Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_13_2_255833_SfcM1R.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 28.96 T-atoms per nm^3
Material density = 2.890 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6282 Angstrom
T1  -- O2  = 1.6182 Angstrom
T1  -- O3  = 1.6777 Angstrom
T1  -- O4  = 1.6496 Angstrom
      mean = 1.6434 Angstrom
        t1 = 0.024408  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013174  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6234 Angstrom
T2  -- O3  = 1.6234 Angstrom
T2  -- O4  = 1.6235 Angstrom
T2  -- O4  = 1.6235 Angstrom
      mean = 1.6234 Angstrom
        t1 = 0.042338  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031470  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6182 A <--> 1.6777 A
          Mean   = 1.6368 A
          StdDev = 0.0213 A

       t1 Range  = 0.0244 <-- 0.0334 --> 0.0423
       t2 Range  = 0.0132 <-- 0.0223 --> 0.0315

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.072 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.224 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.345 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.312 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.549 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.318 deg; O3  -- O4  = 3 A
       108.312 deg <-- 109.470 deg --> 111.224 deg

O3  -- T2  -- O3  = 105.427 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 104.975 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 119.384 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 119.384 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 104.975 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 103.625 deg; O4  -- O4  = 3 A
       103.625 deg <-- 109.628 deg --> 119.384 deg

        O-T-O SUMMARY
          Range  = 103.6246 deg <--> 119.3836 deg
          Mean   = 109.5699 deg
          StdDev = 5.1107 deg

        O--O SUMMARY
          Range  = 2.5521 A <--> 2.8031 A
          Mean   = 2.6672 A
          StdDev = 0.0855 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 138.120 deg; T2  -- T1  = 5.6833 A
T2  - O1  - T1  - O3  - T1  = 116.756 deg; T2  -- T1  = 4.8863 A
T2  - O1  - T1  - O4  - T2  =  94.190 deg; T2  -- T2  = 4.1720 A
T1  - O2  - T1  - O3  - T1  =  96.738 deg; T1  -- T1  = 4.5857 A
T1  - O2  - T1  - O4  - T2  =  92.048 deg; T1  -- T2  = 4.3872 A
T1  - O3  - T1  - O4  - T2  = 116.739 deg; T1  -- T2  = 4.8873 A

T1  - O3  - T2  - O3  - T1  =  85.841 deg; T1  -- T1  = 3.8776 A
T1  - O3  - T2  - O4  - T1  =  94.190 deg; T1  -- T1  = 4.1720 A
T1  - O3  - T2  - O4  - T1  = 179.969 deg; T1  -- T1  = 5.6957 A
T1  - O3  - T2  - O4  - T1  = 179.969 deg; T1  -- T1  = 5.6957 A
T1  - O3  - T2  - O4  - T1  =  94.190 deg; T1  -- T1  = 4.1720 A
T1  - O4  - T2  - O4  - T1  =  85.779 deg; T1  -- T1  = 3.8776 A

        T-T-T SUMMARY
          Range  = 85.7794 deg <--> 179.9691 deg
          Mean   = 113.5191 deg
          StdDev = 33.4048 deg

        T--T SUMMARY
          Range  = 3.8776 A <--> 5.6957 A
          Mean   = 4.6305 A
          StdDev = 0.6519 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.202 deg ; T1  -- T1   2.8912 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2363 A

T1  -- O3  -- T2  = 119.173 deg ; T1  -- T2   2.8470 A

T1  -- O4  -- T2  = 120.994 deg ; T1  -- T2   2.8487 A


        T-O-T SUMMARY
          Range  = 119.1728° <--> 180.0000 deg
          Mean   = 136.3422 deg
          StdDev = 26.1303 deg

        T--T SUMMARY
          Range  = 2.8470 A <--> 3.2363 A
          Mean   = 2.9558 A
          StdDev = 0.1683 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 41 62 90 122 157 200 247 296 354 416 479 552 629
TD10 = 959
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 25
Vertex symbol  = 4.8_{6}.6.6.6.6
Weight = 25

T2 (Si): multiplicity = 2
Coordination Sequence =
    1 4 10 24 40 64 90 120 160 200 244 300 354 412 484 552 624
TD10 = 957
Circuit symbol = 4.4.6_{2}.6_{2}.8_{6}.8_{6}
Weight = 29
Vertex symbol  = 4.4.6_{2}.6_{2}.8_{2}.8_{2}
Weight = 29

<TD10> = 958.333
Average ring size = 6.4000