Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_3300407_SEyPAR.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 19.68 T-atoms per nm^3
Material density = 1.963 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6554 Angstrom
T1  -- O2  = 1.6205 Angstrom
T1  -- O3  = 1.6426 Angstrom
T1  -- O4  = 1.6399 Angstrom
      mean = 1.6396 Angstrom
        t1 = 0.026471  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018196  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6148 Angstrom
T2  -- O5  = 1.5791 Angstrom
T2  -- O6  = 1.6329 Angstrom
T2  -- O7  = 1.6145 Angstrom
      mean = 1.6103 Angstrom
        t1 = 0.026855  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023612  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6458 Angstrom
T3  -- O8  = 1.6288 Angstrom
T3  -- O9  = 1.6338 Angstrom
T3  -- O10 = 1.6190 Angstrom
      mean = 1.6319 Angstrom
        t1 = 0.017014  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007245  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.5942 Angstrom
T4  -- O10 = 1.6054 Angstrom
T4  -- O11 = 1.6270 Angstrom
T4  -- O12 = 1.6112 Angstrom
      mean = 1.6095 Angstrom
        t1 = 0.014320  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011697  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6154 Angstrom
T5  -- O12 = 1.6154 Angstrom
T5  -- O13 = 1.6248 Angstrom
T5  -- O13 = 1.6248 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.007192  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002955  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5791 A <--> 1.6554 A
          Mean   = 1.6225 A
          StdDev = 0.0182 A

       t1 Range  = 0.0072 <-- 0.0184 --> 0.0269
       t2 Range  = 0.0030 <-- 0.0127 --> 0.0236

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.065 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.005 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.761 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.418 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.989 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.426 deg; O3  -- O4  = 3 A
       106.426 deg <-- 109.444 deg --> 113.761 deg

O3  -- T2  -- O5  = 104.306 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 112.202 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 112.656 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.105 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 105.932 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 112.084 deg; O6  -- O7  = 3 A
       104.306 deg <-- 109.381 deg --> 112.656 deg

O4  -- T3  -- O8  = 108.899 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.391 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 106.261 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 111.078 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.265 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 111.796 deg; O9  -- O10 = 3 A
       106.261 deg <-- 109.448 deg --> 111.796 deg

O7  -- T4  -- O10 = 106.493 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 111.248 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 107.762 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 109.736 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 111.739 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.820 deg; O11 -- O12 = 3 A
       106.493 deg <-- 109.466 deg --> 111.739 deg

O12 -- T5  -- O12 = 109.399 deg; O12 -- O12 = 3 A
O12 -- T5  -- O13 = 108.977 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 110.247 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 110.247 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 108.977 deg; O12 -- O13 = 3 A
O13 -- T5  -- O13 = 108.985 deg; O13 -- O13 = 3 A
       108.977 deg <-- 109.472 deg --> 110.247 deg

        O-T-O SUMMARY
          Range  = 104.3063 deg <--> 113.7615 deg
          Mean   = 109.4518 deg
          StdDev = 2.2497 deg

        O--O SUMMARY
          Range  = 2.5222 A <--> 2.7600 A
          Mean   = 2.6481 A
          StdDev = 0.0497 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 151.711 deg; T1  -- T2  = 5.7058 A
T1  - O1  - T1  - O3  - T3  =  89.678 deg; T1  -- T3  = 4.1725 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2648 A
T2  - O2  - T1  - O3  - T3  = 100.896 deg; T2  -- T3  = 4.5683 A
T2  - O2  - T1  - O4  - T1  =  89.927 deg; T2  -- T1  = 4.2672 A
T3  - O3  - T1  - O4  - T1  = 157.297 deg; T3  -- T1  = 5.9513 A

T1  - O3  - T2  - O5  - T2  = 106.711 deg; T1  -- T2  = 4.7109 A
T1  - O3  - T2  - O6  - T4  = 117.407 deg; T1  -- T4  = 5.0398 A
T1  - O3  - T2  - O7  - T2  =  90.073 deg; T1  -- T2  = 4.2672 A
T2  - O5  - T2  - O6  - T4  = 129.260 deg; T2  -- T4  = 5.3108 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.2505 A
T4  - O6  - T2  - O7  - T2  = 112.716 deg; T4  -- T2  = 5.0253 A

T1  - O4  - T3  - O8  - T3  = 105.600 deg; T1  -- T3  = 4.7763 A
T1  - O4  - T3  - O9  - T4  =  99.169 deg; T1  -- T4  = 4.5924 A
T1  - O4  - T3  - O10 - T3  =  90.322 deg; T1  -- T3  = 4.1725 A
T3  - O8  - T3  - O9  - T4  = 126.652 deg; T3  -- T4  = 5.4241 A
T3  - O8  - T3  - O10 - T3  = 135.000 deg; T3  -- T3  = 5.4717 A
T4  - O9  - T3  - O10 - T3  =  90.287 deg; T4  -- T3  = 4.2244 A

T2  - O7  - T4  - O10 - T3  = 103.385 deg; T2  -- T3  = 4.7123 A
T2  - O7  - T4  - O11 - T5  = 100.037 deg; T2  -- T5  = 4.6516 A
T2  - O7  - T4  - O12 - T4  = 157.225 deg; T2  -- T4  = 5.7717 A
T3  - O10 - T4  - O11 - T5  = 116.988 deg; T3  -- T5  = 5.2601 A
T3  - O10 - T4  - O12 - T4  =  89.713 deg; T3  -- T4  = 4.2244 A
T5  - O11 - T4  - O12 - T4  =  90.140 deg; T5  -- T4  = 4.2868 A

T4  - O12 - T5  - O12 - T4  = 105.761 deg; T4  -- T4  = 4.9706 A
T4  - O12 - T5  - O13 - T5  = 148.859 deg; T4  -- T5  = 5.8450 A
T4  - O12 - T5  - O13 - T5  =  89.860 deg; T4  -- T5  = 4.2868 A
T4  - O12 - T5  - O13 - T5  =  89.860 deg; T4  -- T5  = 4.2868 A
T4  - O12 - T5  - O13 - T5  = 148.859 deg; T4  -- T5  = 5.8450 A
T5  - O13 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 4.1729 A

        T-T-T SUMMARY
          Range  = 89.6784 deg <--> 157.2968 deg
          Mean   = 109.0922 deg
          StdDev = 22.6840 deg

        T--T SUMMARY
          Range  = 4.1725 A <--> 5.9513 A
          Mean   = 4.7930 A
          StdDev = 0.5894 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.018 deg ; T1  -- T1   3.0911 A

T1  -- O2  -- T1  = 130.076 deg ; T1  -- T1   2.9383 A

T1  -- O3  -- T2  = 129.467 deg ; T1  -- T2   2.9458 A

T1  -- O4  -- T3  = 130.081 deg ; T1  -- T3   2.9789 A

T2  -- O5  -- T2  = 155.016 deg ; T2  -- T2   3.0835 A

T2  -- O6  -- T2  = 127.224 deg ; T2  -- T2   2.9255 A

T2  -- O7  -- T4  = 133.866 deg ; T2  -- T4   2.9522 A

T3  -- O8  -- T3  = 126.186 deg ; T3  -- T3   2.9049 A

T3  -- O9  -- T3  = 134.863 deg ; T3  -- T3   3.0175 A

T3  -- O10 -- T4  = 142.425 deg ; T3  -- T4   3.0526 A

T4  -- O11 -- T4  = 128.870 deg ; T4  -- T4   2.9354 A

T4  -- O12 -- T5  = 150.030 deg ; T4  -- T5   3.1168 A

T5  -- O13 -- T5  = 130.473 deg ; T5  -- T5   2.9507 A


        T-O-T SUMMARY
          Range  = 126.1860° <--> 155.0158 deg
          Mean   = 135.3087 deg
          StdDev = 8.7558 deg

        T--T SUMMARY
          Range  = 2.9049 A <--> 3.1168 A
          Mean   = 2.9934 A
          StdDev = 0.0699 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 49 70 98 130 159 188 226 273 326 386 452 513
TD10 = 758
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 14
Vertex symbol  = 4.4.4.6_{2}.8_{2}.8_{2}
Weight = 22

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 328 377 430 491
TD10 = 763
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 328 377 430 491
TD10 = 763
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 328 377 430 491
TD10 = 763
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 32 49 70 98 130 159 188 226 273 326 386 452 513
TD10 = 758
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 14
Vertex symbol  = 4.4.4.6_{2}.8_{2}.8_{2}
Weight = 22

<TD10> = 761.333
Average ring size = 5.4783