Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_13_2_265761_hzJKFT.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 26.63 T-atoms per nm^3
Material density = 2.657 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6355 Angstrom
T1  -- O2  = 1.6131 Angstrom
T1  -- O3  = 1.7490 Angstrom
T1  -- O4  = 1.6362 Angstrom
      mean = 1.6584 Angstrom
        t1 = 0.070074  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039583  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6208 Angstrom
T2  -- O3  = 1.6208 Angstrom
T2  -- O4  = 1.6315 Angstrom
T2  -- O4  = 1.6315 Angstrom
      mean = 1.6261 Angstrom
        t1 = 0.092234  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.067876  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6131 A <--> 1.7490 A
          Mean   = 1.6477 A
          StdDev = 0.0471 A

       t1 Range  = 0.0701 <-- 0.0812 --> 0.0922
       t2 Range  = 0.0396 <-- 0.0537 --> 0.0679

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 105.530 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.403 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 119.428 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 117.378 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  95.027 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 114.155 deg; O3  -- O4  = 3 A
       95.027 deg <-- 109.487 deg --> 119.428 deg

O3  -- T2  -- O3  =  88.551 deg; O3  -- O3  = 2 A
O3  -- T2  -- O4  =  99.909 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 127.791 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 127.791 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  =  99.909 deg; O3  -- O4  = 2 A
O4  -- T2  -- O4  = 113.528 deg; O4  -- O4  = 3 A
       88.551 deg <-- 109.580 deg --> 127.791 deg

        O-T-O SUMMARY
          Range  = 88.5508 deg <--> 127.7906 deg
          Mean   = 109.7072 deg
          StdDev = 12.3796 deg

        O--O SUMMARY
          Range  = 2.2629 A <--> 2.9205 A
          Mean   = 2.6727 A
          StdDev = 0.2178 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  82.664 deg; T1  -- T2  = 3.9392 A
T1  - O1  - T1  - O3  - T1  = 105.530 deg; T1  -- T1  = 5.1728 A
T1  - O1  - T1  - O4  - T2  = 102.643 deg; T1  -- T2  = 4.8790 A
T2  - O2  - T1  - O3  - T1  = 114.399 deg; T2  -- T1  = 5.0362 A
T2  - O2  - T1  - O4  - T2  = 104.145 deg; T2  -- T2  = 4.5247 A
T1  - O3  - T1  - O4  - T2  = 134.367 deg; T1  -- T2  = 5.8009 A

T1  - O3  - T2  - O3  - T1  =  80.713 deg; T1  -- T1  = 3.5091 A
T1  - O3  - T2  - O4  - T1  = 104.145 deg; T1  -- T1  = 4.5247 A
T1  - O3  - T2  - O4  - T1  = 175.142 deg; T1  -- T1  = 5.7260 A
T1  - O3  - T2  - O4  - T1  = 175.142 deg; T1  -- T1  = 5.7260 A
T1  - O3  - T2  - O4  - T1  = 104.145 deg; T1  -- T1  = 4.5247 A
T1  - O4  - T2  - O4  - T1  =  70.997 deg; T1  -- T1  = 3.5091 A

        T-T-T SUMMARY
          Range  = 70.9968 deg <--> 175.1417 deg
          Mean   = 114.1477 deg
          StdDev = 32.4300 deg

        T--T SUMMARY
          Range  = 3.5091 A <--> 5.8009 A
          Mean   = 4.7742 A
          StdDev = 0.7798 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2710 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2261 A

T1  -- O3  -- T2  = 106.981 deg ; T1  -- T2   2.7096 A

T1  -- O4  -- T2  = 135.237 deg ; T1  -- T2   3.0216 A


        T-O-T SUMMARY
          Range  = 106.9814° <--> 180.0000 deg
          Mean   = 150.5546 deg
          StdDev = 32.1136 deg

        T--T SUMMARY
          Range  = 2.7096 A <--> 3.2710 A
          Mean   = 3.0571 A
          StdDev = 0.2288 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O3  = 2.2629 A
T1  -- T2  = 2.7096 Angstrom
T2  -- T1  = 2.7096 Angstrom
T2  -- T1  = 2.7096 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 552 624
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000