Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_138_3_56084852_2RosvL.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 16.94 T-atoms per nm^3
Material density = 1.690 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6195 Angstrom
T1  -- O2  = 1.6114 Angstrom
T1  -- O3  = 1.6183 Angstrom
T1  -- O4  = 1.6186 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.005610  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003723  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6165 Angstrom
T2  -- O5  = 1.6200 Angstrom
T2  -- O6  = 1.6170 Angstrom
T2  -- O3  = 1.6188 Angstrom
      mean = 1.6181 Angstrom
        t1 = 0.005378  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002415  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6210 Angstrom
T3  -- O6  = 1.6210 Angstrom
T3  -- O6  = 1.6210 Angstrom
T3  -- O6  = 1.6210 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.010337  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005969  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6114 A <--> 1.6210 A
          Mean   = 1.6179 A
          StdDev = 0.0027 A

       t1 Range  = 0.0054 <-- 0.0071 --> 0.0103
       t2 Range  = 0.0024 <-- 0.0040 --> 0.0060

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.300 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.029 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.473 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.245 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.822 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.949 deg; O3  -- O4  = 3 A
       108.822 deg <-- 109.470 deg --> 110.029 deg

O4  -- T2  -- O5  = 109.557 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.070 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 109.515 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 109.429 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 109.248 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 110.007 deg; O6  -- O3  = 3 A
       109.070 deg <-- 109.471 deg --> 110.007 deg

O6  -- T3  -- O6  = 111.252 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.588 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.588 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.588 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.588 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 111.252 deg; O6  -- O6  = 3 A
       108.588 deg <-- 109.476 deg --> 111.252 deg

        O-T-O SUMMARY
          Range  = 108.5882 deg <--> 111.2520 deg
          Mean   = 109.4773 deg
          StdDev = 0.7941 deg

        O--O SUMMARY
          Range  = 2.6266 A <--> 2.6759 A
          Mean   = 2.6435 A
          StdDev = 0.0137 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4615 A
T1  - O1  - T1  - O3  - T2  = 122.008 deg; T1  -- T2  = 5.3650 A
T1  - O1  - T1  - O4  - T2  = 116.995 deg; T1  -- T2  = 5.2367 A
T1  - O2  - T1  - O3  - T2  = 130.163 deg; T1  -- T2  = 5.6692 A
T1  - O2  - T1  - O4  - T2  = 125.854 deg; T1  -- T2  = 5.5733 A
T2  - O3  - T1  - O4  - T2  =  75.601 deg; T2  -- T2  = 3.7290 A

T2  - O4  - T2  - O5  - T3  = 127.341 deg; T2  -- T3  = 5.6484 A
T2  - O4  - T2  - O6  - T1  = 129.978 deg; T2  -- T1  = 5.6891 A
T2  - O4  - T2  - O3  - T1  = 125.584 deg; T2  -- T1  = 5.5763 A
T3  - O5  - T2  - O6  - T1  =  91.123 deg; T3  -- T1  = 4.3672 A
T3  - O5  - T2  - O3  - T1  =  91.275 deg; T3  -- T1  = 4.3672 A
T1  - O6  - T2  - O3  - T1  =  76.061 deg; T1  -- T1  = 3.7483 A

T2  - O6  - T3  - O6  - T2  =  74.779 deg; T2  -- T2  = 3.7290 A
T2  - O6  - T3  - O6  - T2  = 129.144 deg; T2  -- T2  = 5.5461 A
T2  - O6  - T3  - O6  - T2  = 129.144 deg; T2  -- T2  = 5.5461 A
T2  - O6  - T3  - O6  - T2  = 129.144 deg; T2  -- T2  = 5.5461 A
T2  - O6  - T3  - O6  - T2  = 129.144 deg; T2  -- T2  = 5.5461 A
T2  - O6  - T3  - O6  - T2  =  74.779 deg; T2  -- T2  = 3.7290 A

        T-T-T SUMMARY
          Range  = 74.7786 deg <--> 130.1625 deg
          Mean   = 109.8923 deg
          StdDev = 22.6966 deg

        T--T SUMMARY
          Range  = 3.7290 A <--> 5.6891 A
          Mean   = 4.9624 A
          StdDev = 0.7841 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.789 deg ; T1  -- T1   3.0958 A

T1  -- O2  -- T1  = 170.918 deg ; T1  -- T1   3.2126 A

T1  -- O3  -- T2  = 140.424 deg ; T1  -- T2   3.0460 A

T1  -- O4  -- T2  = 139.800 deg ; T1  -- T2   3.0380 A

T2  -- O5  -- T2  = 171.540 deg ; T2  -- T2   3.2312 A

T2  -- O6  -- T3  = 142.970 deg ; T2  -- T3   3.0705 A


        T-O-T SUMMARY
          Range  = 139.7998° <--> 171.5401 deg
          Mean   = 151.9069 deg
          StdDev = 13.8722 deg

        T--T SUMMARY
          Range  = 3.0380 A <--> 3.2312 A
          Mean   = 3.1157 A
          StdDev = 0.0779 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 53 77 108 134 161 204 254 303 355 408 464 526
TD10 = 805
Circuit symbol = 4.4_{2}.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 24
Vertex symbol  = 4.4_{2}.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 35 55 75 99 135 174 209 249 298 351 406 465 532
TD10 = 817
Circuit symbol = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29
Vertex symbol  = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29

T3 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 20 36 50 72 104 132 168 218 256 288 340 408 474 536
TD10 = 813
Circuit symbol = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29
Vertex symbol  = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29

<TD10> = 811.222
Average ring size = 6.3051