Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_13_2_256459_YX9S2N.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 28.61 T-atoms per nm^3
Material density = 2.855 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6286 Angstrom
T1  -- O2  = 1.6169 Angstrom
T1  -- O3  = 1.6539 Angstrom
T1  -- O4  = 1.6523 Angstrom
      mean = 1.6379 Angstrom
        t1 = 0.019966  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008831  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6241 Angstrom
T2  -- O4  = 1.6241 Angstrom
T2  -- O3  = 1.6240 Angstrom
T2  -- O3  = 1.6240 Angstrom
      mean = 1.6241 Angstrom
        t1 = 0.047082  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050481  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6169 A <--> 1.6539 A
          Mean   = 1.6333 A
          StdDev = 0.0147 A

       t1 Range  = 0.0200 <-- 0.0335 --> 0.0471
       t2 Range  = 0.0088 <-- 0.0297 --> 0.0505

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.265 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.767 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.985 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.330 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.112 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.378 deg; O3  -- O4  = 3 A
       107.985 deg <-- 109.473 deg --> 110.767 deg

O4  -- T2  -- O4  = 104.056 deg; O4  -- O4  = 3 A
O4  -- T2  -- O3  = 120.633 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 104.473 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 104.473 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 120.633 deg; O4  -- O3  = 3 A
O3  -- T2  -- O3  = 103.780 deg; O3  -- O3  = 3 A
       103.780 deg <-- 109.675 deg --> 120.633 deg

        O-T-O SUMMARY
          Range  = 103.7796 deg <--> 120.6331 deg
          Mean   = 109.5871 deg
          StdDev = 5.7127 deg

        O--O SUMMARY
          Range  = 2.5557 A <--> 2.8219 A
          Mean   = 2.6627 A
          StdDev = 0.0921 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  92.745 deg; T2  -- T1  = 4.4134 A
T2  - O1  - T1  - O3  - T1  = 116.383 deg; T2  -- T1  = 4.8818 A
T2  - O1  - T1  - O4  - T2  =  94.426 deg; T2  -- T2  = 4.1882 A
T1  - O2  - T1  - O3  - T1  =  97.386 deg; T1  -- T1  = 4.6070 A
T1  - O2  - T1  - O4  - T2  = 137.399 deg; T1  -- T2  = 5.6738 A
T1  - O3  - T1  - O4  - T2  = 116.367 deg; T1  -- T2  = 4.8828 A

T1  - O4  - T2  - O4  - T1  = 179.969 deg; T1  -- T1  = 5.7069 A
T1  - O4  - T2  - O3  - T1  =  94.426 deg; T1  -- T1  = 4.1882 A
T1  - O4  - T2  - O3  - T1  =  85.605 deg; T1  -- T1  = 3.8766 A
T1  - O4  - T2  - O3  - T1  =  85.543 deg; T1  -- T1  = 3.8766 A
T1  - O4  - T2  - O3  - T1  =  94.426 deg; T1  -- T1  = 4.1882 A
T1  - O3  - T2  - O3  - T1  = 179.969 deg; T1  -- T1  = 5.7069 A

        T-T-T SUMMARY
          Range  = 85.5433 deg <--> 179.9691 deg
          Mean   = 115.5018 deg
          StdDev = 33.3388 deg

        T--T SUMMARY
          Range  = 3.8766 A <--> 5.7069 A
          Mean   = 4.6942 A
          StdDev = 0.6821 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.210 deg ; T1  -- T1   2.8919 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2338 A

T1  -- O3  -- T2  = 121.089 deg ; T1  -- T2   2.8543 A

T1  -- O4  -- T2  = 121.071 deg ; T1  -- T2   2.8526 A


        T-O-T SUMMARY
          Range  = 121.0711° <--> 180.0000 deg
          Mean   = 136.8424 deg
          StdDev = 25.7930 deg

        T--T SUMMARY
          Range  = 2.8526 A <--> 3.2338 A
          Mean   = 2.9581 A
          StdDev = 0.1652 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 552 624
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000