Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_141_4_2430861_MoHSk7.cif"

There are 112 T-atoms per unit cell
There are 224 O-atoms per unit cell

Framework density = 19.18 T-atoms per nm^3
Material density = 1.913 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5506 Angstrom
T1  -- O2  = 1.6137 Angstrom
T1  -- O3  = 1.6682 Angstrom
T1  -- O4  = 1.6381 Angstrom
      mean = 1.6177 Angstrom
        t1 = 0.102126  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076417  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6640 Angstrom
T2  -- O5  = 1.6231 Angstrom
T2  -- O6  = 1.6739 Angstrom
T2  -- O7  = 1.6168 Angstrom
      mean = 1.6445 Angstrom
        t1 = 0.038501  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048900  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6146 Angstrom
T3  -- O8  = 1.6178 Angstrom
T3  -- O9  = 1.6249 Angstrom
T3  -- O10 = 1.6185 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.006867  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002553  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6207 Angstrom
T4  -- O11 = 1.6209 Angstrom
T4  -- O10 = 1.6207 Angstrom
T4  -- O11 = 1.6209 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.008139  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006242  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5506 A <--> 1.6739 A
          Mean   = 1.6261 A
          StdDev = 0.0292 A

       t1 Range  = 0.0069 <-- 0.0389 --> 0.1021
       t2 Range  = 0.0026 <-- 0.0335 --> 0.0764

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.427 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.279 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  78.524 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 114.560 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.994 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.762 deg; O3  -- O4  = 3 A
       78.524 deg <-- 108.591 deg --> 119.279 deg

O4  -- T2  -- O5  = 105.904 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 118.742 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 107.750 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 106.753 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.029 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.364 deg; O6  -- O7  = 3 A
       105.904 deg <-- 109.424 deg --> 118.742 deg

O7  -- T3  -- O8  = 108.980 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.375 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 109.225 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 109.564 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.234 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 110.438 deg; O9  -- O10 = 3 A
       108.980 deg <-- 109.470 deg --> 110.438 deg

O10 -- T4  -- O11 = 109.238 deg; O10 -- O11 = 3 A
O10 -- T4  -- O10 = 108.071 deg; O10 -- O10 = 3 A
O10 -- T4  -- O11 = 109.959 deg; O10 -- O11 = 3 A
O11 -- T4  -- O10 = 109.959 deg; O11 -- O10 = 3 A
O11 -- T4  -- O11 = 110.340 deg; O11 -- O11 = 3 A
O10 -- T4  -- O11 = 109.238 deg; O10 -- O11 = 3 A
       108.071 deg <-- 109.468 deg --> 110.340 deg

        O-T-O SUMMARY
          Range  = 78.5236 deg <--> 119.2786 deg
          Mean   = 108.7738 deg
          StdDev = 7.4025 deg

        O--O SUMMARY
          Range  = 2.0192 A <--> 2.8722 A
          Mean   = 2.6396 A
          StdDev = 0.1506 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  87.293 deg; T1  -- T2  = 3.9863 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.2367 A
T1  - O1  - T1  - O4  - T1  = 180.000 deg; T1  -- T1  = 5.0499 A
T2  - O2  - T1  - O3  - T1  = 127.713 deg; T2  -- T1  = 5.7895 A
T2  - O2  - T1  - O4  - T1  =  92.707 deg; T2  -- T1  = 4.0433 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1131 A

T1  - O4  - T2  - O5  - T2  =  87.293 deg; T1  -- T2  = 4.0433 A
T1  - O4  - T2  - O6  - T2  = 127.713 deg; T1  -- T2  = 5.4566 A
T1  - O4  - T2  - O7  - T3  = 127.995 deg; T1  -- T3  = 5.6574 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.0135 A
T2  - O5  - T2  - O7  - T3  = 132.100 deg; T2  -- T3  = 5.3838 A
T2  - O6  - T2  - O7  - T3  =  90.186 deg; T2  -- T3  = 4.3393 A

T2  - O7  - T3  - O8  - T3  =  89.814 deg; T2  -- T3  = 4.3393 A
T2  - O7  - T3  - O9  - T4  = 124.428 deg; T2  -- T4  = 5.5195 A
T2  - O7  - T3  - O10 - T3  = 132.100 deg; T2  -- T3  = 5.7590 A
T3  - O8  - T3  - O9  - T4  = 130.403 deg; T3  -- T4  = 5.4856 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.3187 A
T4  - O9  - T3  - O10 - T3  =  90.149 deg; T4  -- T3  = 4.3905 A

T3  - O10 - T4  - O11 - T4  = 130.403 deg; T3  -- T4  = 5.6435 A
T3  - O10 - T4  - O10 - T4  =  89.851 deg; T3  -- T4  = 4.3905 A
T3  - O10 - T4  - O11 - T3  = 125.680 deg; T3  -- T3  = 5.4611 A
T4  - O11 - T4  - O10 - T4  =  90.000 deg; T4  -- T4  = 4.4515 A
T4  - O11 - T4  - O11 - T3  =  89.851 deg; T4  -- T3  = 4.3905 A
T4  - O10 - T4  - O11 - T3  = 130.403 deg; T4  -- T3  = 5.6435 A

        T-T-T SUMMARY
          Range  = 87.2933 deg <--> 180.0000 deg
          Mean   = 110.8786 deg
          StdDev = 24.5377 deg

        T--T SUMMARY
          Range  = 3.9863 A <--> 5.7895 A
          Mean   = 4.8550 A
          StdDev = 0.6602 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 115.804 deg ; T1  -- T1   2.6272 A

T1  -- O2  -- T1  =  97.295 deg ; T1  -- T1   2.4227 A

T1  -- O3  -- T1  = 170.058 deg ; T1  -- T1   3.3238 A

T1  -- O4  -- T2  = 142.270 deg ; T1  -- T2   3.1247 A

T2  -- O5  -- T2  = 113.696 deg ; T2  -- T2   2.7179 A

T2  -- O6  -- T2  = 123.804 deg ; T2  -- T2   2.9532 A

T2  -- O7  -- T3  = 157.575 deg ; T2  -- T3   3.1698 A

T3  -- O8  -- T3  = 150.887 deg ; T3  -- T3   3.1317 A

T3  -- O9  -- T3  = 132.431 deg ; T3  -- T3   2.9738 A

T3  -- O10 -- T4  = 142.679 deg ; T3  -- T4   3.0689 A

T4  -- O11 -- T4  = 152.321 deg ; T4  -- T4   3.1477 A


        T-O-T SUMMARY
          Range  = 97.2953° <--> 170.0582 deg
          Mean   = 135.4913 deg
          StdDev = 21.0219 deg

        T--T SUMMARY
          Range  = 2.4227 A <--> 3.3238 A
          Mean   = 2.9607 A
          StdDev = 0.2624 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.0192 A
O1  -- O4  = 2.0192 A
T1  -- T1  = 2.6272 Angstrom
T1  -- T1  = 2.4227 Angstrom
T2  -- T2  = 2.7179 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

<TD10> = 726.000
Average ring size = 5.6000