Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146-2_2_69692_1fiABg.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 15.56 T-atoms per nm^3
Material density = 1.552 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6194 Angstrom
T1  -- O1  = 1.6037 Angstrom
T1  -- O2  = 1.6105 Angstrom
T1  -- O3  = 1.6177 Angstrom
      mean = 1.6128 Angstrom
        t1 = 0.019474  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018657  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6295 Angstrom
T2  -- O2  = 1.6227 Angstrom
T2  -- O3  = 1.6235 Angstrom
T2  -- O4  = 1.6532 Angstrom
      mean = 1.6322 Angstrom
        t1 = 0.048315  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032517  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6037 A <--> 1.6532 A
          Mean   = 1.6225 A
          StdDev = 0.0141 A

       t1 Range  = 0.0195 <-- 0.0339 --> 0.0483
       t2 Range  = 0.0187 <-- 0.0256 --> 0.0325

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.326 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 105.692 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.376 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 110.538 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.668 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 114.244 deg; O2  -- O3  = 3 A
       105.668 deg <-- 109.474 deg --> 114.244 deg

O4  -- T2  -- O2  = 125.045 deg; O4  -- O2  = 3 A
O4  -- T2  -- O3  = 106.150 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 107.235 deg; O4  -- O4  = 3 A
O2  -- T2  -- O3  = 102.318 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 102.378 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 114.004 deg; O3  -- O4  = 3 A
       102.318 deg <-- 109.522 deg --> 125.045 deg

        O-T-O SUMMARY
          Range  = 102.3176 deg <--> 125.0452 deg
          Mean   = 109.4978 deg
          StdDev = 6.1196 deg

        O--O SUMMARY
          Range  = 2.5284 A <--> 2.8853 A
          Mean   = 2.6463 A
          StdDev = 0.0967 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.8579 A
T1  - O1  - T1  - O2  - T2  = 119.682 deg; T1  -- T2  = 5.1561 A
T1  - O1  - T1  - O3  - T2  =  91.914 deg; T1  -- T2  = 4.2988 A
T1  - O1  - T1  - O2  - T2  = 144.989 deg; T1  -- T2  = 5.6860 A
T1  - O1  - T1  - O3  - T2  =  88.623 deg; T1  -- T2  = 4.1781 A
T2  - O2  - T1  - O3  - T2  = 125.358 deg; T2  -- T2  = 5.5270 A

T1  - O4  - T2  - O2  - T1  = 126.599 deg; T1  -- T1  = 5.5576 A
T1  - O4  - T2  - O3  - T2  =  87.809 deg; T1  -- T2  = 4.1781 A
T1  - O4  - T2  - O4  - T2  =  91.048 deg; T1  -- T2  = 4.2988 A
T1  - O2  - T2  - O3  - T2  = 145.581 deg; T1  -- T2  = 5.7388 A
T1  - O2  - T2  - O4  - T2  = 113.768 deg; T1  -- T2  = 5.0328 A
T2  - O3  - T2  - O4  - T2  =  60.000 deg; T2  -- T2  = 2.9038 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 145.5809 deg
          Mean   = 104.6143 deg
          StdDev = 28.3809 deg

        T--T SUMMARY
          Range  = 2.8579 A <--> 5.7388 A
          Mean   = 4.6178 A
          StdDev = 0.9796 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 124.921 deg ; T1  -- T1   2.8579 A

T1  -- O2  -- T2  = 147.457 deg ; T1  -- T2   3.1037 A

T1  -- O3  -- T2  = 148.209 deg ; T1  -- T2   3.1172 A

T2  -- O4  -- T2  = 124.391 deg ; T2  -- T2   2.9038 A


        T-O-T SUMMARY
          Range  = 124.3908° <--> 148.2086 deg
          Mean   = 136.2444 deg
          StdDev = 12.1085 deg

        T--T SUMMARY
          Range  = 2.8579 A <--> 3.1172 A
          Mean   = 2.9957 A
          StdDev = 0.1212 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 8 16 32 49 67 93 123 149 188 230 268 314 369 420 479
TD10 = 730
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

T2 (Si): multiplicity = 3
Coordination Sequence =
    1 4 8 16 32 49 67 93 123 149 188 230 268 314 369 420 479
TD10 = 730
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

<TD10> = 730.000
Average ring size = 6.3871