Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_140_1_6_UB5277.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.4201 Angstrom
T1  -- O2  = 1.8450 Angstrom
T1  -- O3  = 1.6751 Angstrom
T1  -- O2  = 1.8450 Angstrom
T1  -- O4  = 1.8811 Angstrom
      mean = 1.7333 Angstrom

        T-O SUMMARY
          Range  = 1.4201 A <--> 1.8811 A
          Mean   = 1.7333 A
          StdDev = 0.1727 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  89.459 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 136.573 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  =  89.459 deg; O1  -- O2  = 2 A
O1  -- T1  -- O4  =  70.893 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 108.605 deg; O2  -- O3  = 3 A
O2  -- T1  -- O2  =  79.054 deg; O2  -- O2  = 2 A
O2  -- T1  -- O4  = 157.258 deg; O2  -- O4  = 4 A
O3  -- T1  -- O2  = 131.866 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  =  93.775 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  =  89.137 deg; O2  -- O4  = 3 A
       70.893 deg <-- 104.608 deg --> 157.258 deg

        O-T-O SUMMARY
          Range  = 70.8927 deg <--> 157.2580 deg
          Mean   = 104.6081 deg
          StdDev = 26.8387 deg

        O--O SUMMARY
          Range  = 1.9510 A <--> 3.6530 A
          Mean   = 2.6755 A
          StdDev = 0.4725 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  90.822 deg ; T1  -- T1   2.0227 A

T1  -- O2  -- T1  = 112.969 deg ; T1  -- T1   3.0765 A
T1  -- O2  -- T1  =  66.482 deg ; T1  -- T1   2.0227 A
T1  -- O2  -- T1  = 172.394 deg ; T1  -- T1   3.6819 A
T1  -- O2  -- T1  = 172.394 deg ; T1  -- T1   3.6819 A
T1  -- O2  -- T1  =  66.482 deg ; T1  -- T1   2.0227 A
T1  -- O2  -- T1  = 112.969 deg ; T1  -- T1   3.0765 A

T1  -- O3  -- T1  = 147.440 deg ; T1  -- T1   3.2158 A

T1  -- O4  -- T1  = 157.840 deg ; T1  -- T1   3.6922 A


        T-O-T SUMMARY
          Range  = 66.4820° <--> 172.3936 deg
          Mean   = 122.1991 deg
          StdDev = 39.9443 deg

        T--T SUMMARY
          Range  = 2.0227 A <--> 3.6922 A
          Mean   = 2.9436 A
          StdDev = 0.6927 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.2822 A
O1  -- O4  = 1.9510 A
O1  -- O1  = 2.2822 A
O1  -- O4  = 1.9510 A

T-T-T analysis was not conducted.
T1  -- T1  = 2.0227 Angstrom