Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_2_86_bWnKj2.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 15.56 T-atoms per nm^3
Material density = 1.552 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5938 Angstrom
T1  -- O2  = 1.6245 Angstrom
T1  -- O2  = 1.6245 Angstrom
T1  -- O1  = 1.5938 Angstrom
      mean = 1.6092 Angstrom
        t1 = 0.025739  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018436  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6642 Angstrom
T2  -- O3  = 1.6158 Angstrom
T2  -- O4  = 1.6184 Angstrom
T2  -- O4  = 1.6184 Angstrom
      mean = 1.6292 Angstrom
        t1 = 0.016235  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010238  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5938 A <--> 1.6642 A
          Mean   = 1.6225 A
          StdDev = 0.0211 A

       t1 Range  = 0.0162 <-- 0.0210 --> 0.0257
       t2 Range  = 0.0102 <-- 0.0143 --> 0.0184

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.207 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 107.207 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 110.619 deg; O1  -- O1  = 3 A
O2  -- T1  -- O2  = 117.365 deg; O2  -- O2  = 3 A
O2  -- T1  -- O1  = 107.207 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 107.207 deg; O2  -- O1  = 3 A
       107.207 deg <-- 109.469 deg --> 117.365 deg

O2  -- T2  -- O3  = 109.621 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 110.205 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 110.205 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.321 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.321 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 108.140 deg; O4  -- O4  = 3 A
       108.140 deg <-- 109.469 deg --> 110.205 deg

        O-T-O SUMMARY
          Range  = 107.2073 deg <--> 117.3652 deg
          Mean   = 109.4189 deg
          StdDev = 2.7478 deg

        O--O SUMMARY
          Range  = 2.5906 A <--> 2.7757 A
          Mean   = 2.6445 A
          StdDev = 0.0558 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.408 deg; T1  -- T2  = 4.2860 A
T1  - O1  - T1  - O2  - T2  =  90.408 deg; T1  -- T2  = 4.2860 A
T1  - O1  - T1  - O1  - T1  = 110.619 deg; T1  -- T1  = 5.2420 A
T2  - O2  - T1  - O2  - T2  = 178.567 deg; T2  -- T2  = 5.6846 A
T2  - O2  - T1  - O1  - T1  =  90.408 deg; T2  -- T1  = 4.2860 A
T2  - O2  - T1  - O1  - T1  =  90.408 deg; T2  -- T1  = 4.2860 A

T1  - O2  - T2  - O3  - T2  =  89.582 deg; T1  -- T2  = 4.2860 A
T1  - O2  - T2  - O4  - T2  = 135.716 deg; T1  -- T2  = 5.6217 A
T1  - O2  - T2  - O4  - T2  =  89.582 deg; T1  -- T2  = 4.2860 A
T2  - O3  - T2  - O4  - T2  = 114.388 deg; T2  -- T2  = 5.4242 A
T2  - O3  - T2  - O4  - T2  = 108.544 deg; T2  -- T2  = 5.2420 A
T2  - O4  - T2  - O4  - T2  = 114.388 deg; T2  -- T2  = 5.4242 A

        T-T-T SUMMARY
          Range  = 89.5816 deg <--> 178.5671 deg
          Mean   = 108.4962 deg
          StdDev = 26.0254 deg

        T--T SUMMARY
          Range  = 4.2860 A <--> 5.6846 A
          Mean   = 4.8464 A
          StdDev = 0.5980 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1876 A

T1  -- O2  -- T2  = 119.603 deg ; T1  -- T2   2.8425 A

T2  -- O3  -- T2  = 172.598 deg ; T2  -- T2   3.2248 A

T2  -- O4  -- T2  = 171.825 deg ; T2  -- T2   3.2286 A


        T-O-T SUMMARY
          Range  = 119.6028° <--> 180.0000 deg
          Mean   = 158.2930 deg
          StdDev = 24.8355 deg

        T--T SUMMARY
          Range  = 2.8425 A <--> 3.2286 A
          Mean   = 3.1114 A
          StdDev = 0.1721 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 16 30 44 59 82 115 148 170 200 252 306 344 378 439
TD10 = 677
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.12.16_{2}
Weight = 37

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 30 45 65 89 115 142 175 214 255 297 341 393 450
TD10 = 695
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12
Weight = 25

<TD10> = 689.000
Average ring size = 5.6296