Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_13_2_246506_Dv5olq.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 26.43 T-atoms per nm^3
Material density = 2.637 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6162 Angstrom
T1  -- O2  = 1.5444 Angstrom
T1  -- O4  = 1.6590 Angstrom
T1  -- O3  = 1.6717 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.038371  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027166  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.5706 Angstrom
T2  -- O3  = 1.6530 Angstrom
T2  -- O4  = 1.6593 Angstrom
T2  -- O5  = 1.6139 Angstrom
      mean = 1.6242 Angstrom
        t1 = 0.043076  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027339  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5444 A <--> 1.6717 A
          Mean   = 1.6235 A
          StdDev = 0.0439 A

       t1 Range  = 0.0384 <-- 0.0407 --> 0.0431
       t2 Range  = 0.0272 <-- 0.0273 --> 0.0273

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 124.276 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 103.801 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 102.977 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 114.853 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 110.619 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  =  96.181 deg; O4  -- O3  = 2 A
       96.181 deg <-- 108.784 deg --> 124.276 deg

O2  -- T2  -- O3  = 101.869 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 108.564 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 107.251 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 119.260 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 111.100 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 108.066 deg; O4  -- O5  = 3 A
       101.869 deg <-- 109.352 deg --> 119.260 deg

        O-T-O SUMMARY
          Range  = 96.1810 deg <--> 124.2761 deg
          Mean   = 109.0680 deg
          StdDev = 7.5086 deg

        O--O SUMMARY
          Range  = 2.4787 A <--> 2.8578 A
          Mean   = 2.6384 A
          StdDev = 0.1080 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 115.482 deg; T2  -- T1  = 5.0628 A
T2  - O1  - T1  - O4  - T2  = 137.490 deg; T2  -- T2  = 5.6558 A
T2  - O1  - T1  - O3  - T2  = 100.454 deg; T2  -- T2  = 4.5079 A
T1  - O2  - T1  - O4  - T2  = 104.215 deg; T1  -- T2  = 5.1697 A
T1  - O2  - T1  - O3  - T2  = 112.325 deg; T1  -- T2  = 5.2692 A
T2  - O4  - T1  - O3  - T2  =  76.690 deg; T2  -- T2  = 3.9916 A

T1  - O2  - T2  - O3  - T1  =  81.025 deg; T1  -- T1  = 3.9635 A
T1  - O2  - T2  - O4  - T2  = 123.489 deg; T1  -- T2  = 5.2674 A
T1  - O2  - T2  - O5  - T1  = 100.454 deg; T1  -- T1  = 4.5079 A
T1  - O3  - T2  - O4  - T2  = 107.747 deg; T1  -- T2  = 5.2874 A
T1  - O3  - T2  - O5  - T1  = 138.017 deg; T1  -- T1  = 6.0025 A
T2  - O4  - T2  - O5  - T1  = 105.948 deg; T2  -- T1  = 5.0609 A

        T-T-T SUMMARY
          Range  = 76.6895 deg <--> 138.0173 deg
          Mean   = 108.6114 deg
          StdDev = 18.2682 deg

        T--T SUMMARY
          Range  = 3.9635 A <--> 6.0025 A
          Mean   = 4.9789 A
          StdDev = 0.6027 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2325 A

T1  -- O2  -- T2  = 123.704 deg ; T1  -- T2   2.7466 A

T1  -- O3  -- T2  = 138.663 deg ; T1  -- T2   3.1107 A

T1  -- O4  -- T2  = 178.502 deg ; T1  -- T2   3.3180 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2278 A


        T-O-T SUMMARY
          Range  = 123.7037° <--> 180.0000 deg
          Mean   = 160.1738 deg
          StdDev = 24.7721 deg

        T--T SUMMARY
          Range  = 2.7466 A <--> 3.3180 A
          Mean   = 3.1271 A
          StdDev = 0.2066 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7466 Angstrom
T2  -- T1  = 2.7466 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 377 450 527 612 702 800
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 377 450 527 612 702 800
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 1199.000
Average ring size = 6.0000