Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146_2_7946_wD0cEg.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 19.19 T-atoms per nm^3
Material density = 1.915 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6217 Angstrom
T1  -- O1  = 1.6228 Angstrom
T1  -- O2  = 1.6207 Angstrom
T1  -- O3  = 1.6215 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007377  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001007  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6199 Angstrom
T2  -- O3  = 1.6209 Angstrom
T2  -- O4  = 1.6222 Angstrom
T2  -- O4  = 1.6219 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.007137  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001607  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6199 A <--> 1.6228 A
          Mean   = 1.6215 A
          StdDev = 0.0009 A

       t1 Range  = 0.0071 <-- 0.0073 --> 0.0074
       t2 Range  = 0.0010 <-- 0.0013 --> 0.0016

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.617 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.362 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.713 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.158 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.298 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.679 deg; O2  -- O3  = 3 A
       109.158 deg <-- 109.471 deg --> 109.713 deg

O2  -- T2  -- O3  = 109.393 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.820 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.078 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.403 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.666 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 109.467 deg; O4  -- O4  = 3 A
       109.078 deg <-- 109.471 deg --> 109.820 deg

        O-T-O SUMMARY
          Range  = 109.0783 deg <--> 109.8202 deg
          Mean   = 109.4711 deg
          StdDev = 0.2222 deg

        O--O SUMMARY
          Range  = 2.6405 A <--> 2.6528 A
          Mean   = 2.6478 A
          StdDev = 0.0038 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  =  89.711 deg; T1  -- T2  = 4.2749 A
T1  - O1  - T1  - O2  - T1  = 121.224 deg; T1  -- T1  = 5.2521 A
T1  - O1  - T1  - O3  - T2  = 119.524 deg; T1  -- T2  = 5.2165 A
T2  - O1  - T1  - O2  - T1  = 119.198 deg; T2  -- T1  = 5.2276 A
T2  - O1  - T1  - O3  - T2  = 120.160 deg; T2  -- T2  = 5.2620 A
T1  - O2  - T1  - O3  - T2  =  90.199 deg; T1  -- T2  = 4.2770 A

T1  - O2  - T2  - O3  - T1  = 119.840 deg; T1  -- T1  = 5.2536 A
T1  - O2  - T2  - O4  - T2  =  90.236 deg; T1  -- T2  = 4.2749 A
T1  - O2  - T2  - O4  - T2  = 119.391 deg; T1  -- T2  = 5.2089 A
T1  - O3  - T2  - O4  - T2  = 119.218 deg; T1  -- T2  = 5.2240 A
T1  - O3  - T2  - O4  - T2  =  89.854 deg; T1  -- T2  = 4.2770 A
T2  - O4  - T2  - O4  - T2  = 121.442 deg; T2  -- T2  = 5.2494 A

        T-T-T SUMMARY
          Range  = 89.7106 deg <--> 121.4419 deg
          Mean   = 109.9997 deg
          StdDev = 14.2247 deg

        T--T SUMMARY
          Range  = 4.2749 A <--> 5.2620 A
          Mean   = 4.9165 A
          StdDev = 0.4553 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.532 deg ; T1  -- T1   3.0139 A

T1  -- O2  -- T2  = 140.193 deg ; T1  -- T2   3.0470 A

T1  -- O3  -- T2  = 137.712 deg ; T1  -- T2   3.0242 A

T2  -- O4  -- T2  = 136.116 deg ; T2  -- T2   3.0091 A


        T-O-T SUMMARY
          Range  = 136.1155° <--> 140.1933 deg
          Mean   = 137.6380 deg
          StdDev = 1.6097 deg

        T--T SUMMARY
          Range  = 3.0091 A <--> 3.0470 A
          Mean   = 3.0235 A
          StdDev = 0.0148 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 9
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

T2 (Si): multiplicity = 9
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 791.000
Average ring size = 5.1429