = 1193
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 110 151 200 251 310 375 446 520 588 647 705
TD10 = 1193
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 1193.000
Average ring size = 6.0000