Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_141_4_1944535_QCUZbJ.cif"

There are 128 T-atoms per unit cell
There are 256 O-atoms per unit cell

Framework density = 19.30 T-atoms per nm^3
Material density = 1.926 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6284 Angstrom
T1  -- O2  = 1.6326 Angstrom
T1  -- O3  = 1.5613 Angstrom
T1  -- O4  = 1.5767 Angstrom
      mean = 1.5997 Angstrom
        t1 = 0.036907  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024035  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5442 Angstrom
T2  -- O5  = 1.6140 Angstrom
T2  -- O6  = 1.6454 Angstrom
T2  -- O7  = 1.6571 Angstrom
      mean = 1.6152 Angstrom
        t1 = 0.025106  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026103  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6040 Angstrom
T3  -- O7  = 1.6449 Angstrom
T3  -- O8  = 1.5431 Angstrom
T3  -- O9  = 1.6724 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.054851  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.070569  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.5192 Angstrom
T4  -- O9  = 1.6739 Angstrom
T4  -- O10 = 1.6380 Angstrom
T4  -- O11 = 1.5995 Angstrom
      mean = 1.6077 Angstrom
        t1 = 0.027245  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024984  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5192 A <--> 1.6739 A
          Mean   = 1.6097 A
          StdDev = 0.0468 A

       t1 Range  = 0.0251 <-- 0.0360 --> 0.0549
       t2 Range  = 0.0240 <-- 0.0364 --> 0.0706

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.376 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.581 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.151 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.238 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.834 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 100.167 deg; O3  -- O4  = 2 A
       100.167 deg <-- 109.391 deg --> 112.834 deg

O3  -- T2  -- O5  = 109.042 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 106.158 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.716 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.923 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.516 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 112.393 deg; O6  -- O7  = 3 A
       106.158 deg <-- 109.458 deg --> 112.393 deg

O4  -- T3  -- O7  = 112.043 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  =  98.070 deg; O4  -- O8  = 2 A
O4  -- T3  -- O9  = 112.719 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 104.501 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 116.101 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 111.604 deg; O8  -- O9  = 3 A
       98.070 deg <-- 109.173 deg --> 116.101 deg

O8  -- T4  -- O9  = 113.018 deg; O8  -- O9  = 3 A
O8  -- T4  -- O10 = 107.708 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 107.151 deg; O8  -- O11 = 3 A
O9  -- T4  -- O10 = 110.173 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 108.957 deg; O9  -- O11 = 3 A
O10 -- T4  -- O11 = 109.760 deg; O10 -- O11 = 3 A
       107.151 deg <-- 109.461 deg --> 113.018 deg

        O-T-O SUMMARY
          Range  = 98.0696 deg <--> 116.1013 deg
          Mean   = 109.3053 deg
          StdDev = 4.0498 deg

        O--O SUMMARY
          Range  = 2.3767 A <--> 2.8148 A
          Mean   = 2.6236 A
          StdDev = 0.1022 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T3  =  98.466 deg; T2  -- T3  = 4.4030 A
T2  - O1  - T1  - O3  - T1  =  90.504 deg; T2  -- T1  = 4.1180 A
T2  - O1  - T1  - O4  - T1  =  87.600 deg; T2  -- T1  = 4.2567 A
T3  - O2  - T1  - O3  - T1  = 155.890 deg; T3  -- T1  = 5.6977 A
T3  - O2  - T1  - O4  - T1  =  89.621 deg; T3  -- T1  = 4.3523 A
T1  - O3  - T1  - O4  - T1  = 113.199 deg; T1  -- T1  = 5.1391 A

T1  - O3  - T2  - O5  - T2  = 152.224 deg; T1  -- T2  = 5.6095 A
T1  - O3  - T2  - O6  - T2  =  89.496 deg; T1  -- T2  = 4.1180 A
T1  - O3  - T2  - O7  - T3  =  92.879 deg; T1  -- T3  = 4.3523 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.1312 A
T2  - O5  - T2  - O7  - T3  = 112.148 deg; T2  -- T3  = 4.9762 A
T2  - O6  - T2  - O7  - T3  = 116.063 deg; T2  -- T3  = 5.1468 A

T1  - O4  - T3  - O7  - T2  =  89.744 deg; T1  -- T2  = 4.2567 A
T1  - O4  - T3  - O8  - T4  = 132.898 deg; T1  -- T4  = 5.1286 A
T1  - O4  - T3  - O9  - T4  = 126.319 deg; T1  -- T4  = 5.5626 A
T2  - O7  - T3  - O8  - T4  = 104.220 deg; T2  -- T4  = 4.5715 A
T2  - O7  - T3  - O9  - T4  = 133.071 deg; T2  -- T4  = 5.8898 A
T4  - O8  - T3  - O9  - T4  =  74.352 deg; T4  -- T4  = 3.6510 A

T3  - O8  - T4  - O9  - T3  =  88.571 deg; T3  -- T3  = 4.2027 A
T3  - O8  - T4  - O10 - T4  = 115.288 deg; T3  -- T4  = 4.7493 A
T3  - O8  - T4  - O11 - T4  = 119.178 deg; T3  -- T4  = 4.9681 A
T3  - O9  - T4  - O10 - T4  = 110.176 deg; T3  -- T4  = 5.1353 A
T3  - O9  - T4  - O11 - T4  = 135.174 deg; T3  -- T4  = 5.9108 A
T4  - O10 - T4  - O11 - T4  =  90.000 deg; T4  -- T4  = 4.2645 A

        T-T-T SUMMARY
          Range  = 74.3519 deg <--> 155.8898 deg
          Mean   = 109.6821 deg
          StdDev = 21.7793 deg

        T--T SUMMARY
          Range  = 3.6510 A <--> 5.9108 A
          Mean   = 4.8085 A
          StdDev = 0.6356 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 170.722 deg ; T1  -- T1   3.2461 A

T1  -- O2  -- T1  = 125.704 deg ; T1  -- T1   2.9055 A

T1  -- O3  -- T2  = 137.342 deg ; T1  -- T2   2.8928 A

T1  -- O4  -- T3  = 133.347 deg ; T1  -- T3   2.9207 A

T2  -- O5  -- T2  = 126.738 deg ; T2  -- T2   2.8855 A

T2  -- O6  -- T2  = 127.892 deg ; T2  -- T2   2.9564 A

T2  -- O7  -- T3  = 140.693 deg ; T2  -- T3   3.1097 A

T3  -- O8  -- T4  = 121.580 deg ; T3  -- T4   2.6729 A

T3  -- O9  -- T4  = 163.219 deg ; T3  -- T4   3.3104 A

T4  -- O10 -- T4  = 140.438 deg ; T4  -- T4   3.0827 A

T4  -- O11 -- T4  = 134.181 deg ; T4  -- T4   2.9467 A


        T-O-T SUMMARY
          Range  = 121.5797° <--> 170.7219 deg
          Mean   = 138.3505 deg
          StdDev = 14.8076 deg

        T--T SUMMARY
          Range  = 2.6729 A <--> 3.3104 A
          Mean   = 2.9936 A
          StdDev = 0.1726 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T3  -- T4  = 2.6729 Angstrom
T4  -- T3  = 2.6729 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 33 49 71 97 127 161 198 238 279 328 386 451 516
TD10 = 769
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{4}.8.8_{2}
Weight = 29

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 16 28 49 74 96 119 151 191 235 283 332 380 431 494
TD10 = 738
Circuit symbol = 4.4.4.6_{2}.6.6_{2}
Weight = 15
Vertex symbol  = 4.4.4.6_{2}.6.8
Weight = 20

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 18 31 50 70 95 125 159 196 233 280 331 387 446 505
TD10 = 759
Circuit symbol = 4.4.6.8_{4}.6_{2}.8_{2}
Weight = 21
Vertex symbol  = 4.4.6.8.6_{2}.8
Weight = 21

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 72 96 122 155 196 240 285 335 389 441 496
TD10 = 759
Circuit symbol = 4.4.6.6_{3}.6_{3}.8_{5}
Weight = 21
Vertex symbol  = 4.4.6.6_{3}.6_{3}.8
Weight = 21

<TD10> = 756.250
Average ring size = 5.7223