Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_147_2_30287_pwlf_C.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 19.08 T-atoms per nm^3
Material density = 1.904 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6193 Angstrom
T1  -- O2  = 1.6110 Angstrom
T1  -- O4  = 1.6198 Angstrom
T1  -- O3  = 1.6265 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.007930  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003857  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6166 Angstrom
T2  -- O2  = 1.6132 Angstrom
T2  -- O3  = 1.6254 Angstrom
T2  -- O4  = 1.6287 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.008167  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003281  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6110 A <--> 1.6287 A
          Mean   = 1.6201 A
          StdDev = 0.0061 A

       t1 Range  = 0.0079 <-- 0.0080 --> 0.0082
       t2 Range  = 0.0033 <-- 0.0036 --> 0.0039

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.510 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.845 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.883 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 108.289 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.079 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 110.206 deg; O4  -- O3  = 3 A
       108.289 deg <-- 109.469 deg --> 110.206 deg

O1  -- T2  -- O2  = 109.089 deg; O1  -- O2  = 3 A
O1  -- T2  -- O3  = 109.890 deg; O1  -- O3  = 3 A
O1  -- T2  -- O4  = 110.029 deg; O1  -- O4  = 3 A
O2  -- T2  -- O3  = 108.776 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.330 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.703 deg; O3  -- O4  = 3 A
       108.776 deg <-- 109.469 deg --> 110.029 deg

        O-T-O SUMMARY
          Range  = 108.2894 deg <--> 110.2055 deg
          Mean   = 109.4691 deg
          StdDev = 0.5507 deg

        O--O SUMMARY
          Range  = 2.6186 A <--> 2.6625 A
          Mean   = 2.6455 A
          StdDev = 0.0135 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 120.184 deg; T2  -- T2  = 5.4157 A
T2  - O1  - T1  - O4  - T2  = 113.801 deg; T2  -- T2  = 5.0714 A
T2  - O1  - T1  - O3  - T2  = 113.061 deg; T2  -- T2  = 5.0464 A
T2  - O2  - T1  - O4  - T2  =  90.126 deg; T2  -- T2  = 4.3808 A
T2  - O2  - T1  - O3  - T2  =  89.444 deg; T2  -- T2  = 4.3518 A
T2  - O4  - T1  - O3  - T2  = 125.501 deg; T2  -- T2  = 5.3233 A

T1  - O1  - T2  - O2  - T1  = 119.807 deg; T1  -- T1  = 5.4054 A
T1  - O1  - T2  - O3  - T1  = 113.695 deg; T1  -- T1  = 5.0648 A
T1  - O1  - T2  - O4  - T1  = 112.886 deg; T1  -- T1  = 5.0449 A
T1  - O2  - T2  - O3  - T1  =  90.556 deg; T1  -- T1  = 4.3942 A
T1  - O2  - T2  - O4  - T1  =  89.874 deg; T1  -- T1  = 4.3712 A
T1  - O3  - T2  - O4  - T1  = 125.501 deg; T1  -- T1  = 5.3233 A

        T-T-T SUMMARY
          Range  = 89.4437 deg <--> 125.5014 deg
          Mean   = 108.7030 deg
          StdDev = 13.9619 deg

        T--T SUMMARY
          Range  = 4.3518 A <--> 5.4157 A
          Mean   = 4.9328 A
          StdDev = 0.4184 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 141.798 deg ; T1  -- T2   3.0577 A

T1  -- O2  -- T2  = 163.190 deg ; T1  -- T2   3.1895 A

T1  -- O3  -- T2  = 134.238 deg ; T1  -- T2   2.9960 A

T1  -- O4  -- T2  = 134.132 deg ; T1  -- T2   2.9918 A


        T-O-T SUMMARY
          Range  = 134.1315° <--> 163.1904 deg
          Mean   = 143.3396 deg
          StdDev = 12.1303 deg

        T--T SUMMARY
          Range  = 2.9918 A <--> 3.1895 A
          Mean   = 3.0588 A
          StdDev = 0.0816 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 34 54 78 104 134 168 210 256 302 352 406 470 538
TD10 = 817
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 34 54 78 104 134 168 210 256 302 352 406 470 538
TD10 = 817
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 817.000
Average ring size = 5.1429