Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_7231485_Ui2cXj.cif"

There are 112 T-atoms per unit cell
There are 224 O-atoms per unit cell

Framework density = 20.19 T-atoms per nm^3
Material density = 2.015 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6150 Angstrom
T1  -- O2  = 1.6627 Angstrom
T1  -- O3  = 1.5185 Angstrom
T1  -- O4  = 1.7018 Angstrom
      mean = 1.6245 Angstrom
        t1 = 0.043178  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053695  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5611 Angstrom
T2  -- O5  = 1.5725 Angstrom
T2  -- O6  = 1.6033 Angstrom
T2  -- O7  = 1.6547 Angstrom
      mean = 1.5979 Angstrom
        t1 = 0.042452  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027031  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6352 Angstrom
T3  -- O8  = 1.6350 Angstrom
T3  -- O9  = 1.6220 Angstrom
T3  -- O7  = 1.6352 Angstrom
      mean = 1.6318 Angstrom
        t1 = 0.023902  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013731  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6549 Angstrom
T4  -- O10 = 1.7318 Angstrom
T4  -- O11 = 1.4975 Angstrom
T4  -- O4  = 1.6549 Angstrom
      mean = 1.6348 Angstrom
        t1 = 0.082962  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.083089  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.4869 Angstrom
T5  -- O12 = 1.5952 Angstrom
T5  -- O13 = 1.6002 Angstrom
T5  -- O12 = 1.5952 Angstrom
      mean = 1.5694 Angstrom
        t1 = 0.035338  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019961  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4869 A <--> 1.7318 A
          Mean   = 1.6115 A
          StdDev = 0.0599 A

       t1 Range  = 0.0239 <-- 0.0456 --> 0.0830
       t2 Range  = 0.0137 <-- 0.0395 --> 0.0831

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.171 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.170 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 109.074 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.408 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 114.190 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.178 deg; O3  -- O4  = 3 A
       103.170 deg <-- 109.365 deg --> 114.190 deg

O3  -- T2  -- O5  =  99.911 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 109.501 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 118.553 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 111.056 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 107.999 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.411 deg; O6  -- O7  = 3 A
       99.911 deg <-- 109.405 deg --> 118.553 deg

O7  -- T3  -- O8  = 113.465 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.270 deg; O7  -- O9  = 3 A
O7  -- T3  -- O7  = 104.922 deg; O7  -- O7  = 3 A
O8  -- T3  -- O9  = 108.228 deg; O8  -- O9  = 3 A
O8  -- T3  -- O7  = 113.465 deg; O8  -- O7  = 3 A
O9  -- T3  -- O7  = 108.270 deg; O9  -- O7  = 3 A
       104.922 deg <-- 109.437 deg --> 113.465 deg

O4  -- T4  -- O10 = 116.878 deg; O4  -- O10 = 3 A
O4  -- T4  -- O11 =  98.024 deg; O4  -- O11 = 2 A
O4  -- T4  -- O4  = 115.672 deg; O4  -- O4  = 3 A
O10 -- T4  -- O11 = 106.669 deg; O10 -- O11 = 3 A
O10 -- T4  -- O4  = 116.878 deg; O10 -- O4  = 3 A
O11 -- T4  -- O4  =  98.024 deg; O11 -- O4  = 2 A
       98.024 deg <-- 108.691 deg --> 116.878 deg

O11 -- T5  -- O12 = 107.771 deg; O11 -- O12 = 2 A
O11 -- T5  -- O13 = 109.075 deg; O11 -- O13 = 3 A
O11 -- T5  -- O12 = 107.771 deg; O11 -- O12 = 2 A
O12 -- T5  -- O13 = 111.166 deg; O12 -- O13 = 3 A
O12 -- T5  -- O12 = 109.767 deg; O12 -- O12 = 3 A
O13 -- T5  -- O12 = 111.166 deg; O13 -- O12 = 3 A
       107.771 deg <-- 109.453 deg --> 111.166 deg

        O-T-O SUMMARY
          Range  = 98.0236 deg <--> 118.5531 deg
          Mean   = 109.3183 deg
          StdDev = 5.4081 deg

        O--O SUMMARY
          Range  = 2.3818 A <--> 2.8861 A
          Mean   = 2.6357 A
          StdDev = 0.1401 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4883 A
T1  - O1  - T1  - O3  - T2  =  93.194 deg; T1  -- T2  = 4.3099 A
T1  - O1  - T1  - O4  - T4  = 125.948 deg; T1  -- T4  = 5.7709 A
T1  - O2  - T1  - O3  - T2  = 127.945 deg; T1  -- T2  = 5.2296 A
T1  - O2  - T1  - O4  - T4  = 125.518 deg; T1  -- T4  = 5.6757 A
T2  - O3  - T1  - O4  - T4  =  93.070 deg; T2  -- T4  = 4.3342 A

T1  - O3  - T2  - O5  - T2  = 118.307 deg; T1  -- T2  = 4.7393 A
T1  - O3  - T2  - O6  - T3  = 135.203 deg; T1  -- T3  = 5.0614 A
T1  - O3  - T2  - O7  - T2  = 141.872 deg; T1  -- T2  = 5.2719 A
T2  - O5  - T2  - O6  - T3  =  94.244 deg; T2  -- T3  = 4.1139 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.0426 A
T3  - O6  - T2  - O7  - T2  =  58.767 deg; T3  -- T2  = 2.7843 A

T2  - O7  - T3  - O8  - T3  =  85.756 deg; T2  -- T3  = 4.1139 A
T2  - O7  - T3  - O9  - T3  = 148.414 deg; T2  -- T3  = 5.6287 A
T2  - O7  - T3  - O7  - T2  =  62.466 deg; T2  -- T2  = 2.8874 A
T3  - O8  - T3  - O9  - T3  =  90.000 deg; T3  -- T3  = 4.4610 A
T3  - O8  - T3  - O7  - T2  =  85.756 deg; T3  -- T2  = 4.1139 A
T3  - O9  - T3  - O7  - T2  = 148.414 deg; T3  -- T2  = 5.6287 A

T1  - O4  - T4  - O10 - T5  =  91.641 deg; T1  -- T5  = 4.4244 A
T1  - O4  - T4  - O11 - T1  = 111.361 deg; T1  -- T1  = 5.3807 A
T1  - O4  - T4  - O4  - T4  = 124.319 deg; T1  -- T4  = 5.9285 A
T5  - O10 - T4  - O11 - T1  =  91.641 deg; T5  -- T1  = 4.4244 A
T5  - O10 - T4  - O4  - T4  =  87.526 deg; T5  -- T4  = 4.4087 A
T1  - O11 - T4  - O4  - T4  = 124.319 deg; T1  -- T4  = 5.9285 A

T4  - O11 - T5  - O12 - T5  = 134.947 deg; T4  -- T5  = 5.2767 A
T4  - O11 - T5  - O13 - T5  = 134.947 deg; T4  -- T5  = 5.2767 A
T4  - O11 - T5  - O12 - T5  =  92.474 deg; T4  -- T5  = 4.4087 A
T5  - O12 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 3.9742 A
T5  - O12 - T5  - O12 - T5  =  90.000 deg; T5  -- T5  = 4.2556 A
T5  - O13 - T5  - O12 - T5  =  90.000 deg; T5  -- T5  = 4.2556 A

        T-T-T SUMMARY
          Range  = 58.7672 deg <--> 148.4145 deg
          Mean   = 107.3302 deg
          StdDev = 25.0924 deg

        T--T SUMMARY
          Range  = 2.7843 A <--> 5.9285 A
          Mean   = 4.7279 A
          StdDev = 0.8445 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.307 deg ; T1  -- T1   3.2208 A

T1  -- O2  -- T1  = 140.098 deg ; T1  -- T1   3.1259 A

T1  -- O3  -- T2  = 121.730 deg ; T1  -- T2   2.6900 A

T1  -- O4  -- T4  = 152.061 deg ; T1  -- T4   3.2575 A

T2  -- O5  -- T2  = 133.286 deg ; T2  -- T2   2.8874 A

T2  -- O6  -- T2  = 123.867 deg ; T2  -- T2   2.8295 A

T2  -- O7  -- T3  = 115.626 deg ; T2  -- T3   2.7843 A

T3  -- O8  -- T3  = 139.192 deg ; T3  -- T3   3.0648 A

T3  -- O9  -- T3  = 175.648 deg ; T3  -- T3   3.2416 A

T4  -- O10 -- T4  = 168.554 deg ; T4  -- T4   3.4464 A

T4  -- O11 -- T5  = 153.061 deg ; T4  -- T5   2.9023 A

T5  -- O12 -- T5  = 123.492 deg ; T5  -- T5   2.8102 A

T5  -- O13 -- T5  = 173.835 deg ; T5  -- T5   3.1958 A


        T-O-T SUMMARY
          Range  = 115.6259° <--> 175.6484 deg
          Mean   = 142.4867 deg
          StdDev = 20.3650 deg

        T--T SUMMARY
          Range  = 2.6900 A <--> 3.4464 A
          Mean   = 3.0126 A
          StdDev = 0.2209 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.6900 Angstrom
T2  -- T1  = 2.6900 Angstrom
T2  -- T3  = 2.7843 Angstrom
T3  -- T2  = 2.7843 Angstrom
T3  -- T2  = 2.7843 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 11 24 41 62 93 133 171 216 266 327 405 472 540 632 727
TD10 = 1022
Circuit symbol = 4.5.6.8.8.8_{2}
Weight = 24
Vertex symbol  = 4.5.6.8.8.8
Weight = 24

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 8 16 34 60 86 120 160 207 266 315 381 451 531 617 703
TD10 = 962
Circuit symbol = 3.5.4.7.4.7
Weight = 9
Vertex symbol  = 3.5.4.8_{2}.4.9
Weight = 22

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 7 12 26 53 88 122 155 202 262 322 374 431 514 628 702
TD10 = 932
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.9.4.9
Weight = 20

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 23 42 66 90 126 171 220 273 328 388 470 554 625 713
TD10 = 1027
Circuit symbol = 4.5.6.8_{5}.6.8_{5}
Weight = 30
Vertex symbol  = 4.5.6.8_{3}.6.8_{3}
Weight = 30

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 14 27 52 87 120 151 193 246 307 373 436 510 601 686
TD10 = 903
Circuit symbol = 4.4.4.6_{2}.4.6_{2}
Weight = 15
Vertex symbol  = 4.4.4.6.4.6
Weight = 15

<TD10> = 975.714
Average ring size = 5.3665