Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_13_2_247201_4zu4zx.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 24.19 T-atoms per nm^3
Material density = 2.413 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6157 Angstrom
T1  -- O2  = 1.6104 Angstrom
T1  -- O3  = 1.6221 Angstrom
T1  -- O4  = 1.6220 Angstrom
      mean = 1.6175 Angstrom
        t1 = 0.004993  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001098  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6103 Angstrom
T2  -- O3  = 1.6214 Angstrom
T2  -- O4  = 1.6222 Angstrom
T2  -- O5  = 1.6156 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.004812  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000956  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6103 A <--> 1.6222 A
          Mean   = 1.6174 A
          StdDev = 0.0049 A

       t1 Range  = 0.0048 <-- 0.0049 --> 0.0050
       t2 Range  = 0.0010 <-- 0.0010 --> 0.0011

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.515 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.348 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.701 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.577 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.342 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.345 deg; O3  -- O4  = 3 A
       109.342 deg <-- 109.471 deg --> 109.701 deg

O2  -- T2  -- O3  = 109.358 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.572 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.609 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.387 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.611 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.291 deg; O4  -- O5  = 3 A
       109.291 deg <-- 109.471 deg --> 109.611 deg

        O-T-O SUMMARY
          Range  = 109.2909 deg <--> 109.7006 deg
          Mean   = 109.4712 deg
          StdDev = 0.1352 deg

        O--O SUMMARY
          Range  = 2.6348 A <--> 2.6473 A
          Mean   = 2.6413 A
          StdDev = 0.0043 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 109.482 deg; T2  -- T1  = 5.2684 A
T2  - O1  - T1  - O3  - T2  = 128.516 deg; T2  -- T2  = 5.6123 A
T2  - O1  - T1  - O4  - T2  =  97.480 deg; T2  -- T2  = 4.6854 A
T1  - O2  - T1  - O3  - T2  =  90.591 deg; T1  -- T2  = 4.4382 A
T1  - O2  - T1  - O4  - T2  = 131.630 deg; T1  -- T2  = 5.6937 A
T2  - O3  - T1  - O4  - T2  = 103.265 deg; T2  -- T2  = 4.7189 A

T1  - O2  - T2  - O3  - T1  = 128.515 deg; T1  -- T1  = 5.6125 A
T1  - O2  - T2  - O4  - T2  = 109.642 deg; T1  -- T2  = 5.2734 A
T1  - O2  - T2  - O5  - T1  =  97.482 deg; T1  -- T1  = 4.6853 A
T1  - O3  - T2  - O4  - T2  =  90.503 deg; T1  -- T2  = 4.4348 A
T1  - O3  - T2  - O5  - T1  = 103.265 deg; T1  -- T1  = 4.7189 A
T2  - O4  - T2  - O5  - T1  = 131.528 deg; T2  -- T1  = 5.6911 A

        T-T-T SUMMARY
          Range  = 90.5025 deg <--> 131.6295 deg
          Mean   = 110.1582 deg
          StdDev = 15.3763 deg

        T--T SUMMARY
          Range  = 4.4348 A <--> 5.6937 A
          Mean   = 5.0694 A
          StdDev = 0.4872 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2313 A

T1  -- O2  -- T2  = 179.934 deg ; T1  -- T2   3.2206 A

T1  -- O3  -- T2  = 136.176 deg ; T1  -- T2   3.0092 A

T1  -- O4  -- T2  = 136.145 deg ; T1  -- T2   3.0094 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2312 A


        T-O-T SUMMARY
          Range  = 136.1451° <--> 180.0000 deg
          Mean   = 162.4509 deg
          StdDev = 22.0237 deg

        T--T SUMMARY
          Range  = 3.0092 A <--> 3.2313 A
          Mean   = 3.1404 A
          StdDev = 0.1098 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 377 450 527 612 702 800
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 377 450 527 612 702 800
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 1199.000
Average ring size = 6.0000