Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_5_2449050_bZbVJi.cif"

There are 160 T-atoms per unit cell
There are 320 O-atoms per unit cell

Framework density = 17.22 T-atoms per nm^3
Material density = 1.718 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6215 Angstrom
T1  -- O2  = 1.6151 Angstrom
T1  -- O3  = 1.6241 Angstrom
T1  -- O4  = 1.6185 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006470  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003040  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6245 Angstrom
T2  -- O5  = 1.6204 Angstrom
T2  -- O6  = 1.6207 Angstrom
T2  -- O7  = 1.6252 Angstrom
      mean = 1.6227 Angstrom
        t1 = 0.008101  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001183  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6185 Angstrom
T3  -- O8  = 1.6206 Angstrom
T3  -- O9  = 1.6199 Angstrom
T3  -- O10 = 1.6181 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.005939  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001151  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6236 Angstrom
T4  -- O11 = 1.6246 Angstrom
T4  -- O12 = 1.6218 Angstrom
T4  -- O13 = 1.6235 Angstrom
      mean = 1.6234 Angstrom
        t1 = 0.008507  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001668  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6178 Angstrom
T5  -- O13 = 1.6228 Angstrom
T5  -- O14 = 1.6184 Angstrom
T5  -- O15 = 1.6193 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.006335  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002451  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6151 A <--> 1.6252 A
          Mean   = 1.6209 A
          StdDev = 0.0027 A

       t1 Range  = 0.0059 <-- 0.0071 --> 0.0085
       t2 Range  = 0.0012 <-- 0.0019 --> 0.0030

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.475 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.861 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.044 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.474 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.488 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.484 deg; O3  -- O4  = 3 A
       109.044 deg <-- 109.471 deg --> 109.861 deg

O3  -- T2  -- O5  = 109.414 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.403 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.757 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.198 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.556 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.497 deg; O6  -- O7  = 3 A
       109.198 deg <-- 109.471 deg --> 109.757 deg

O4  -- T3  -- O8  = 109.415 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.645 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.125 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.285 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.509 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.848 deg; O9  -- O10 = 3 A
       109.125 deg <-- 109.471 deg --> 109.848 deg

O7  -- T4  -- O11 = 109.982 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.227 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 109.268 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 109.292 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.469 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.589 deg; O12 -- O13 = 3 A
       109.227 deg <-- 109.471 deg --> 109.982 deg

O10 -- T5  -- O13 = 110.059 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 109.096 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 109.536 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 109.386 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.259 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 109.491 deg; O14 -- O15 = 3 A
       109.096 deg <-- 109.471 deg --> 110.059 deg

        O-T-O SUMMARY
          Range  = 109.0442 deg <--> 110.0589 deg
          Mean   = 109.4823 deg
          StdDev = 0.2498 deg

        O--O SUMMARY
          Range  = 2.6362 A <--> 2.6605 A
          Mean   = 2.6473 A
          StdDev = 0.0059 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4348 A
T1  - O1  - T1  - O3  - T2  = 119.466 deg; T1  -- T2  = 5.2545 A
T1  - O1  - T1  - O4  - T3  = 122.085 deg; T1  -- T3  = 5.3168 A
T1  - O2  - T1  - O3  - T2  =  88.418 deg; T1  -- T2  = 4.3769 A
T1  - O2  - T1  - O4  - T3  =  89.100 deg; T1  -- T3  = 4.3986 A
T2  - O3  - T1  - O4  - T3  = 118.388 deg; T2  -- T3  = 5.2237 A

T1  - O3  - T2  - O5  - T2  = 126.341 deg; T1  -- T2  = 5.4658 A
T1  - O3  - T2  - O6  - T2  =  91.582 deg; T1  -- T2  = 4.3769 A
T1  - O3  - T2  - O7  - T4  =  99.995 deg; T1  -- T4  = 4.6495 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.6745 A
T2  - O5  - T2  - O7  - T4  =  89.064 deg; T2  -- T4  = 4.2821 A
T2  - O6  - T2  - O7  - T4  = 109.166 deg; T2  -- T4  = 4.9603 A

T1  - O4  - T3  - O8  - T3  =  90.900 deg; T1  -- T3  = 4.3986 A
T1  - O4  - T3  - O9  - T5  =  91.835 deg; T1  -- T5  = 4.3592 A
T1  - O4  - T3  - O10 - T3  = 126.250 deg; T1  -- T3  = 5.4366 A
T3  - O8  - T3  - O9  - T5  =  88.942 deg; T3  -- T5  = 4.3198 A
T3  - O8  - T3  - O10 - T3  = 135.000 deg; T3  -- T3  = 5.7205 A
T5  - O9  - T3  - O10 - T3  = 111.335 deg; T5  -- T3  = 5.0280 A

T2  - O7  - T4  - O11 - T4  =  90.936 deg; T2  -- T4  = 4.2821 A
T2  - O7  - T4  - O12 - T5  = 100.002 deg; T2  -- T5  = 4.5957 A
T2  - O7  - T4  - O13 - T4  = 153.368 deg; T2  -- T4  = 5.8605 A
T4  - O11 - T4  - O12 - T5  = 154.910 deg; T4  -- T5  = 5.8135 A
T4  - O11 - T4  - O13 - T4  =  90.000 deg; T4  -- T4  = 4.2278 A
T5  - O12 - T4  - O13 - T4  =  90.095 deg; T5  -- T4  = 4.2259 A

T3  - O10 - T5  - O13 - T4  = 117.488 deg; T3  -- T4  = 5.1337 A
T3  - O10 - T5  - O14 - T5  =  91.058 deg; T3  -- T5  = 4.3198 A
T3  - O10 - T5  - O15 - T5  = 150.238 deg; T3  -- T5  = 5.8359 A
T4  - O13 - T5  - O14 - T5  = 109.910 deg; T4  -- T5  = 4.9092 A
T4  - O13 - T5  - O15 - T5  =  89.905 deg; T4  -- T5  = 4.2259 A
T5  - O14 - T5  - O15 - T5  =  90.000 deg; T5  -- T5  = 4.2635 A

        T-T-T SUMMARY
          Range  = 88.4177 deg <--> 154.9098 deg
          Mean   = 108.0491 deg
          StdDev = 20.3324 deg

        T--T SUMMARY
          Range  = 4.2259 A <--> 5.8605 A
          Mean   = 4.8406 A
          StdDev = 0.5601 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 139.162 deg ; T1  -- T1   3.0392 A

T1  -- O2  -- T1  = 178.060 deg ; T1  -- T1   3.2296 A

T1  -- O3  -- T2  = 139.174 deg ; T1  -- T2   3.0446 A

T1  -- O4  -- T3  = 139.540 deg ; T1  -- T3   3.0373 A

T2  -- O5  -- T2  = 143.799 deg ; T2  -- T2   3.0805 A

T2  -- O6  -- T2  = 141.645 deg ; T2  -- T2   3.0615 A

T2  -- O7  -- T4  = 137.222 deg ; T2  -- T4   3.0251 A

T3  -- O8  -- T3  = 141.251 deg ; T3  -- T3   3.0576 A

T3  -- O9  -- T3  = 150.666 deg ; T3  -- T3   3.1342 A

T3  -- O10 -- T5  = 139.025 deg ; T3  -- T5   3.0312 A

T4  -- O11 -- T4  = 134.591 deg ; T4  -- T4   2.9974 A

T4  -- O12 -- T4  = 133.631 deg ; T4  -- T4   2.9817 A

T4  -- O13 -- T5  = 132.725 deg ; T4  -- T5   2.9740 A

T5  -- O14 -- T5  = 136.579 deg ; T5  -- T5   3.0072 A

T5  -- O15 -- T5  = 137.871 deg ; T5  -- T5   3.0223 A


        T-O-T SUMMARY
          Range  = 132.7253° <--> 178.0599 deg
          Mean   = 141.6627 deg
          StdDev = 10.6218 deg

        T--T SUMMARY
          Range  = 2.9740 A <--> 3.2296 A
          Mean   = 3.0482 A
          StdDev = 0.0620 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 34 54 73 94 125 168 212 250 291 345 407 464 522
TD10 = 792
Circuit symbol = 4.5.4.6.4.6
Weight = 10
Vertex symbol  = 4.5.4.8.4.8
Weight = 20

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 19 31 49 74 104 136 169 205 245 291 345 404 470 540
TD10 = 802
Circuit symbol = 4.4.5.8_{2}.6.7
Weight = 16
Vertex symbol  = 4.4.5.8.6.8
Weight = 21

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 20 34 53 78 105 132 165 205 252 305 358 411 469 531
TD10 = 807
Circuit symbol = 4.8.4.8.5.8
Weight = 24
Vertex symbol  = 4.8.4.8.5.8
Weight = 24

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 16 26 45 73 102 132 168 211 253 289 334 400 474 540
TD10 = 787
Circuit symbol = 4.4.4.5.6.6
Weight = 10
Vertex symbol  = 4.4.4.5.8_{2}.12_{2}
Weight = 28

T5 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 16 28 48 71 98 134 175 213 245 289 356 424 476 525
TD10 = 797
Circuit symbol = 4.4.4.5.6.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.5.6.8
Weight = 17

<TD10> = 797.000
Average ring size = 5.3333