Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_37210_ifwBmF.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.62 T-atoms per nm^3
Material density = 1.958 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6163 Angstrom
T1  -- O2  = 1.6261 Angstrom
T1  -- O4  = 1.6125 Angstrom
T1  -- O3  = 1.6090 Angstrom
      mean = 1.6160 Angstrom
        t1 = 0.005805  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003260  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6266 Angstrom
T2  -- O3  = 1.6087 Angstrom
T2  -- O4  = 1.6136 Angstrom
T2  -- O5  = 1.6172 Angstrom
      mean = 1.6165 Angstrom
        t1 = 0.006463  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003884  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6087 A <--> 1.6266 A
          Mean   = 1.6162 A
          StdDev = 0.0066 A

       t1 Range  = 0.0058 <-- 0.0061 --> 0.0065
       t2 Range  = 0.0033 <-- 0.0036 --> 0.0039

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.637 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 110.048 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.316 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.779 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.392 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 108.647 deg; O4  -- O3  = 3 A
       108.647 deg <-- 109.470 deg --> 110.048 deg

O2  -- T2  -- O3  = 109.316 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.682 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.869 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 108.525 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.307 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 110.118 deg; O4  -- O5  = 3 A
       108.525 deg <-- 109.469 deg --> 110.118 deg

        O-T-O SUMMARY
          Range  = 108.5252 deg <--> 110.1178 deg
          Mean   = 109.4697 deg
          StdDev = 0.4821 deg

        O--O SUMMARY
          Range  = 2.6155 A <--> 2.6551 A
          Mean   = 2.6393 A
          StdDev = 0.0127 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 119.633 deg; T2  -- T2  = 5.3519 A
T2  - O1  - T1  - O4  - T1  = 118.914 deg; T2  -- T1  = 5.3858 A
T2  - O1  - T1  - O3  - T2  =  90.034 deg; T2  -- T2  = 4.4117 A
T2  - O2  - T1  - O4  - T1  = 102.656 deg; T2  -- T1  = 4.9998 A
T2  - O2  - T1  - O3  - T2  = 117.534 deg; T2  -- T2  = 5.4603 A
T1  - O4  - T1  - O3  - T2  = 108.114 deg; T1  -- T2  = 5.2198 A

T1  - O2  - T2  - O3  - T1  = 119.656 deg; T1  -- T1  = 5.3525 A
T1  - O2  - T2  - O4  - T2  = 119.120 deg; T1  -- T2  = 5.3931 A
T1  - O2  - T2  - O5  - T1  =  89.966 deg; T1  -- T1  = 4.4091 A
T1  - O3  - T2  - O4  - T2  = 102.646 deg; T1  -- T2  = 5.0009 A
T1  - O3  - T2  - O5  - T1  = 117.452 deg; T1  -- T1  = 5.4580 A
T2  - O4  - T2  - O5  - T1  = 108.016 deg; T2  -- T1  = 5.2180 A

        T-T-T SUMMARY
          Range  = 89.9661 deg <--> 119.6563 deg
          Mean   = 109.4784 deg
          StdDev = 10.8106 deg

        T--T SUMMARY
          Range  = 4.4091 A <--> 5.4603 A
          Mean   = 5.1384 A
          StdDev = 0.3614 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2326 A

T1  -- O2  -- T2  = 136.352 deg ; T1  -- T2   3.0195 A

T1  -- O3  -- T2  = 175.061 deg ; T1  -- T2   3.2147 A

T1  -- O4  -- T2  = 158.820 deg ; T1  -- T2   3.1712 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2345 A


        T-O-T SUMMARY
          Range  = 136.3521° <--> 180.0000 deg
          Mean   = 166.0467 deg
          StdDev = 17.1964 deg

        T--T SUMMARY
          Range  = 3.0195 A <--> 3.2345 A
          Mean   = 3.1745 A
          StdDev = 0.0829 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000