Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146-2_2_73295_VxKUev.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 19.17 T-atoms per nm^3
Material density = 1.913 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6214 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6215 Angstrom
T1  -- O1  = 1.6215 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.007031  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000303  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6208 Angstrom
T2  -- O3  = 1.6214 Angstrom
T2  -- O4  = 1.6212 Angstrom
T2  -- O4  = 1.6215 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.006982  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000213  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6208 A <--> 1.6215 A
          Mean   = 1.6213 A
          StdDev = 0.0003 A

       t1 Range  = 0.0070 <-- 0.0070 --> 0.0070
       t2 Range  = 0.0002 <-- 0.0003 --> 0.0003

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.402 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.512 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.495 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.497 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.428 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.493 deg; O3  -- O1  = 3 A
       109.402 deg <-- 109.471 deg --> 109.512 deg

O2  -- T2  -- O3  = 109.454 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.455 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.566 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.452 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.449 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 109.452 deg; O4  -- O4  = 3 A
       109.449 deg <-- 109.471 deg --> 109.566 deg

        O-T-O SUMMARY
          Range  = 109.4016 deg <--> 109.5658 deg
          Mean   = 109.4712 deg
          StdDev = 0.0423 deg

        O--O SUMMARY
          Range  = 2.6462 A <--> 2.6489 A
          Mean   = 2.6475 A
          StdDev = 0.0008 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 120.020 deg; T2  -- T2  = 5.2437 A
T2  - O1  - T1  - O3  - T1  =  89.900 deg; T2  -- T1  = 4.2751 A
T2  - O1  - T1  - O1  - T1  = 119.820 deg; T2  -- T1  = 5.2358 A
T2  - O2  - T1  - O3  - T1  = 119.913 deg; T2  -- T1  = 5.2346 A
T2  - O2  - T1  - O1  - T1  =  90.088 deg; T2  -- T1  = 4.2792 A
T1  - O3  - T1  - O1  - T1  = 120.260 deg; T1  -- T1  = 5.2412 A

T1  - O2  - T2  - O3  - T1  = 119.980 deg; T1  -- T1  = 5.2426 A
T1  - O2  - T2  - O4  - T2  =  90.022 deg; T1  -- T2  = 4.2792 A
T1  - O2  - T2  - O4  - T2  = 119.861 deg; T1  -- T2  = 5.2363 A
T1  - O3  - T2  - O4  - T2  = 119.859 deg; T1  -- T2  = 5.2327 A
T1  - O3  - T2  - O4  - T2  =  89.990 deg; T1  -- T2  = 4.2751 A
T2  - O4  - T2  - O4  - T2  = 120.287 deg; T2  -- T2  = 5.2408 A

        T-T-T SUMMARY
          Range  = 89.9004 deg <--> 120.2867 deg
          Mean   = 110.0000 deg
          StdDev = 14.3435 deg

        T--T SUMMARY
          Range  = 4.2751 A <--> 5.2437 A
          Mean   = 4.9180 A
          StdDev = 0.4596 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 137.462 deg ; T1  -- T1   3.0220 A

T1  -- O2  -- T2  = 138.283 deg ; T1  -- T2   3.0292 A

T1  -- O3  -- T2  = 137.761 deg ; T1  -- T2   3.0251 A

T2  -- O4  -- T2  = 137.420 deg ; T2  -- T2   3.0214 A


        T-O-T SUMMARY
          Range  = 137.4195° <--> 138.2833 deg
          Mean   = 137.7315 deg
          StdDev = 0.3601 deg

        T--T SUMMARY
          Range  = 3.0214 A <--> 3.0292 A
          Mean   = 3.0244 A
          StdDev = 0.0032 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

T2 (Si): multiplicity = 3
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 791.000
Average ring size = 5.1429