Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_141-2_1_7p_gFY_eP.cif"

There are 16 T-atoms per unit cell
There are 56 O-atoms per unit cell

Framework density = 17.53 T-atoms per nm^3
Material density = 2.448 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6145 Angstrom
T1  -- O1  = 1.8245 Angstrom
T1  -- O3  = 1.4900 Angstrom
T1  -- O3  = 1.4900 Angstrom
T1  -- O1  = 2.0299 Angstrom
T1  -- O2  = 1.6101 Angstrom
T1  -- O3  = 1.6163 Angstrom
T1  -- O3  = 1.6163 Angstrom
      mean = 1.6615 Angstrom

        T-O SUMMARY
          Range  = 1.4900 A <--> 2.0299 A
          Mean   = 1.6615 A
          StdDev = 0.1702 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  17.732 deg; O1  -- O1  = 1 A
O1  -- T1  -- O3  =  75.101 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  =  75.101 deg; O1  -- O3  = 2 A
O1  -- T1  -- O1  = 157.569 deg; O1  -- O1  = 4 A
O1  -- T1  -- O2  = 110.065 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.827 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 108.827 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  68.879 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  =  68.879 deg; O1  -- O3  = 2 A
O1  -- T1  -- O1  = 139.836 deg; O1  -- O1  = 4 A
O1  -- T1  -- O2  = 127.798 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  99.389 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  99.389 deg; O1  -- O3  = 3 A
O3  -- T1  -- O3  = 125.482 deg; O3  -- O3  = 3 A
O3  -- T1  -- O1  =  95.338 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 116.375 deg; O3  -- O2  = 3 A
O3  -- T1  -- O3  = 129.193 deg; O3  -- O3  = 3 A
O3  -- T1  -- O3  =  34.410 deg; O3  -- O3  = 1 A
O3  -- T1  -- O1  =  95.338 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 116.375 deg; O3  -- O2  = 3 A
O3  -- T1  -- O3  =  34.410 deg; O3  -- O3  = 1 A
O3  -- T1  -- O3  = 129.193 deg; O3  -- O3  = 3 A
O1  -- T1  -- O2  =  92.366 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  61.379 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  =  61.379 deg; O1  -- O3  = 2 A
O2  -- T1  -- O3  = 109.521 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 109.521 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  = 110.066 deg; O3  -- O3  = 3 A
       17.732 deg <-- 95.633 deg --> 157.569 deg

        O-T-O SUMMARY
          Range  = 17.7324 deg <--> 157.5687 deg
          Mean   = 94.2021 deg
          StdDev = 30.7420 deg

        O--O SUMMARY
          Range  = 0.5692 A <--> 3.6208 A
          Mean   = 2.3402 A
          StdDev = 0.6384 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 162.268 deg ; T1  -- T1   3.3981 A
T1  -- O1  -- T1  =   2.589 deg ; T1  -- T1   0.4234 A
T1  -- O1  -- T1  = 159.678 deg ; T1  -- T1   3.7941 A

T1  -- O2  -- T1  =  15.110 deg ; T1  -- T1   0.4234 A

T1  -- O3  -- T1  =  14.962 deg ; T1  -- T1   0.4234 A


        T-O-T SUMMARY
          Range  = 2.5894° <--> 162.2676 deg
          Mean   = 70.9213 deg
          StdDev = 74.1365 deg

        T--T SUMMARY
          Range  = 0.4234 A <--> 3.7941 A
          Mean   = 1.6925 A
          StdDev = 1.5692 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 0.5692 A
O1  -- O3  = 1.8947 A
O1  -- O3  = 1.8947 A
O1  -- O3  = 1.8947 A
O1  -- O3  = 1.8947 A
O3  -- O3  = 0.9267 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 2 neighboring T-atoms within 3.50 A, but 8 bridging O-atoms
  T1  -- T1  = 3.3981 Angstrom
  T1  -- T1  = 0.4234 Angstrom