Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_6619046_CJEP_T.cif"

There are 128 T-atoms per unit cell
There are 256 O-atoms per unit cell

Framework density = 14.62 T-atoms per nm^3
Material density = 1.459 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6163 Angstrom
T1  -- O2  = 1.6108 Angstrom
T1  -- O3  = 1.6093 Angstrom
T1  -- O4  = 1.6183 Angstrom
      mean = 1.6137 Angstrom
        t1 = 0.003410  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001841  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6110 Angstrom
T2  -- O5  = 1.6190 Angstrom
T2  -- O6  = 1.6251 Angstrom
T2  -- O7  = 1.6272 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.007393  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002279  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6188 Angstrom
T3  -- O8  = 1.6177 Angstrom
T3  -- O9  = 1.6254 Angstrom
T3  -- O10 = 1.6338 Angstrom
      mean = 1.6239 Angstrom
        t1 = 0.009012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002735  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6229 Angstrom
T4  -- O7  = 1.6229 Angstrom
T4  -- O11 = 1.6155 Angstrom
T4  -- O12 = 1.6159 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.006670  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002257  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6250 Angstrom
T5  -- O10 = 1.6250 Angstrom
T5  -- O12 = 1.6159 Angstrom
T5  -- O13 = 1.6233 Angstrom
      mean = 1.6223 Angstrom
        t1 = 0.008953  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003053  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6093 A <--> 1.6338 A
          Mean   = 1.6197 A
          StdDev = 0.0065 A

       t1 Range  = 0.0034 <-- 0.0071 --> 0.0090
       t2 Range  = 0.0018 <-- 0.0024 --> 0.0031

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.613 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.784 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.105 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.894 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.533 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.888 deg; O3  -- O4  = 3 A
       108.613 deg <-- 109.470 deg --> 109.894 deg

O3  -- T2  -- O5  = 110.294 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.529 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.617 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.816 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.864 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.689 deg; O6  -- O7  = 3 A
       108.617 deg <-- 109.468 deg --> 110.294 deg

O4  -- T3  -- O8  = 110.215 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.096 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.329 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.865 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.933 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.370 deg; O9  -- O10 = 3 A
       108.370 deg <-- 109.468 deg --> 110.215 deg

O7  -- T4  -- O7  = 108.052 deg; O7  -- O7  = 3 A
O7  -- T4  -- O11 = 109.309 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.956 deg; O7  -- O12 = 3 A
O7  -- T4  -- O11 = 109.309 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.956 deg; O7  -- O12 = 3 A
O11 -- T4  -- O12 = 110.221 deg; O11 -- O12 = 3 A
       108.052 deg <-- 109.467 deg --> 110.221 deg

O10 -- T5  -- O10 = 107.717 deg; O10 -- O10 = 3 A
O10 -- T5  -- O12 = 109.485 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 110.030 deg; O10 -- O13 = 3 A
O10 -- T5  -- O12 = 109.485 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 110.030 deg; O10 -- O13 = 3 A
O12 -- T5  -- O13 = 110.055 deg; O12 -- O13 = 3 A
       107.717 deg <-- 109.467 deg --> 110.055 deg

        O-T-O SUMMARY
          Range  = 107.7174 deg <--> 110.2944 deg
          Mean   = 109.4456 deg
          StdDev = 0.6631 deg

        O--O SUMMARY
          Range  = 2.6209 A <--> 2.6625 A
          Mean   = 2.6451 A
          StdDev = 0.0105 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.7941 A
T1  - O1  - T1  - O3  - T2  = 116.465 deg; T1  -- T2  = 5.3037 A
T1  - O1  - T1  - O4  - T3  = 116.576 deg; T1  -- T3  = 5.2783 A
T1  - O2  - T1  - O3  - T2  =  90.301 deg; T1  -- T2  = 4.4534 A
T1  - O2  - T1  - O4  - T3  =  90.634 deg; T1  -- T3  = 4.4425 A
T2  - O3  - T1  - O4  - T3  = 100.462 deg; T2  -- T3  = 4.7769 A

T1  - O3  - T2  - O5  - T2  =  89.699 deg; T1  -- T2  = 4.4534 A
T1  - O3  - T2  - O6  - T2  = 116.942 deg; T1  -- T2  = 5.1719 A
T1  - O3  - T2  - O7  - T4  = 126.113 deg; T1  -- T4  = 5.4164 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.6666 A
T2  - O5  - T2  - O7  - T4  = 132.598 deg; T2  -- T4  = 5.6242 A
T2  - O6  - T2  - O7  - T4  =  60.098 deg; T2  -- T4  = 2.9512 A

T1  - O4  - T3  - O8  - T3  = 117.583 deg; T1  -- T3  = 5.1343 A
T1  - O4  - T3  - O9  - T5  = 127.011 deg; T1  -- T5  = 5.4109 A
T1  - O4  - T3  - O10 - T3  =  89.366 deg; T1  -- T3  = 4.4425 A
T3  - O8  - T3  - O9  - T5  =  60.486 deg; T3  -- T5  = 2.9550 A
T3  - O8  - T3  - O10 - T3  = 135.000 deg; T3  -- T3  = 5.6712 A
T5  - O9  - T3  - O10 - T3  = 131.486 deg; T5  -- T3  = 5.6361 A

T2  - O7  - T4  - O7  - T2  =  59.804 deg; T2  -- T2  = 2.9424 A
T2  - O7  - T4  - O11 - T5  = 117.202 deg; T2  -- T5  = 5.2718 A
T2  - O7  - T4  - O12 - T4  = 137.356 deg; T2  -- T4  = 5.6450 A
T2  - O7  - T4  - O11 - T5  = 117.202 deg; T2  -- T5  = 5.2718 A
T2  - O7  - T4  - O12 - T4  = 137.356 deg; T2  -- T4  = 5.6450 A
T5  - O11 - T4  - O12 - T4  =  90.122 deg; T5  -- T4  = 4.4823 A

T3  - O10 - T5  - O10 - T3  =  59.027 deg; T3  -- T3  = 2.9114 A
T3  - O10 - T5  - O12 - T4  = 116.474 deg; T3  -- T4  = 5.2544 A
T3  - O10 - T5  - O13 - T5  = 138.446 deg; T3  -- T5  = 5.6821 A
T3  - O10 - T5  - O12 - T4  = 116.474 deg; T3  -- T4  = 5.2544 A
T3  - O10 - T5  - O13 - T5  = 138.446 deg; T3  -- T5  = 5.6821 A
T4  - O12 - T5  - O13 - T5  =  89.878 deg; T4  -- T5  = 4.4823 A

        T-T-T SUMMARY
          Range  = 59.0275 deg <--> 138.4465 deg
          Mean   = 110.3042 deg
          StdDev = 25.0146 deg

        T--T SUMMARY
          Range  = 2.9114 A <--> 5.7941 A
          Mean   = 4.9243 A
          StdDev = 0.8669 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 148.880 deg ; T1  -- T1   3.1141 A

T1  -- O2  -- T1  = 157.075 deg ; T1  -- T1   3.1573 A

T1  -- O3  -- T2  = 151.935 deg ; T1  -- T2   3.1242 A

T1  -- O4  -- T3  = 145.393 deg ; T1  -- T3   3.0906 A

T2  -- O5  -- T2  = 160.268 deg ; T2  -- T2   3.1902 A

T2  -- O6  -- T2  = 129.722 deg ; T2  -- T2   2.9424 A

T2  -- O7  -- T4  = 130.466 deg ; T2  -- T4   2.9512 A

T3  -- O8  -- T3  = 171.080 deg ; T3  -- T3   3.2257 A

T3  -- O9  -- T3  = 127.178 deg ; T3  -- T3   2.9114 A

T3  -- O10 -- T5  = 130.121 deg ; T3  -- T5   2.9550 A

T4  -- O11 -- T4  = 148.323 deg ; T4  -- T4   3.1083 A

T4  -- O12 -- T5  = 171.479 deg ; T4  -- T5   3.2228 A

T5  -- O13 -- T5  = 148.165 deg ; T5  -- T5   3.1221 A


        T-O-T SUMMARY
          Range  = 127.1778° <--> 171.4793 deg
          Mean   = 146.6175 deg
          StdDev = 14.5773 deg

        T--T SUMMARY
          Range  = 2.9114 A <--> 3.2257 A
          Mean   = 3.0773 A
          StdDev = 0.1079 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 19 32 50 72 96 124 160 199 242 288 332 382 444 513
TD10 = 767
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 21
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 31 47 71 95 125 160 193 235 285 336 388 446 499
TD10 = 755
Circuit symbol = 3.4.6.8_{2}.6.8_{3}
Weight = 23
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 31 47 71 95 125 160 193 235 285 336 388 446 499
TD10 = 755
Circuit symbol = 3.4.6.8_{2}.6.8_{3}
Weight = 23
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 31 48 68 91 125 165 199 233 276 327 384 442 506
TD10 = 759
Circuit symbol = 3.4.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 31 48 68 91 125 165 199 233 276 327 384 442 506
TD10 = 759
Circuit symbol = 3.4.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

<TD10> = 759.000
Average ring size = 5.1892