Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_4_42015__gUorn.cif"

There are 128 T-atoms per unit cell
There are 256 O-atoms per unit cell

Framework density = 19.40 T-atoms per nm^3
Material density = 1.935 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6091 Angstrom
T1  -- O2  = 1.6244 Angstrom
T1  -- O3  = 1.6327 Angstrom
T1  -- O4  = 1.6087 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.024014  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018788  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6148 Angstrom
T2  -- O5  = 1.6230 Angstrom
T2  -- O6  = 1.6234 Angstrom
T2  -- O7  = 1.6335 Angstrom
      mean = 1.6237 Angstrom
        t1 = 0.011108  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008321  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6342 Angstrom
T3  -- O8  = 1.6310 Angstrom
T3  -- O9  = 1.6298 Angstrom
T3  -- O10 = 1.6279 Angstrom
      mean = 1.6307 Angstrom
        t1 = 0.013329  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002216  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6300 Angstrom
T4  -- O11 = 1.6188 Angstrom
T4  -- O12 = 1.6279 Angstrom
T4  -- O13 = 1.6263 Angstrom
      mean = 1.6257 Angstrom
        t1 = 0.010642  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004387  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6087 A <--> 1.6342 A
          Mean   = 1.6247 A
          StdDev = 0.0079 A

       t1 Range  = 0.0106 <-- 0.0148 --> 0.0240
       t2 Range  = 0.0022 <-- 0.0084 --> 0.0188

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.751 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.134 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 102.497 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.618 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.962 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.498 deg; O3  -- O4  = 3 A
       102.497 deg <-- 109.410 deg --> 112.134 deg

O4  -- T2  -- O5  = 108.777 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.137 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 110.952 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.037 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.957 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.959 deg; O6  -- O7  = 3 A
       108.137 deg <-- 109.470 deg --> 110.952 deg

O7  -- T3  -- O8  = 109.878 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.290 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 108.361 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 110.045 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.806 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.433 deg; O9  -- O10 = 3 A
       108.361 deg <-- 109.469 deg --> 110.045 deg

O10 -- T4  -- O11 = 108.660 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 110.044 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 = 109.685 deg; O10 -- O13 = 3 A
O11 -- T4  -- O12 = 109.221 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.271 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.935 deg; O12 -- O13 = 3 A
       108.660 deg <-- 109.469 deg --> 110.044 deg

        O-T-O SUMMARY
          Range  = 102.4975 deg <--> 112.1337 deg
          Mean   = 109.2701 deg
          StdDev = 1.7727 deg

        O--O SUMMARY
          Range  = 2.5094 A <--> 2.6942 A
          Mean   = 2.6498 A
          StdDev = 0.0359 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.2422 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.0663 A
T1  - O1  - T1  - O4  - T2  =  89.957 deg; T1  -- T2  = 4.2056 A
T1  - O2  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 5.4016 A
T1  - O2  - T1  - O4  - T2  =  90.677 deg; T1  -- T2  = 4.2982 A
T1  - O3  - T1  - O4  - T2  =  89.085 deg; T1  -- T2  = 4.2889 A

T1  - O4  - T2  - O5  - T2  =  90.915 deg; T1  -- T2  = 4.2889 A
T1  - O4  - T2  - O6  - T3  = 123.178 deg; T1  -- T3  = 5.3687 A
T1  - O4  - T2  - O7  - T2  =  89.323 deg; T1  -- T2  = 4.2982 A
T2  - O5  - T2  - O6  - T3  =  92.485 deg; T2  -- T3  = 4.1980 A
T2  - O5  - T2  - O7  - T2  = 135.000 deg; T2  -- T2  = 5.3775 A
T3  - O6  - T2  - O7  - T2  = 124.078 deg; T3  -- T2  = 5.2224 A

T2  - O7  - T3  - O8  - T3  = 128.435 deg; T2  -- T3  = 5.5646 A
T2  - O7  - T3  - O9  - T3  =  87.515 deg; T2  -- T3  = 4.1980 A
T2  - O7  - T3  - O10 - T4  =  78.371 deg; T2  -- T4  = 3.8443 A
T3  - O8  - T3  - O9  - T3  = 135.000 deg; T3  -- T3  = 5.8595 A
T3  - O8  - T3  - O10 - T4  = 120.012 deg; T3  -- T4  = 5.5043 A
T3  - O9  - T3  - O10 - T4  =  89.885 deg; T3  -- T4  = 4.4110 A

T3  - O10 - T4  - O11 - T4  =  90.115 deg; T3  -- T4  = 4.4110 A
T3  - O10 - T4  - O12 - T4  = 119.824 deg; T3  -- T4  = 5.4385 A
T3  - O10 - T4  - O13 - T4  = 135.142 deg; T3  -- T4  = 5.7617 A
T4  - O11 - T4  - O12 - T4  = 135.000 deg; T4  -- T4  = 5.7833 A
T4  - O11 - T4  - O13 - T4  =  90.000 deg; T4  -- T4  = 4.3894 A
T4  - O12 - T4  - O13 - T4  =  90.000 deg; T4  -- T4  = 4.4275 A

        T-T-T SUMMARY
          Range  = 78.3705 deg <--> 135.1421 deg
          Mean   = 106.6377 deg
          StdDev = 20.3299 deg

        T--T SUMMARY
          Range  = 3.8443 A <--> 5.8595 A
          Mean   = 4.8083 A
          StdDev = 0.6382 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.053 deg ; T1  -- T1   2.7877 A

T1  -- O2  -- T1  = 125.341 deg ; T1  -- T1   2.8862 A

T1  -- O3  -- T1  = 130.068 deg ; T1  -- T1   2.9603 A

T1  -- O4  -- T2  = 155.662 deg ; T1  -- T2   3.1510 A

T2  -- O5  -- T2  = 131.604 deg ; T2  -- T2   2.9607 A

T2  -- O6  -- T2  = 123.468 deg ; T2  -- T2   2.8597 A

T2  -- O7  -- T3  = 129.207 deg ; T2  -- T3   2.9519 A

T3  -- O8  -- T3  = 163.080 deg ; T3  -- T3   3.2265 A

T3  -- O9  -- T3  = 145.810 deg ; T3  -- T3   3.1156 A

T3  -- O10 -- T4  = 147.611 deg ; T3  -- T4   3.1286 A

T4  -- O11 -- T4  = 147.044 deg ; T4  -- T4   3.1045 A

T4  -- O12 -- T4  = 151.655 deg ; T4  -- T4   3.1567 A

T4  -- O13 -- T4  = 145.121 deg ; T4  -- T4   3.1031 A


        T-O-T SUMMARY
          Range  = 120.0535° <--> 163.0801 deg
          Mean   = 139.6711 deg
          StdDev = 13.1765 deg

        T--T SUMMARY
          Range  = 2.7877 A <--> 3.2265 A
          Mean   = 3.0302 A
          StdDev = 0.1307 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7877 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 49 70 97 127 159 196 236 279 329 384 441 502
TD10 = 762
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 17
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 25

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 50 73 99 126 156 191 234 284 337 390 441 495
TD10 = 759
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 21 36 52 70 94 124 160 202 243 283 328 379 438 503
TD10 = 774
Circuit symbol = 4.8_{3}.4.8_{3}.6_{2}.8
Weight = 28
Vertex symbol  = 4.8_{3}.4.8_{3}.6.8
Weight = 28

T4 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 50 74 103 132 161 193 231 278 332 387 440 495
TD10 = 777
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

<TD10> = 768.000
Average ring size = 5.6585