Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_14_2_36040_ENAgxG.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 21.73 T-atoms per nm^3
Material density = 2.168 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6293 Angstrom
T1  -- O2  = 1.6263 Angstrom
T1  -- O2  = 1.6247 Angstrom
T1  -- O3  = 1.6094 Angstrom
      mean = 1.6224 Angstrom
        t1 = 0.013276  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014157  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6077 Angstrom
T2  -- O3  = 1.6119 Angstrom
T2  -- O5  = 1.6310 Angstrom
T2  -- O5  = 1.6291 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.016971  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010134  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6077 A <--> 1.6310 A
          Mean   = 1.6212 A
          StdDev = 0.0093 A

       t1 Range  = 0.0133 <-- 0.0151 --> 0.0170
       t2 Range  = 0.0101 <-- 0.0121 --> 0.0142

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.521 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 112.217 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.261 deg; O1  -- O3  = 3 A
O2  -- T1  -- O2  = 109.202 deg; O2  -- O2  = 3 A
O2  -- T1  -- O3  = 109.323 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 107.279 deg; O2  -- O3  = 3 A
       107.279 deg <-- 109.467 deg --> 112.217 deg

O4  -- T2  -- O3  = 105.597 deg; O4  -- O3  = 3 A
O4  -- T2  -- O5  = 109.062 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 113.310 deg; O4  -- O5  = 3 A
O3  -- T2  -- O5  = 110.331 deg; O3  -- O5  = 3 A
O3  -- T2  -- O5  = 109.261 deg; O3  -- O5  = 3 A
O5  -- T2  -- O5  = 109.226 deg; O5  -- O5  = 3 A
       105.597 deg <-- 109.464 deg --> 113.310 deg

        O-T-O SUMMARY
          Range  = 105.5969 deg <--> 113.3097 deg
          Mean   = 109.4658 deg
          StdDev = 1.9510 deg

        O--O SUMMARY
          Range  = 2.5644 A <--> 2.7040 A
          Mean   = 2.6470 A
          StdDev = 0.0362 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  95.857 deg; T1  -- T1  = 4.5629 A
T1  - O1  - T1  - O2  - T1  = 139.663 deg; T1  -- T1  = 5.7625 A
T1  - O1  - T1  - O3  - T2  = 116.868 deg; T1  -- T2  = 5.5025 A
T1  - O2  - T1  - O2  - T1  = 115.115 deg; T1  -- T1  = 4.8590 A
T1  - O2  - T1  - O3  - T2  =  90.240 deg; T1  -- T2  = 4.3128 A
T1  - O2  - T1  - O3  - T2  =  89.470 deg; T1  -- T2  = 4.2840 A

T1  - O4  - T2  - O3  - T2  =  89.756 deg; T1  -- T2  = 4.2840 A
T1  - O4  - T2  - O5  - T2  = 112.174 deg; T1  -- T2  = 5.3235 A
T1  - O4  - T2  - O5  - T2  =  90.530 deg; T1  -- T2  = 4.3128 A
T2  - O3  - T2  - O5  - T2  =  94.976 deg; T2  -- T2  = 4.4867 A
T2  - O3  - T2  - O5  - T2  = 116.135 deg; T2  -- T2  = 4.8590 A
T2  - O5  - T2  - O5  - T2  = 141.890 deg; T2  -- T2  = 5.7461 A

        T-T-T SUMMARY
          Range  = 89.4698 deg <--> 141.8898 deg
          Mean   = 107.7228 deg
          StdDev = 18.3974 deg

        T--T SUMMARY
          Range  = 4.2840 A <--> 5.7625 A
          Mean   = 4.8580 A
          StdDev = 0.5625 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2586 A

T1  -- O2  -- T1  = 124.628 deg ; T1  -- T1   2.8788 A

T1  -- O3  -- T2  = 166.608 deg ; T1  -- T2   3.1993 A

T2  -- O4  -- T2  = 180.000 deg ; T2  -- T2   3.2153 A

T2  -- O5  -- T2  = 122.827 deg ; T2  -- T2   2.8627 A


        T-O-T SUMMARY
          Range  = 122.8265° <--> 180.0000 deg
          Mean   = 154.8126 deg
          StdDev = 26.5256 deg

        T--T SUMMARY
          Range  = 2.8627 A <--> 3.2586 A
          Mean   = 3.0830 A
          StdDev = 0.1790 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 99 106 113 132 135 151 166 173 195 197
TD10 = 654
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 99 106 114 128 138 154 165 171 190 205
TD10 = 651
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 652.500
Average ring size = 5.6000