Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_146-2_1_70_qjJHP_.cif"

There are 3 T-atoms per unit cell
There are 6 O-atoms per unit cell

Framework density = 27.46 T-atoms per nm^3
Material density = 2.739 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6284 Angstrom
T1  -- O1  = 1.6289 Angstrom
T1  -- O2  = 1.6288 Angstrom
T1  -- O2  = 1.6287 Angstrom
      mean = 1.6287 Angstrom
        t1 = 0.178825  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.130620  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6284 A <--> 1.6289 A
          Mean   = 1.6287 A
          StdDev = 0.0002 A

       t1 Range  = 0.1788 <-- 0.1788 --> 0.1788
       t2 Range  = 0.1306 <-- 0.1306 --> 0.1306

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  80.120 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  81.584 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 132.998 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 133.006 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  81.672 deg; O1  -- O2  = 2 A
O2  -- T1  -- O2  =  80.028 deg; O2  -- O2  = 2 A
       80.028 deg <-- 98.234 deg --> 133.006 deg

        O-T-O SUMMARY
          Range  = 80.0282 deg <--> 133.0056 deg
          Mean   = 98.2345 deg
          StdDev = 25.3053 deg

        O--O SUMMARY
          Range  = 2.0945 A <--> 2.9876 A
          Mean   = 2.4039 A
          StdDev = 0.4247 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.8913 A
T1  - O1  - T1  - O2  - T1  = 119.952 deg; T1  -- T1  = 5.0071 A
T1  - O1  - T1  - O2  - T1  = 179.952 deg; T1  -- T1  = 5.7831 A
T1  - O1  - T1  - O2  - T1  = 179.952 deg; T1  -- T1  = 5.7831 A
T1  - O1  - T1  - O2  - T1  = 120.048 deg; T1  -- T1  = 5.0095 A
T1  - O2  - T1  - O2  - T1  =  60.000 deg; T1  -- T1  = 2.8919 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 179.9524 deg
          Mean   = 119.9841 deg
          StdDev = 50.3901 deg

        T--T SUMMARY
          Range  = 2.8913 A <--> 5.7831 A
          Mean   = 4.5610 A
          StdDev = 1.2575 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.149 deg ; T1  -- T1   2.8913 A

T1  -- O2  -- T1  = 125.183 deg ; T1  -- T1   2.8919 A


        T-O-T SUMMARY
          Range  = 125.1486° <--> 125.1833 deg
          Mean   = 125.1659 deg
          StdDev = 0.0190 deg

        T--T SUMMARY
          Range  = 2.8913 A <--> 2.8919 A
          Mean   = 2.8916 A
          StdDev = 0.0003 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.0964 A
O1  -- O1  = 2.0964 A
O1  -- O2  = 2.1302 A
O1  -- O2  = 2.1280 A
O2  -- O2  = 2.0945 A
O2  -- O2  = 2.0945 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 8 14 18 22 28 30 38 38 48 46 58 54 68 62 78
TD10 = 249
Circuit symbol = 3.3.6.6.7_{2}.7_{2}
Weight = 11
Vertex symbol  = 3.3.6.6.*.*
Weight = 11

<TD10> = 249.000
Average ring size = 4.0000