Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_13_2_246501_62p1GE.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 27.71 T-atoms per nm^3
Material density = 2.764 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6266 Angstrom
T1  -- O2  = 1.5897 Angstrom
T1  -- O3  = 1.6377 Angstrom
T1  -- O4  = 1.6747 Angstrom
      mean = 1.6322 Angstrom
        t1 = 0.065157  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.066921  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.5759 Angstrom
T2  -- O3  = 1.6182 Angstrom
T2  -- O5  = 1.6220 Angstrom
T2  -- O4  = 1.6691 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.035683  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028052  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5759 A <--> 1.6747 A
          Mean   = 1.6267 A
          StdDev = 0.0327 A

       t1 Range  = 0.0357 <-- 0.0504 --> 0.0652
       t2 Range  = 0.0281 <-- 0.0475 --> 0.0669

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 126.720 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  95.118 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 108.674 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 105.159 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 117.578 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  95.203 deg; O3  -- O4  = 2 A
       95.118 deg <-- 108.075 deg --> 126.720 deg

O2  -- T2  -- O3  = 103.034 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 116.464 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 107.360 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 106.400 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 116.143 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 107.773 deg; O5  -- O4  = 3 A
       103.034 deg <-- 109.529 deg --> 116.464 deg

        O-T-O SUMMARY
          Range  = 95.1178 deg <--> 126.7202 deg
          Mean   = 108.8021 deg
          StdDev = 8.9363 deg

        O--O SUMMARY
          Range  = 2.4090 A <--> 2.8749 A
          Mean   = 2.6372 A
          StdDev = 0.1393 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 104.051 deg; T2  -- T1  = 4.7117 A
T2  - O1  - T1  - O3  - T2  = 100.373 deg; T2  -- T2  = 4.4912 A
T2  - O1  - T1  - O4  - T2  = 135.688 deg; T2  -- T2  = 5.5471 A
T1  - O2  - T1  - O3  - T2  = 102.138 deg; T1  -- T2  = 4.9643 A
T1  - O2  - T1  - O4  - T2  = 120.041 deg; T1  -- T2  = 5.6556 A
T2  - O3  - T1  - O4  - T2  =  75.799 deg; T2  -- T2  = 3.9354 A

T1  - O2  - T2  - O3  - T2  = 134.008 deg; T1  -- T2  = 5.4838 A
T1  - O2  - T2  - O5  - T1  =  80.664 deg; T1  -- T1  = 3.8976 A
T1  - O2  - T2  - O4  - T1  = 100.373 deg; T1  -- T1  = 4.4912 A
T2  - O3  - T2  - O5  - T1  =  97.085 deg; T2  -- T1  = 4.8865 A
T2  - O3  - T2  - O4  - T1  = 111.153 deg; T2  -- T1  = 5.2562 A
T1  - O5  - T2  - O4  - T1  = 136.432 deg; T1  -- T1  = 5.9466 A

        T-T-T SUMMARY
          Range  = 75.7993 deg <--> 136.4319 deg
          Mean   = 108.1505 deg
          StdDev = 19.5168 deg

        T--T SUMMARY
          Range  = 3.8976 A <--> 5.9466 A
          Mean   = 4.9389 A
          StdDev = 0.6421 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2532 A

T1  -- O2  -- T2  = 117.678 deg ; T1  -- T2   2.7089 A

T1  -- O3  -- T2  = 147.725 deg ; T1  -- T2   3.1276 A

T1  -- O4  -- T2  = 156.879 deg ; T1  -- T2   3.2760 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2440 A


        T-O-T SUMMARY
          Range  = 117.6776° <--> 180.0000 deg
          Mean   = 156.4565 deg
          StdDev = 23.7921 deg

        T--T SUMMARY
          Range  = 2.7089 A <--> 3.2760 A
          Mean   = 3.1219 A
          StdDev = 0.2184 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7089 Angstrom
T2  -- T1  = 2.7089 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 377 450 527 612 702 800
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 27 50 77 112 152 200 252 312 377 450 527 612 702 800
TD10 = 1199
Circuit symbol = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26
Vertex symbol  = 6.6.6.6_{2}.6_{2}.6_{2}
Weight = 26

<TD10> = 1199.000
Average ring size = 6.0000