Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146_1_33_1_pqtQ.cif"

There are 9 T-atoms per unit cell
There are 18 O-atoms per unit cell

Framework density = 30.18 T-atoms per nm^3
Material density = 3.011 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6628 Angstrom
T1  -- O2  = 1.6774 Angstrom
T1  -- O1  = 1.6631 Angstrom
T1  -- O2  = 1.6773 Angstrom
      mean = 1.6702 Angstrom
        t1 = 0.116331  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.142662  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6628 A <--> 1.6774 A
          Mean   = 1.6702 A
          StdDev = 0.0073 A

       t1 Range  = 0.1163 <-- 0.1163 --> 0.1163
       t2 Range  = 0.1427 <-- 0.1427 --> 0.1427

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 103.641 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  =  81.455 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 131.406 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  = 131.392 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 107.399 deg; O2  -- O2  = 3 A
O1  -- T1  -- O2  = 103.659 deg; O1  -- O2  = 3 A
       81.455 deg <-- 109.825 deg --> 131.406 deg

        O-T-O SUMMARY
          Range  = 81.4554 deg <--> 131.4058 deg
          Mean   = 109.8254 deg
          StdDev = 17.5697 deg

        O--O SUMMARY
          Range  = 2.1700 A <--> 3.0445 A
          Mean   = 2.7024 A
          StdDev = 0.2997 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  79.099 deg; T1  -- T1  = 3.8229 A
T1  - O1  - T1  - O1  - T1  = 168.380 deg; T1  -- T1  = 5.9214 A
T1  - O1  - T1  - O2  - T1  = 110.236 deg; T1  -- T1  = 4.3469 A
T1  - O2  - T1  - O1  - T1  =  92.555 deg; T1  -- T1  = 4.7728 A
T1  - O2  - T1  - O2  - T1  = 168.380 deg; T1  -- T1  = 5.9214 A
T1  - O1  - T1  - O2  - T1  =  79.116 deg; T1  -- T1  = 3.8236 A

        T-T-T SUMMARY
          Range  = 79.0991 deg <--> 168.3795 deg
          Mean   = 116.2942 deg
          StdDev = 38.6384 deg

        T--T SUMMARY
          Range  = 3.8229 A <--> 5.9214 A
          Mean   = 4.7682 A
          StdDev = 0.8860 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 105.618 deg ; T1  -- T1   2.6495 A

T1  -- O2  -- T1  = 159.659 deg ; T1  -- T1   3.3021 A


        T-O-T SUMMARY
          Range  = 105.6177° <--> 159.6593 deg
          Mean   = 132.6385 deg
          StdDev = 27.8042 deg

        T--T SUMMARY
          Range  = 2.6495 A <--> 3.3021 A
          Mean   = 2.9758 A
          StdDev = 0.3357 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.1700 A
O1  -- O1  = 2.1700 A
T1  -- T1  = 2.6495 Angstrom
T1  -- T1  = 2.6495 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 9
Coordination Sequence =
    1 4 12 28 50 76 110 148 194 244 302 364 434 508 590 676 770
TD10 = 1169
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 31
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 31

<TD10> = 1169.000
Average ring size = 6.5455