Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146_2_5327_JHVJnl.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 25.58 T-atoms per nm^3
Material density = 2.552 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6157 Angstrom
T1  -- O3  = 1.6271 Angstrom
T1  -- O1  = 1.6412 Angstrom
T1  -- O2  = 1.6715 Angstrom
      mean = 1.6389 Angstrom
        t1 = 0.050155  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037256  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6579 Angstrom
T2  -- O3  = 1.6193 Angstrom
T2  -- O4  = 1.5348 Angstrom
T2  -- O4  = 1.7036 Angstrom
      mean = 1.6289 Angstrom
        t1 = 0.086508  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.074905  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5348 A <--> 1.7036 A
          Mean   = 1.6339 A
          StdDev = 0.0469 A

       t1 Range  = 0.0502 <-- 0.0683 --> 0.0865
       t2 Range  = 0.0373 <-- 0.0561 --> 0.0749

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  =  97.156 deg; O1  -- O3  = 2 A
O1  -- T1  -- O1  = 104.458 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 113.543 deg; O1  -- O2  = 3 A
O3  -- T1  -- O1  = 112.373 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 114.734 deg; O3  -- O2  = 3 A
O1  -- T1  -- O2  = 113.089 deg; O1  -- O2  = 3 A
       97.156 deg <-- 109.226 deg --> 114.734 deg

O2  -- T2  -- O3  = 111.932 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  =  98.466 deg; O2  -- O4  = 2 A
O2  -- T2  -- O4  = 121.894 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  =  94.166 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 119.019 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 103.657 deg; O4  -- O4  = 3 A
       94.166 deg <-- 108.189 deg --> 121.894 deg

        O-T-O SUMMARY
          Range  = 94.1663 deg <--> 121.8936 deg
          Mean   = 108.7073 deg
          StdDev = 8.5852 deg

        O--O SUMMARY
          Range  = 2.3106 A <--> 2.9386 A
          Mean   = 2.6508 A
          StdDev = 0.1855 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  =  60.000 deg; T1  -- T1  = 2.8336 A
T1  - O1  - T1  - O1  - T2  =  89.610 deg; T1  -- T2  = 4.1407 A
T1  - O1  - T1  - O2  - T2  = 130.472 deg; T1  -- T2  = 5.2872 A
T1  - O3  - T1  - O1  - T2  = 113.053 deg; T1  -- T2  = 4.8996 A
T1  - O3  - T1  - O2  - T2  = 119.673 deg; T1  -- T2  = 5.0344 A
T2  - O1  - T1  - O2  - T2  = 124.647 deg; T2  -- T2  = 5.3377 A

T2  - O2  - T2  - O3  - T2  =  60.000 deg; T2  -- T2  = 2.9257 A
T2  - O2  - T2  - O4  - T1  = 119.616 deg; T2  -- T1  = 5.1121 A
T2  - O2  - T2  - O4  - T1  = 117.103 deg; T2  -- T1  = 5.0886 A
T2  - O3  - T2  - O4  - T1  =  81.068 deg; T2  -- T1  = 3.8440 A
T2  - O3  - T2  - O4  - T1  = 104.301 deg; T2  -- T1  = 4.7101 A
T1  - O4  - T2  - O4  - T1  = 116.044 deg; T1  -- T1  = 5.1127 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 130.4725 deg
          Mean   = 102.9658 deg
          StdDev = 23.5748 deg

        T--T SUMMARY
          Range  = 2.8336 A <--> 5.3377 A
          Mean   = 4.5272 A
          StdDev = 0.8561 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.923 deg ; T1  -- T1   2.8336 A

T1  -- O2  -- T2  = 127.700 deg ; T1  -- T2   2.9886 A

T1  -- O3  -- T2  = 138.789 deg ; T1  -- T2   3.0387 A

T2  -- O4  -- T2  = 129.153 deg ; T2  -- T2   2.9257 A


        T-O-T SUMMARY
          Range  = 120.9229° <--> 138.7892 deg
          Mean   = 129.1413 deg
          StdDev = 6.4682 deg

        T--T SUMMARY
          Range  = 2.8336 A <--> 3.0387 A
          Mean   = 2.9466 A
          StdDev = 0.0777 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 9
Coordination Sequence =
    1 4 10 26 40 66 90 126 160 206 250 306 360 426 490 566 640
TD10 = 979
Circuit symbol = 3.7.7.7.7_{2}.7_{2}
Weight = 27
Vertex symbol  = 3.7.7.7.7_{2}.7_{2}
Weight = 27

T2 (Si): multiplicity = 9
Coordination Sequence =
    1 4 10 26 40 66 90 126 160 206 250 306 360 426 490 566 640
TD10 = 979
Circuit symbol = 3.7.7.7.7_{2}.7_{2}
Weight = 27
Vertex symbol  = 3.7.7.7.7_{2}.7_{2}
Weight = 27

<TD10> = 979.000
Average ring size = 6.0000