Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_37240_Q2LTDz.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.51 T-atoms per nm^3
Material density = 1.947 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6166 Angstrom
T1  -- O2  = 1.6243 Angstrom
T1  -- O3  = 1.6089 Angstrom
T1  -- O4  = 1.6123 Angstrom
      mean = 1.6155 Angstrom
        t1 = 0.005443  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003067  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6242 Angstrom
T2  -- O3  = 1.6090 Angstrom
T2  -- O4  = 1.6127 Angstrom
T2  -- O5  = 1.6163 Angstrom
      mean = 1.6156 Angstrom
        t1 = 0.005191  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002991  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6089 A <--> 1.6243 A
          Mean   = 1.6155 A
          StdDev = 0.0058 A

       t1 Range  = 0.0052 <-- 0.0053 --> 0.0054
       t2 Range  = 0.0030 <-- 0.0030 --> 0.0031

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.650 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.360 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.148 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.396 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.610 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.656 deg; O3  -- O4  = 3 A
       108.656 deg <-- 109.470 deg --> 110.148 deg

O2  -- T2  -- O3  = 109.459 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.620 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.612 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 108.729 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.412 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.991 deg; O4  -- O5  = 3 A
       108.729 deg <-- 109.471 deg --> 109.991 deg

        O-T-O SUMMARY
          Range  = 108.6564 deg <--> 110.1482 deg
          Mean   = 109.4703 deg
          StdDev = 0.4186 deg

        O--O SUMMARY
          Range  = 2.6168 A <--> 2.6491 A
          Mean   = 2.6381 A
          StdDev = 0.0108 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 118.650 deg; T2  -- T1  = 5.3896 A
T2  - O1  - T1  - O3  - T2  = 119.254 deg; T2  -- T2  = 5.3567 A
T2  - O1  - T1  - O4  - T2  =  89.969 deg; T2  -- T2  = 4.4193 A
T1  - O2  - T1  - O3  - T2  = 103.040 deg; T1  -- T2  = 5.0176 A
T1  - O2  - T1  - O4  - T2  = 108.534 deg; T1  -- T2  = 5.2357 A
T2  - O3  - T1  - O4  - T2  = 117.439 deg; T2  -- T2  = 5.4636 A

T1  - O2  - T2  - O3  - T1  =  90.031 deg; T1  -- T1  = 4.4217 A
T1  - O2  - T2  - O4  - T2  = 118.658 deg; T1  -- T2  = 5.3893 A
T1  - O2  - T2  - O5  - T1  = 119.176 deg; T1  -- T1  = 5.3546 A
T1  - O3  - T2  - O4  - T2  = 108.627 deg; T1  -- T2  = 5.2383 A
T1  - O3  - T2  - O5  - T1  = 117.492 deg; T1  -- T1  = 5.4651 A
T2  - O4  - T2  - O5  - T1  = 102.947 deg; T2  -- T1  = 5.0139 A

        T-T-T SUMMARY
          Range  = 89.9689 deg <--> 119.2538 deg
          Mean   = 109.4848 deg
          StdDev = 10.6396 deg

        T--T SUMMARY
          Range  = 4.4193 A <--> 5.4651 A
          Mean   = 5.1471 A
          StdDev = 0.3588 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2332 A

T1  -- O2  -- T2  = 137.936 deg ; T1  -- T2   3.0321 A

T1  -- O3  -- T2  = 176.793 deg ; T1  -- T2   3.2167 A

T1  -- O4  -- T2  = 160.047 deg ; T1  -- T2   3.1762 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2326 A


        T-O-T SUMMARY
          Range  = 137.9363° <--> 180.0000 deg
          Mean   = 166.9552 deg
          StdDev = 16.7139 deg

        T--T SUMMARY
          Range  = 3.0321 A <--> 3.2332 A
          Mean   = 3.1782 A
          StdDev = 0.0779 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000