Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_3300902_YCuXtt.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 21.10 T-atoms per nm^3
Material density = 2.106 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5819 Angstrom
T1  -- O2  = 1.6395 Angstrom
T1  -- O3  = 1.6360 Angstrom
T1  -- O4  = 1.6140 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.029725  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021656  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6479 Angstrom
T2  -- O5  = 1.6628 Angstrom
T2  -- O6  = 1.6546 Angstrom
T2  -- O7  = 1.6503 Angstrom
      mean = 1.6539 Angstrom
        t1 = 0.032480  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011818  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6009 Angstrom
T3  -- O8  = 1.6166 Angstrom
T3  -- O9  = 1.6102 Angstrom
T3  -- O10 = 1.5927 Angstrom
      mean = 1.6051 Angstrom
        t1 = 0.015910  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011955  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6568 Angstrom
T4  -- O10 = 1.6035 Angstrom
T4  -- O11 = 1.6403 Angstrom
T4  -- O12 = 1.6441 Angstrom
      mean = 1.6362 Angstrom
        t1 = 0.186029  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.206302  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6085 Angstrom
T5  -- O12 = 1.6085 Angstrom
T5  -- O13 = 1.6343 Angstrom
T5  -- O13 = 1.6343 Angstrom
      mean = 1.6214 Angstrom
        t1 = 0.032884  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029499  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5819 A <--> 1.6628 A
          Mean   = 1.6275 A
          StdDev = 0.0236 A

       t1 Range  = 0.0159 <-- 0.0594 --> 0.1860
       t2 Range  = 0.0118 <-- 0.0562 --> 0.2063

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.590 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.361 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 103.150 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.156 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.497 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.448 deg; O3  -- O4  = 3 A
       103.150 deg <-- 109.367 deg --> 114.156 deg

O3  -- T2  -- O5  = 108.416 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.667 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 104.631 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.008 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 113.421 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.616 deg; O6  -- O7  = 3 A
       104.631 deg <-- 109.460 deg --> 113.421 deg

O4  -- T3  -- O8  = 109.720 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 111.124 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 105.058 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 110.937 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 110.533 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.318 deg; O9  -- O10 = 3 A
       105.058 deg <-- 109.448 deg --> 111.124 deg

O7  -- T4  -- O10 =  72.922 deg; O7  -- O10 = 2 A
O7  -- T4  -- O11 = 132.454 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 =  80.921 deg; O7  -- O12 = 2 A
O10 -- T4  -- O11 =  79.849 deg; O10 -- O11 = 2 A
O10 -- T4  -- O12 = 122.772 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 =  82.194 deg; O11 -- O12 = 2 A
       72.922 deg <-- 95.185 deg --> 132.454 deg

O12 -- T5  -- O12 = 101.350 deg; O12 -- O12 = 2 A
O12 -- T5  -- O13 = 115.013 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.693 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 107.693 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 115.013 deg; O12 -- O13 = 3 A
O13 -- T5  -- O13 = 110.026 deg; O13 -- O13 = 3 A
       101.350 deg <-- 109.465 deg --> 115.013 deg

        O-T-O SUMMARY
          Range  = 72.9221 deg <--> 132.4541 deg
          Mean   = 106.3488 deg
          StdDev = 12.6524 deg

        O--O SUMMARY
          Range  = 1.9380 A <--> 3.0173 A
          Mean   = 2.5888 A
          StdDev = 0.2332 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 128.207 deg ; T1  -- T1   2.8462 A

T1  -- O2  -- T1  = 131.095 deg ; T1  -- T1   2.9849 A

T1  -- O3  -- T2  = 151.132 deg ; T1  -- T2   3.1802 A

T1  -- O4  -- T3  = 130.782 deg ; T1  -- T3   2.9229 A

T2  -- O5  -- T2  = 141.666 deg ; T2  -- T2   3.1413 A

T2  -- O6  -- T2  = 162.471 deg ; T2  -- T2   3.2705 A

T2  -- O7  -- T4  = 167.674 deg ; T2  -- T4   3.2879 A

T3  -- O8  -- T3  = 118.155 deg ; T3  -- T3   2.7737 A

T3  -- O9  -- T3  = 128.486 deg ; T3  -- T3   2.9005 A

T3  -- O10 -- T4  = 135.402 deg ; T3  -- T4   2.9572 A

T4  -- O11 -- T4  = 176.445 deg ; T4  -- T4   3.2790 A

T4  -- O12 -- T5  = 118.359 deg ; T4  -- T5   2.7933 A

T5  -- O13 -- T5  = 112.266 deg ; T5  -- T5   2.7140 A


        T-O-T SUMMARY
          Range  = 112.2659° <--> 176.4452 deg
          Mean   = 139.6805 deg
          StdDev = 19.0220 deg

        T--T SUMMARY
          Range  = 2.7140 A <--> 3.2879 A
          Mean   = 3.0156 A
          StdDev = 0.1920 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O10 = 1.9380 A
O7  -- O12 = 2.1420 A
O10 -- O11 = 2.0820 A
O11 -- O12 = 2.1589 A
O11 -- O12 = 2.1589 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.9849 Angstrom
  T1  -- T2  = 3.1802 Angstrom
  T1  -- T3  = 2.9229 Angstrom
  T1  -- T4  = 2.8725 Angstrom
  T1  -- T1  = 2.8462 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.1802 Angstrom
  T2  -- T2  = 3.2705 Angstrom
  T2  -- T4  = 3.4358 Angstrom
  T2  -- T4  = 3.2879 Angstrom
  T2  -- T2  = 3.1413 Angstrom
T3  -- T3  = 2.7737 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 2.8725 Angstrom
  T4  -- T2  = 3.4358 Angstrom
  T4  -- T2  = 3.2879 Angstrom
  T4  -- T3  = 2.9572 Angstrom
  T4  -- T4  = 3.2790 Angstrom
  T4  -- T5  = 2.7933 Angstrom
T5  -- T4  = 2.7933 Angstrom
T5  -- T4  = 2.7933 Angstrom
T5  -- T5  = 2.7140 Angstrom
T5  -- T5  = 2.7140 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 49 70 98 130 159 188 226 273 326 386 452 513
TD10 = 758
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 14
Vertex symbol  = 4.4.4.6_{2}.8_{2}.8_{2}
Weight = 22

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 328 377 430 491
TD10 = 763
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 328 377 430 491
TD10 = 763
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 328 377 430 491
TD10 = 763
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 32 49 70 98 130 159 188 226 273 326 386 452 513
TD10 = 758
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 14
Vertex symbol  = 4.4.4.6_{2}.8_{2}.8_{2}
Weight = 22

<TD10> = 761.333
Average ring size = 5.4783