Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_139_2_28_niMnj6.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 17.82 T-atoms per nm^3
Material density = 1.778 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6221 Angstrom
T1  -- O2  = 1.6178 Angstrom
T1  -- O3  = 1.6181 Angstrom
T1  -- O4  = 1.6178 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.005941  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001354  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6180 Angstrom
T2  -- O5  = 1.6191 Angstrom
T2  -- O6  = 1.6222 Angstrom
T2  -- O7  = 1.6213 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.006565  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001208  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6178 A <--> 1.6222 A
          Mean   = 1.6195 A
          StdDev = 0.0019 A

       t1 Range  = 0.0059 <-- 0.0063 --> 0.0066
       t2 Range  = 0.0012 <-- 0.0013 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.621 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.356 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.795 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.906 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.450 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.696 deg; O3  -- O4  = 3 A
       108.906 deg <-- 109.471 deg --> 109.795 deg

O4  -- T2  -- O5  = 108.998 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.580 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.606 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.465 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.617 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.561 deg; O6  -- O7  = 3 A
       108.998 deg <-- 109.471 deg --> 109.617 deg

        O-T-O SUMMARY
          Range  = 108.9060 deg <--> 109.7946 deg
          Mean   = 109.4874 deg
          StdDev = 0.2584 deg

        O--O SUMMARY
          Range  = 2.6328 A <--> 2.6506 A
          Mean   = 2.6447 A
          StdDev = 0.0052 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 117.658 deg; T1  -- T1  = 5.2229 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3151 A
T1  - O1  - T1  - O4  - T2  =  97.390 deg; T1  -- T2  = 4.5690 A
T1  - O2  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 5.7563 A
T1  - O2  - T1  - O4  - T2  = 118.500 deg; T1  -- T2  = 5.3376 A
T1  - O3  - T1  - O4  - T2  =  89.359 deg; T1  -- T2  = 4.3654 A

T1  - O4  - T2  - O5  - T2  =  90.641 deg; T1  -- T2  = 4.3654 A
T1  - O4  - T2  - O6  - T2  = 117.473 deg; T1  -- T2  = 5.2391 A
T1  - O4  - T2  - O7  - T2  = 138.417 deg; T1  -- T2  = 5.7933 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.6168 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3470 A
T2  - O6  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.3400 A

        T-T-T SUMMARY
          Range  = 89.3591 deg <--> 138.4167 deg
          Mean   = 108.9565 deg
          StdDev = 18.7110 deg

        T--T SUMMARY
          Range  = 4.3151 A <--> 5.7933 A
          Mean   = 4.9410 A
          StdDev = 0.5713 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.086 deg ; T1  -- T1   2.9872 A

T1  -- O2  -- T1  = 148.821 deg ; T1  -- T1   3.1165 A

T1  -- O3  -- T1  = 148.426 deg ; T1  -- T1   3.1140 A

T1  -- O4  -- T2  = 145.991 deg ; T1  -- T2   3.0943 A

T2  -- O5  -- T2  = 146.708 deg ; T2  -- T2   3.1025 A

T2  -- O6  -- T2  = 138.568 deg ; T2  -- T2   3.0347 A

T2  -- O7  -- T2  = 139.765 deg ; T2  -- T2   3.0448 A


        T-O-T SUMMARY
          Range  = 134.0860° <--> 148.8214 deg
          Mean   = 143.1950 deg
          StdDev = 5.2941 deg

        T--T SUMMARY
          Range  = 2.9872 A <--> 3.1165 A
          Mean   = 3.0706 A
          StdDev = 0.0456 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 10 21 36 53 74 100 129 163 203 245 291 344 399 456 519
TD10 = 794
Circuit symbol = 4.6.4.8_{3}.6_{2}.8_{3}
Weight = 27
Vertex symbol  = 4.6.4.8_{3}.6.8
Weight = 26

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 18 32 50 74 103 133 166 204 245 290 340 392 448 513
TD10 = 794
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

<TD10> = 794.000
Average ring size = 5.6000