Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_2_36_8UX7pP.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 20.40 T-atoms per nm^3
Material density = 2.035 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6218 Angstrom
T1  -- O2  = 1.6244 Angstrom
T1  -- O3  = 1.6203 Angstrom
T1  -- O4  = 1.6202 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007568  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001580  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6231 Angstrom
T2  -- O4  = 1.6212 Angstrom
T2  -- O5  = 1.6222 Angstrom
T2  -- O6  = 1.6228 Angstrom
      mean = 1.6223 Angstrom
        t1 = 0.007938  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001988  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6202 A <--> 1.6244 A
          Mean   = 1.6220 A
          StdDev = 0.0013 A

       t1 Range  = 0.0076 <-- 0.0078 --> 0.0079
       t2 Range  = 0.0016 <-- 0.0018 --> 0.0020

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.334 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.314 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.642 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.056 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.321 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.161 deg; O3  -- O4  = 3 A
       109.161 deg <-- 109.471 deg --> 110.056 deg

O3  -- T2  -- O4  = 109.381 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.058 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.893 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.103 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.609 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.778 deg; O5  -- O6  = 3 A
       109.058 deg <-- 109.470 deg --> 109.893 deg

        O-T-O SUMMARY
          Range  = 109.0581 deg <--> 110.0557 deg
          Mean   = 109.4631 deg
          StdDev = 0.3140 deg

        O--O SUMMARY
          Range  = 2.6408 A <--> 2.6588 A
          Mean   = 2.6485 A
          StdDev = 0.0057 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 148.369 deg; T1  -- T2  = 5.7717 A
T1  - O1  - T1  - O3  - T2  =  89.610 deg; T1  -- T2  = 4.2166 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2107 A
T2  - O2  - T1  - O3  - T2  =  84.176 deg; T2  -- T2  = 4.0530 A
T2  - O2  - T1  - O4  - T1  = 109.091 deg; T2  -- T1  = 4.9023 A
T2  - O3  - T1  - O4  - T1  = 153.217 deg; T2  -- T1  = 5.8395 A

T1  - O3  - T2  - O4  - T1  =  84.581 deg; T1  -- T1  = 4.0688 A
T1  - O3  - T2  - O5  - T2  = 108.190 deg; T1  -- T2  = 4.9062 A
T1  - O3  - T2  - O6  - T2  = 114.202 deg; T1  -- T2  = 5.0026 A
T1  - O4  - T2  - O5  - T2  = 108.287 deg; T1  -- T2  = 4.8967 A
T1  - O4  - T2  - O6  - T2  =  90.390 deg; T1  -- T2  = 4.2166 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.4997 A

        T-T-T SUMMARY
          Range  = 84.1761 deg <--> 153.2172 deg
          Mean   = 106.6754 deg
          StdDev = 22.0494 deg

        T--T SUMMARY
          Range  = 4.0530 A <--> 5.8395 A
          Mean   = 4.7226 A
          StdDev = 0.5982 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.114 deg ; T1  -- T1   2.9871 A

T1  -- O2  -- T1  = 131.978 deg ; T1  -- T1   2.9677 A

T1  -- O3  -- T2  = 138.308 deg ; T1  -- T2   3.0311 A

T1  -- O4  -- T2  = 136.971 deg ; T1  -- T2   3.0156 A

T2  -- O5  -- T2  = 128.853 deg ; T2  -- T2   2.9266 A

T2  -- O6  -- T2  = 137.614 deg ; T2  -- T2   3.0261 A


        T-O-T SUMMARY
          Range  = 128.8535° <--> 138.3082 deg
          Mean   = 134.6397 deg
          StdDev = 3.3897 deg

        T--T SUMMARY
          Range  = 2.9266 A <--> 3.0311 A
          Mean   = 2.9924 A
          StdDev = 0.0369 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 34 57 81 102 128 167 219 276 320 349 392 469 566
TD10 = 820
Circuit symbol = 4.4.4.8_{4}.6.6
Weight = 19
Vertex symbol  = 4.4.4.8_{3}.8.8_{2}
Weight = 23

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 21 35 52 77 108 142 178 212 250 304 369 431 487 539
TD10 = 840
Circuit symbol = 4.6_{2}.4.8_{3}.6.6_{2}
Weight = 15
Vertex symbol  = 4.6_{2}.4.8.6_{2}.8_{2}
Weight = 24

<TD10> = 830.000
Average ring size = 5.9178