Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_38265_YV857S.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 23.75 T-atoms per nm^3
Material density = 2.370 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6144 Angstrom
T1  -- O4  = 1.6102 Angstrom
T1  -- O3  = 1.7596 Angstrom
T1  -- O2  = 1.6371 Angstrom
      mean = 1.6553 Angstrom
        t1 = 0.072646  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058956  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6032 Angstrom
T2  -- O4  = 1.6070 Angstrom
T2  -- O5  = 1.4931 Angstrom
T2  -- O3  = 1.6297 Angstrom
      mean = 1.5833 Angstrom
        t1 = 0.153410  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.190397  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4931 A <--> 1.7596 A
          Mean   = 1.6193 A
          StdDev = 0.0687 A

       t1 Range  = 0.0726 <-- 0.1130 --> 0.1534
       t2 Range  = 0.0590 <-- 0.1247 --> 0.1904

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 100.641 deg; O1  -- O4  = 2 A
O1  -- T1  -- O3  = 116.472 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 100.810 deg; O1  -- O2  = 3 A
O4  -- T1  -- O3  = 116.270 deg; O4  -- O3  = 3 A
O4  -- T1  -- O2  = 104.122 deg; O4  -- O2  = 3 A
O3  -- T1  -- O2  = 116.140 deg; O3  -- O2  = 3 A
       100.641 deg <-- 109.076 deg --> 116.472 deg

O2  -- T2  -- O4  = 113.360 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  =  73.851 deg; O2  -- O5  = 2 A
O2  -- T2  -- O3  = 131.312 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 124.428 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 114.747 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  =  85.225 deg; O5  -- O3  = 2 A
       73.851 deg <-- 107.154 deg --> 131.312 deg

        O-T-O SUMMARY
          Range  = 73.8512 deg <--> 131.3115 deg
          Mean   = 108.1148 deg
          StdDev = 15.7090 deg

        O--O SUMMARY
          Range  = 1.8623 A <--> 2.9455 A
          Mean   = 2.6034 A
          StdDev = 0.3178 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O4  - T1  = 105.836 deg; T2  -- T1  = 5.1302 A
T2  - O1  - T1  - O3  - T2  = 130.528 deg; T2  -- T2  = 5.4929 A
T2  - O1  - T1  - O2  - T2  =  98.650 deg; T2  -- T2  = 4.7885 A
T1  - O4  - T1  - O3  - T2  = 119.809 deg; T1  -- T2  = 5.2574 A
T1  - O4  - T1  - O2  - T2  = 116.851 deg; T1  -- T2  = 5.4019 A
T2  - O3  - T1  - O2  - T2  =  77.973 deg; T2  -- T2  = 3.7524 A

T1  - O2  - T2  - O4  - T2  = 129.581 deg; T1  -- T2  = 5.5994 A
T1  - O2  - T2  - O5  - T1  = 117.221 deg; T1  -- T1  = 5.1642 A
T1  - O2  - T2  - O3  - T1  = 108.450 deg; T1  -- T1  = 5.1223 A
T2  - O4  - T2  - O5  - T1  = 103.274 deg; T2  -- T1  = 4.5721 A
T2  - O4  - T2  - O3  - T1  =  89.828 deg; T2  -- T1  = 4.3061 A
T1  - O5  - T2  - O3  - T1  = 102.027 deg; T1  -- T1  = 4.6320 A

        T-T-T SUMMARY
          Range  = 77.9730 deg <--> 130.5282 deg
          Mean   = 108.3355 deg
          StdDev = 15.0371 deg

        T--T SUMMARY
          Range  = 3.7524 A <--> 5.5994 A
          Mean   = 4.9349 A
          StdDev = 0.5251 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2288 A

T1  -- O2  -- T2  = 147.563 deg ; T1  -- T2   3.1114 A

T1  -- O3  -- T2  = 114.022 deg ; T1  -- T2   2.8438 A

T1  -- O4  -- T2  = 168.785 deg ; T1  -- T2   3.2018 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   2.9862 A


        T-O-T SUMMARY
          Range  = 114.0220° <--> 180.0000 deg
          Mean   = 158.0739 deg
          StdDev = 25.6588 deg

        T--T SUMMARY
          Range  = 2.8438 A <--> 3.2288 A
          Mean   = 3.0744 A
          StdDev = 0.1468 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O5  = 1.8623 A
O3  -- O5  = 2.1167 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 353 398 440 478 512
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 300 351 397 439 477 511
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000