Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_145_2_9940_3MzeLG.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 21.82 T-atoms per nm^3
Material density = 2.177 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6230 Angstrom
T1  -- O2  = 1.6166 Angstrom
T1  -- O3  = 1.6172 Angstrom
T1  -- O1  = 1.6232 Angstrom
      mean = 1.6200 Angstrom
        t1 = 0.007178  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002334  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6171 Angstrom
T2  -- O4  = 1.6225 Angstrom
T2  -- O2  = 1.6167 Angstrom
T2  -- O4  = 1.6220 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.006657  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003730  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6166 A <--> 1.6232 A
          Mean   = 1.6198 A
          StdDev = 0.0030 A

       t1 Range  = 0.0067 <-- 0.0069 --> 0.0072
       t2 Range  = 0.0023 <-- 0.0030 --> 0.0037

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.025 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.324 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.705 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 108.809 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.846 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 110.109 deg; O3  -- O1  = 3 A
       108.809 deg <-- 109.470 deg --> 110.109 deg

O3  -- T2  -- O4  = 109.199 deg; O3  -- O4  = 3 A
O3  -- T2  -- O2  = 108.917 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 109.752 deg; O3  -- O4  = 3 A
O4  -- T2  -- O2  = 109.218 deg; O4  -- O2  = 3 A
O4  -- T2  -- O4  = 109.634 deg; O4  -- O4  = 3 A
O2  -- T2  -- O4  = 110.099 deg; O2  -- O4  = 3 A
       108.917 deg <-- 109.470 deg --> 110.099 deg

        O-T-O SUMMARY
          Range  = 108.8090 deg <--> 110.1086 deg
          Mean   = 109.4698 deg
          StdDev = 0.4349 deg

        O--O SUMMARY
          Range  = 2.6296 A <--> 2.6561 A
          Mean   = 2.6451 A
          StdDev = 0.0089 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 120.020 deg; T1  -- T2  = 5.2897 A
T1  - O1  - T1  - O3  - T1  = 104.719 deg; T1  -- T1  = 4.7641 A
T1  - O1  - T1  - O1  - T2  =  98.899 deg; T1  -- T2  = 4.6411 A
T2  - O2  - T1  - O3  - T1  = 114.481 deg; T2  -- T1  = 5.1360 A
T2  - O2  - T1  - O1  - T2  = 123.987 deg; T2  -- T2  = 5.4725 A
T1  - O3  - T1  - O1  - T2  =  89.317 deg; T1  -- T2  = 4.2934 A

T1  - O3  - T2  - O4  - T2  =  99.016 deg; T1  -- T2  = 4.6458 A
T1  - O3  - T2  - O2  - T1  = 124.014 deg; T1  -- T1  = 5.4732 A
T1  - O3  - T2  - O4  - T2  =  89.124 deg; T1  -- T2  = 4.2866 A
T2  - O4  - T2  - O2  - T1  = 120.172 deg; T2  -- T1  = 5.2951 A
T2  - O4  - T2  - O4  - T2  = 104.681 deg; T2  -- T2  = 4.7649 A
T1  - O2  - T2  - O4  - T2  = 114.335 deg; T1  -- T2  = 5.1332 A

        T-T-T SUMMARY
          Range  = 89.1242 deg <--> 124.0135 deg
          Mean   = 108.5638 deg
          StdDev = 12.3299 deg

        T--T SUMMARY
          Range  = 4.2866 A <--> 5.4732 A
          Mean   = 4.9330 A
          StdDev = 0.4113 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 135.845 deg ; T1  -- T1   3.0082 A

T1  -- O2  -- T2  = 146.897 deg ; T1  -- T2   3.0994 A

T1  -- O3  -- T2  = 146.740 deg ; T1  -- T2   3.0990 A

T2  -- O4  -- T2  = 136.114 deg ; T2  -- T2   3.0094 A


        T-O-T SUMMARY
          Range  = 135.8455° <--> 146.8966 deg
          Mean   = 141.3990 deg
          StdDev = 5.6614 deg

        T--T SUMMARY
          Range  = 3.0082 A <--> 3.0994 A
          Mean   = 3.0540 A
          StdDev = 0.0472 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 3
Coordination Sequence =
    1 4 12 26 44 72 104 138 178 228 282 340 402 472 550 632 714
TD10 = 1089
Circuit symbol = 5.5.5.5.5.8_{6}
Weight = 27
Vertex symbol  = 5.5.5.5.5.8_{4}
Weight = 27

T2 (Si): multiplicity = 3
Coordination Sequence =
    1 4 12 26 44 72 104 138 178 228 282 340 402 472 550 632 714
TD10 = 1089
Circuit symbol = 5.5.5.5.5.8_{6}
Weight = 27
Vertex symbol  = 5.5.5.5.5.8_{4}
Weight = 27

<TD10> = 1089.000
Average ring size = 6.0000