Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146-2_2_99821_htUwKq.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 17.76 T-atoms per nm^3
Material density = 1.772 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6250 Angstrom
T1  -- O2  = 1.6226 Angstrom
T1  -- O3  = 1.6244 Angstrom
T1  -- O1  = 1.6260 Angstrom
      mean = 1.6245 Angstrom
        t1 = 0.010109  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003431  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6233 Angstrom
T2  -- O3  = 1.6240 Angstrom
T2  -- O4  = 1.6265 Angstrom
T2  -- O4  = 1.6255 Angstrom
      mean = 1.6248 Angstrom
        t1 = 0.010259  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004038  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6226 A <--> 1.6265 A
          Mean   = 1.6247 A
          StdDev = 0.0013 A

       t1 Range  = 0.0101 <-- 0.0102 --> 0.0103
       t2 Range  = 0.0034 <-- 0.0037 --> 0.0040

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.513 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.996 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 108.029 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 110.199 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.756 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.305 deg; O3  -- O1  = 3 A
       108.029 deg <-- 109.466 deg --> 110.513 deg

O2  -- T2  -- O3  = 110.033 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 110.182 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 110.208 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.286 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.116 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 107.975 deg; O4  -- O4  = 3 A
       107.975 deg <-- 109.467 deg --> 110.208 deg

        O-T-O SUMMARY
          Range  = 107.9752 deg <--> 110.5133 deg
          Mean   = 109.4666 deg
          StdDev = 0.8172 deg

        O--O SUMMARY
          Range  = 2.6306 A <--> 2.6686 A
          Mean   = 2.6529 A
          StdDev = 0.0124 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 132.530 deg; T2  -- T1  = 5.4670 A
T2  - O1  - T1  - O3  - T2  = 137.515 deg; T2  -- T2  = 5.6041 A
T2  - O1  - T1  - O1  - T1  = 109.597 deg; T2  -- T1  = 4.8802 A
T1  - O2  - T1  - O3  - T2  =  89.955 deg; T1  -- T2  = 4.1871 A
T1  - O2  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9415 A
T2  - O3  - T1  - O1  - T1  =  90.065 deg; T2  -- T1  = 4.1911 A

T1  - O2  - T2  - O3  - T2  = 110.031 deg; T1  -- T2  = 4.8940 A
T1  - O2  - T2  - O4  - T1  = 137.534 deg; T1  -- T1  = 5.6045 A
T1  - O2  - T2  - O4  - T2  = 132.529 deg; T1  -- T2  = 5.4679 A
T2  - O3  - T2  - O4  - T1  =  90.044 deg; T2  -- T1  = 4.1911 A
T2  - O3  - T2  - O4  - T2  =  60.000 deg; T2  -- T2  = 2.9426 A
T1  - O4  - T2  - O4  - T2  =  89.935 deg; T1  -- T2  = 4.1871 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 137.5341 deg
          Mean   = 103.3112 deg
          StdDev = 27.1403 deg

        T--T SUMMARY
          Range  = 2.9415 A <--> 5.6045 A
          Mean   = 4.5465 A
          StdDev = 0.9177 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.594 deg ; T1  -- T1   2.9415 A

T1  -- O2  -- T2  = 138.016 deg ; T1  -- T2   3.0305 A

T1  -- O3  -- T2  = 133.283 deg ; T1  -- T2   2.9821 A

T2  -- O4  -- T2  = 129.604 deg ; T2  -- T2   2.9426 A


        T-O-T SUMMARY
          Range  = 129.5937° <--> 138.0161 deg
          Mean   = 132.6242 deg
          StdDev = 3.6112 deg

        T--T SUMMARY
          Range  = 2.9415 A <--> 3.0305 A
          Mean   = 2.9742 A
          StdDev = 0.0380 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 8 16 32 49 67 93 123 149 188 230 268 314 369 420 479
TD10 = 730
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

T2 (Si): multiplicity = 3
Coordination Sequence =
    1 4 8 16 32 49 67 93 123 149 188 230 268 314 369 420 479
TD10 = 730
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

<TD10> = 730.000
Average ring size = 6.3871