Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_142-2_2_302414_jGcsX7.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 25.72 T-atoms per nm^3
Material density = 2.566 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6326 Angstrom
T1  -- O2  = 1.6145 Angstrom
T1  -- O1  = 1.6326 Angstrom
T1  -- O2  = 1.6145 Angstrom
      mean = 1.6235 Angstrom
        t1 = 0.017651  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012809  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6325 Angstrom
T2  -- O2  = 1.6188 Angstrom
T2  -- O2  = 1.6188 Angstrom
T2  -- O1  = 1.6326 Angstrom
      mean = 1.6257 Angstrom
        t1 = 0.019274  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010681  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6145 A <--> 1.6326 A
          Mean   = 1.6246 A
          StdDev = 0.0081 A

       t1 Range  = 0.0177 <-- 0.0185 --> 0.0193
       t2 Range  = 0.0107 <-- 0.0117 --> 0.0128

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.493 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 110.644 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 111.004 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  = 111.004 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 105.075 deg; O2  -- O2  = 3 A
O1  -- T1  -- O2  = 109.493 deg; O1  -- O2  = 3 A
       105.075 deg <-- 109.452 deg --> 111.004 deg

O1  -- T2  -- O2  = 110.445 deg; O1  -- O2  = 3 A
O1  -- T2  -- O2  = 109.822 deg; O1  -- O2  = 3 A
O1  -- T2  -- O1  = 111.614 deg; O1  -- O1  = 3 A
O2  -- T2  -- O2  = 104.463 deg; O2  -- O2  = 3 A
O2  -- T2  -- O1  = 109.822 deg; O2  -- O1  = 3 A
O2  -- T2  -- O1  = 110.445 deg; O2  -- O1  = 3 A
       104.463 deg <-- 109.435 deg --> 111.614 deg

        O-T-O SUMMARY
          Range  = 104.4626 deg <--> 111.6137 deg
          Mean   = 109.4437 deg
          StdDev = 2.1863 deg

        O--O SUMMARY
          Range  = 2.5594 A <--> 2.7007 A
          Mean   = 2.6522 A
          StdDev = 0.0428 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 149.254 deg; T2  -- T2  = 5.8953 A
T2  - O1  - T1  - O1  - T2  = 104.883 deg; T2  -- T2  = 4.8469 A
T2  - O1  - T1  - O2  - T2  =  84.012 deg; T2  -- T2  = 4.0637 A
T2  - O2  - T1  - O1  - T2  =  82.623 deg; T2  -- T2  = 4.0637 A
T2  - O2  - T1  - O2  - T2  = 104.883 deg; T2  -- T2  = 4.8469 A
T2  - O1  - T1  - O2  - T2  = 149.254 deg; T2  -- T2  = 5.8953 A

T1  - O1  - T2  - O2  - T1  =  96.683 deg; T1  -- T1  = 4.5680 A
T1  - O1  - T2  - O2  - T1  = 111.513 deg; T1  -- T1  = 5.0543 A
T1  - O1  - T2  - O1  - T1  = 140.642 deg; T1  -- T1  = 5.7178 A
T1  - O2  - T2  - O2  - T1  =  88.342 deg; T1  -- T1  = 4.2893 A
T1  - O2  - T2  - O1  - T1  = 111.513 deg; T1  -- T1  = 5.0543 A
T1  - O2  - T2  - O1  - T1  =  96.683 deg; T1  -- T1  = 4.5680 A

        T-T-T SUMMARY
          Range  = 82.6232 deg <--> 149.2545 deg
          Mean   = 110.0238 deg
          StdDev = 22.9907 deg

        T--T SUMMARY
          Range  = 4.0637 A <--> 5.8953 A
          Mean   = 4.9053 A
          StdDev = 0.6263 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 141.003 deg ; T1  -- T2   3.0778 A

T1  -- O2  -- T2  = 139.775 deg ; T1  -- T2   3.0362 A


        T-O-T SUMMARY
          Range  = 139.7750° <--> 141.0028 deg
          Mean   = 140.3889 deg
          StdDev = 0.6237 deg

        T--T SUMMARY
          Range  = 3.0362 A <--> 3.0778 A
          Mean   = 3.0570 A
          StdDev = 0.0212 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 24 42 64 92 124 162 204 252 304 362 424 492 564 642
TD10 = 979
Circuit symbol = 4.4.8_{2}.8_{2}.8_{8}.8_{8}
Weight = 43
Vertex symbol  = 4.4.8_{2}.8_{2}.8_{8}.8_{8}
Weight = 43

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 24 42 64 90 124 162 204 250 304 362 424 490 564 642
TD10 = 975
Circuit symbol = 4.4.8_{7}.8_{7}.8_{7}.8_{7}
Weight = 51
Vertex symbol  = 4.4.8_{7}.8_{7}.8_{7}.8_{7}
Weight = 51

<TD10> = 977.000
Average ring size = 7.4286