Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_2692620_IYOlyK.cif"

There are 160 T-atoms per unit cell
There are 320 O-atoms per unit cell

Framework density = 15.99 T-atoms per nm^3
Material density = 1.596 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6199 Angstrom
T1  -- O2  = 1.6224 Angstrom
T1  -- O3  = 1.6243 Angstrom
T1  -- O4  = 1.6210 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.009585  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004005  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6268 Angstrom
T2  -- O5  = 1.6208 Angstrom
T2  -- O6  = 1.6201 Angstrom
T2  -- O7  = 1.6261 Angstrom
      mean = 1.6234 Angstrom
        t1 = 0.008743  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001881  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6265 Angstrom
T3  -- O8  = 1.6245 Angstrom
T3  -- O9  = 1.6170 Angstrom
T3  -- O10 = 1.6289 Angstrom
      mean = 1.6242 Angstrom
        t1 = 0.009474  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003732  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6238 Angstrom
T4  -- O10 = 1.6269 Angstrom
T4  -- O11 = 1.6222 Angstrom
T4  -- O12 = 1.6225 Angstrom
      mean = 1.6238 Angstrom
        t1 = 0.009123  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002147  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6254 Angstrom
T5  -- O12 = 1.6219 Angstrom
T5  -- O13 = 1.6240 Angstrom
T5  -- O14 = 1.6247 Angstrom
      mean = 1.6240 Angstrom
        t1 = 0.008898  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001362  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6170 A <--> 1.6289 A
          Mean   = 1.6235 A
          StdDev = 0.0028 A

       t1 Range  = 0.0087 <-- 0.0092 --> 0.0096
       t2 Range  = 0.0014 <-- 0.0026 --> 0.0040

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.513 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.682 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.630 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.455 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.927 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.577 deg; O3  -- O4  = 3 A
       107.577 deg <-- 109.464 deg --> 110.513 deg

O2  -- T2  -- O5  = 109.327 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 109.233 deg; O2  -- O6  = 3 A
O2  -- T2  -- O7  = 110.087 deg; O2  -- O7  = 3 A
O5  -- T2  -- O6  = 109.460 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.421 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.299 deg; O6  -- O7  = 3 A
       109.233 deg <-- 109.471 deg --> 110.087 deg

O3  -- T3  -- O8  = 110.249 deg; O3  -- O8  = 3 A
O3  -- T3  -- O9  = 108.935 deg; O3  -- O9  = 3 A
O3  -- T3  -- O10 = 109.078 deg; O3  -- O10 = 3 A
O8  -- T3  -- O9  = 109.288 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.513 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.764 deg; O9  -- O10 = 3 A
       108.935 deg <-- 109.471 deg --> 110.249 deg

O4  -- T4  -- O10 = 108.708 deg; O4  -- O10 = 3 A
O4  -- T4  -- O11 = 109.315 deg; O4  -- O11 = 3 A
O4  -- T4  -- O12 = 109.329 deg; O4  -- O12 = 3 A
O10 -- T4  -- O11 = 110.212 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.910 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.348 deg; O11 -- O12 = 3 A
       108.708 deg <-- 109.470 deg --> 110.212 deg

O7  -- T5  -- O12 = 108.949 deg; O7  -- O12 = 3 A
O7  -- T5  -- O13 = 109.554 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 109.701 deg; O7  -- O14 = 3 A
O12 -- T5  -- O13 = 109.350 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 109.516 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 109.753 deg; O13 -- O14 = 3 A
       108.949 deg <-- 109.471 deg --> 109.753 deg

        O-T-O SUMMARY
          Range  = 107.5774 deg <--> 110.5130 deg
          Mean   = 109.4678 deg
          StdDev = 0.5751 deg

        O--O SUMMARY
          Range  = 2.6184 A <--> 2.6671 A
          Mean   = 2.6512 A
          StdDev = 0.0101 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 123.832 deg; T1  -- T2  = 5.3648 A
T1  - O1  - T1  - O3  - T3  = 118.827 deg; T1  -- T3  = 5.1981 A
T1  - O1  - T1  - O4  - T4  = 144.834 deg; T1  -- T4  = 5.7370 A
T2  - O2  - T1  - O3  - T3  = 105.693 deg; T2  -- T3  = 4.7460 A
T2  - O2  - T1  - O4  - T4  =  86.154 deg; T2  -- T4  = 4.0536 A
T3  - O3  - T1  - O4  - T4  =  60.070 deg; T3  -- T4  = 2.9491 A

T1  - O2  - T2  - O5  - T2  = 125.868 deg; T1  -- T2  = 5.3717 A
T1  - O2  - T2  - O6  - T5  =  91.539 deg; T1  -- T5  = 4.3214 A
T1  - O2  - T2  - O7  - T2  = 141.714 deg; T1  -- T2  = 5.6825 A
T2  - O5  - T2  - O6  - T5  =  90.149 deg; T2  -- T5  = 4.2947 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.2780 A
T5  - O6  - T2  - O7  - T2  = 102.389 deg; T5  -- T2  = 4.7135 A

T1  - O3  - T3  - O8  - T4  =  59.633 deg; T1  -- T4  = 2.9361 A
T1  - O3  - T3  - O9  - T3  = 125.744 deg; T1  -- T3  = 5.3848 A
T1  - O3  - T3  - O10 - T3  = 143.680 deg; T1  -- T3  = 5.6219 A
T4  - O8  - T3  - O9  - T3  = 109.982 deg; T4  -- T3  = 4.9505 A
T4  - O8  - T3  - O10 - T3  = 118.543 deg; T4  -- T3  = 5.0801 A
T3  - O9  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.2825 A

T1  - O4  - T4  - O10 - T3  =  60.298 deg; T1  -- T3  = 2.9559 A
T1  - O4  - T4  - O11 - T4  = 118.112 deg; T1  -- T4  = 4.9942 A
T1  - O4  - T4  - O12 - T5  =  93.384 deg; T1  -- T5  = 4.3214 A
T3  - O10 - T4  - O11 - T4  = 144.476 deg; T3  -- T4  = 5.5578 A
T3  - O10 - T4  - O12 - T5  = 123.269 deg; T3  -- T5  = 5.2369 A
T4  - O11 - T4  - O12 - T5  =  91.889 deg; T4  -- T5  = 4.2330 A

T2  - O7  - T5  - O12 - T4  =  84.404 deg; T2  -- T4  = 4.0536 A
T2  - O7  - T5  - O13 - T5  =  89.851 deg; T2  -- T5  = 4.2947 A
T2  - O7  - T5  - O14 - T5  = 133.827 deg; T2  -- T5  = 5.6270 A
T4  - O12 - T5  - O13 - T5  = 110.068 deg; T4  -- T5  = 4.9593 A
T4  - O12 - T5  - O14 - T5  =  88.111 deg; T4  -- T5  = 4.2330 A
T5  - O13 - T5  - O14 - T5  = 135.000 deg; T5  -- T5  = 5.6672 A

        T-T-T SUMMARY
          Range  = 59.6329 deg <--> 144.8336 deg
          Mean   = 106.4482 deg
          StdDev = 24.9868 deg

        T--T SUMMARY
          Range  = 2.9361 A <--> 5.7370 A
          Mean   = 4.6893 A
          StdDev = 0.8074 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 144.064 deg ; T1  -- T1   3.0819 A

T1  -- O2  -- T2  = 134.717 deg ; T1  -- T2   2.9988 A

T1  -- O3  -- T3  = 130.811 deg ; T1  -- T3   2.9559 A

T1  -- O4  -- T4  = 129.610 deg ; T1  -- T4   2.9361 A

T2  -- O5  -- T2  = 137.023 deg ; T2  -- T2   3.0164 A

T2  -- O6  -- T2  = 138.858 deg ; T2  -- T2   3.0335 A

T2  -- O7  -- T5  = 137.669 deg ; T2  -- T5   3.0321 A

T3  -- O8  -- T3  = 131.367 deg ; T3  -- T3   2.9608 A

T3  -- O9  -- T3  = 146.167 deg ; T3  -- T3   3.0941 A

T3  -- O10 -- T4  = 129.868 deg ; T3  -- T4   2.9491 A

T4  -- O11 -- T4  = 125.688 deg ; T4  -- T4   2.8868 A

T4  -- O12 -- T5  = 135.444 deg ; T4  -- T5   3.0022 A

T5  -- O13 -- T5  = 139.719 deg ; T5  -- T5   3.0493 A

T5  -- O14 -- T5  = 143.374 deg ; T5  -- T5   3.0848 A


        T-O-T SUMMARY
          Range  = 125.6882° <--> 146.1670 deg
          Mean   = 136.0271 deg
          StdDev = 5.8845 deg

        T--T SUMMARY
          Range  = 2.8868 A <--> 3.0941 A
          Mean   = 3.0058 A
          StdDev = 0.0599 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 29 44 67 91 119 144 181 223 262 304 356 413 472
TD10 = 707
Circuit symbol = 3.8.4.8.5.8
Weight = 21
Vertex symbol  = 3.8.4.8.6.8
Weight = 24

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 17 30 48 64 84 119 156 186 213 252 310 366 410 459
TD10 = 718
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8
Weight = 21

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 17 29 46 65 87 117 147 179 221 262 302 350 407 471
TD10 = 701
Circuit symbol = 3.4.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 8 16 28 44 62 84 118 152 183 216 256 311 359 400 452
TD10 = 700
Circuit symbol = 3.4.4.7.5.6
Weight = 7
Vertex symbol  = 3.4.4.8.6.8
Weight = 20

T5 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 16 27 43 63 87 115 150 191 231 267 302 345 399 465
TD10 = 706
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8
Weight = 21

<TD10> = 706.400
Average ring size = 5.1064