Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_5707287_dmhB0Q.cif"

There are 128 T-atoms per unit cell
There are 256 O-atoms per unit cell

Framework density = 14.80 T-atoms per nm^3
Material density = 1.477 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6194 Angstrom
T1  -- O2  = 1.6178 Angstrom
T1  -- O3  = 1.6269 Angstrom
T1  -- O4  = 1.6281 Angstrom
      mean = 1.6230 Angstrom
        t1 = 0.008167  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000730  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6262 Angstrom
T2  -- O5  = 1.6175 Angstrom
T2  -- O6  = 1.6260 Angstrom
T2  -- O7  = 1.6149 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.007399  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001907  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6269 Angstrom
T3  -- O6  = 1.6265 Angstrom
T3  -- O8  = 1.6163 Angstrom
T3  -- O9  = 1.6146 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007181  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002462  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6190 Angstrom
T4  -- O10 = 1.6100 Angstrom
T4  -- O11 = 1.6183 Angstrom
T4  -- O7  = 1.6190 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.004815  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001666  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6191 Angstrom
T5  -- O12 = 1.6147 Angstrom
T5  -- O13 = 1.6218 Angstrom
T5  -- O9  = 1.6191 Angstrom
      mean = 1.6186 Angstrom
        t1 = 0.005510  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000824  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6100 A <--> 1.6281 A
          Mean   = 1.6207 A
          StdDev = 0.0051 A

       t1 Range  = 0.0048 <-- 0.0066 --> 0.0082
       t2 Range  = 0.0007 <-- 0.0015 --> 0.0025

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.020 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.477 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.484 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.658 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.559 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.620 deg; O3  -- O4  = 3 A
       108.620 deg <-- 109.470 deg --> 110.020 deg

O3  -- T2  -- O5  = 109.899 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.749 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.964 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.892 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.218 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.088 deg; O6  -- O7  = 3 A
       108.749 deg <-- 109.468 deg --> 110.218 deg

O4  -- T3  -- O6  = 108.664 deg; O4  -- O6  = 3 A
O4  -- T3  -- O8  = 109.942 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.012 deg; O4  -- O9  = 3 A
O6  -- T3  -- O8  = 109.682 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 109.322 deg; O6  -- O9  = 3 A
O8  -- T3  -- O9  = 110.191 deg; O8  -- O9  = 3 A
       108.664 deg <-- 109.469 deg --> 110.191 deg

O7  -- T4  -- O10 = 109.604 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.370 deg; O7  -- O11 = 3 A
O7  -- T4  -- O7  = 109.898 deg; O7  -- O7  = 3 A
O10 -- T4  -- O11 = 108.975 deg; O10 -- O11 = 3 A
O10 -- T4  -- O7  = 109.604 deg; O10 -- O7  = 3 A
O11 -- T4  -- O7  = 109.370 deg; O11 -- O7  = 3 A
       108.975 deg <-- 109.470 deg --> 109.898 deg

O9  -- T5  -- O12 = 109.788 deg; O9  -- O12 = 3 A
O9  -- T5  -- O13 = 109.245 deg; O9  -- O13 = 3 A
O9  -- T5  -- O9  = 109.648 deg; O9  -- O9  = 3 A
O12 -- T5  -- O13 = 109.110 deg; O12 -- O13 = 3 A
O12 -- T5  -- O9  = 109.788 deg; O12 -- O9  = 3 A
O13 -- T5  -- O9  = 109.245 deg; O13 -- O9  = 3 A
       109.110 deg <-- 109.471 deg --> 109.788 deg

        O-T-O SUMMARY
          Range  = 108.6204 deg <--> 110.2180 deg
          Mean   = 109.4826 deg
          StdDev = 0.4266 deg

        O--O SUMMARY
          Range  = 2.6278 A <--> 2.6558 A
          Mean   = 2.6462 A
          StdDev = 0.0058 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4897 A
T1  - O1  - T1  - O3  - T2  = 138.041 deg; T1  -- T2  = 5.6619 A
T1  - O1  - T1  - O4  - T3  = 139.028 deg; T1  -- T3  = 5.6783 A
T1  - O2  - T1  - O3  - T2  = 115.386 deg; T1  -- T2  = 5.2092 A
T1  - O2  - T1  - O4  - T3  = 116.554 deg; T1  -- T3  = 5.2405 A
T2  - O3  - T1  - O4  - T3  =  59.535 deg; T2  -- T3  = 2.9159 A

T1  - O3  - T2  - O5  - T2  = 131.473 deg; T1  -- T2  = 5.6228 A
T1  - O3  - T2  - O6  - T3  =  60.195 deg; T1  -- T3  = 2.9354 A
T1  - O3  - T2  - O7  - T4  = 128.161 deg; T1  -- T4  = 5.4006 A
T2  - O5  - T2  - O6  - T3  = 133.962 deg; T2  -- T3  = 5.6565 A
T2  - O5  - T2  - O7  - T4  =  89.797 deg; T2  -- T4  = 4.4449 A
T3  - O6  - T2  - O7  - T4  = 116.925 deg; T3  -- T4  = 5.0994 A

T1  - O4  - T3  - O6  - T2  =  60.270 deg; T1  -- T2  = 2.9377 A
T1  - O4  - T3  - O8  - T5  = 126.674 deg; T1  -- T5  = 5.3768 A
T1  - O4  - T3  - O9  - T3  = 131.223 deg; T1  -- T3  = 5.6073 A
T2  - O6  - T3  - O8  - T5  = 116.654 deg; T2  -- T5  = 5.1042 A
T2  - O6  - T3  - O9  - T3  = 136.037 deg; T2  -- T3  = 5.6909 A
T5  - O8  - T3  - O9  - T3  =  89.836 deg; T5  -- T3  = 4.4500 A

T2  - O7  - T4  - O10 - T4  =  90.203 deg; T2  -- T4  = 4.4449 A
T2  - O7  - T4  - O11 - T4  = 116.291 deg; T2  -- T4  = 5.1744 A
T2  - O7  - T4  - O7  - T2  = 101.905 deg; T2  -- T2  = 4.7632 A
T4  - O10 - T4  - O11 - T4  = 135.000 deg; T4  -- T4  = 5.7581 A
T4  - O10 - T4  - O7  - T2  =  90.203 deg; T4  -- T2  = 4.4449 A
T4  - O11 - T4  - O7  - T2  = 116.291 deg; T4  -- T2  = 5.1744 A

T3  - O9  - T5  - O12 - T5  = 116.726 deg; T3  -- T5  = 5.2422 A
T3  - O9  - T5  - O13 - T5  =  90.164 deg; T3  -- T5  = 4.4500 A
T3  - O9  - T5  - O9  - T3  = 100.583 deg; T3  -- T3  = 4.7401 A
T5  - O12 - T5  - O13 - T5  = 135.000 deg; T5  -- T5  = 5.8010 A
T5  - O12 - T5  - O9  - T3  = 116.726 deg; T5  -- T3  = 5.2422 A
T5  - O13 - T5  - O9  - T3  =  90.164 deg; T5  -- T3  = 4.4500 A

        T-T-T SUMMARY
          Range  = 59.5347 deg <--> 139.0281 deg
          Mean   = 108.2682 deg
          StdDev = 23.3145 deg

        T--T SUMMARY
          Range  = 2.9159 A <--> 5.8010 A
          Mean   = 4.8676 A
          StdDev = 0.8005 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 149.636 deg ; T1  -- T1   3.1258 A

T1  -- O2  -- T1  = 169.875 deg ; T1  -- T1   3.2230 A

T1  -- O3  -- T2  = 129.115 deg ; T1  -- T2   2.9377 A

T1  -- O4  -- T3  = 128.799 deg ; T1  -- T3   2.9354 A

T2  -- O5  -- T2  = 172.758 deg ; T2  -- T2   3.2286 A

T2  -- O6  -- T3  = 127.410 deg ; T2  -- T3   2.9159 A

T2  -- O7  -- T4  = 142.977 deg ; T2  -- T4   3.0666 A

T3  -- O8  -- T3  = 169.814 deg ; T3  -- T3   3.2199 A

T3  -- O9  -- T5  = 144.617 deg ; T3  -- T5   3.0808 A

T4  -- O10 -- T4  = 169.594 deg ; T4  -- T4   3.2068 A

T4  -- O11 -- T4  = 138.357 deg ; T4  -- T4   3.0252 A

T5  -- O12 -- T5  = 165.162 deg ; T5  -- T5   3.2023 A

T5  -- O13 -- T5  = 143.059 deg ; T5  -- T5   3.0765 A


        T-O-T SUMMARY
          Range  = 127.4097° <--> 172.7585 deg
          Mean   = 149.3715 deg
          StdDev = 17.0120 deg

        T--T SUMMARY
          Range  = 2.9159 A <--> 3.2286 A
          Mean   = 3.0899 A
          StdDev = 0.1163 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 31 48 68 91 125 165 199 233 276 327 384 442 506
TD10 = 759
Circuit symbol = 3.4.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 31 47 71 95 125 160 193 235 285 336 388 446 499
TD10 = 755
Circuit symbol = 3.4.6.8_{2}.6.8_{3}
Weight = 23
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 31 47 71 95 125 160 193 235 285 336 388 446 499
TD10 = 755
Circuit symbol = 3.4.6.8_{2}.6.8_{3}
Weight = 23
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 32 50 72 96 124 160 199 242 288 332 382 444 513
TD10 = 767
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 21
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 32 50 72 96 124 160 199 242 288 332 382 444 513
TD10 = 767
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 21
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 759.000
Average ring size = 5.1892