Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_138_3_56056721_QxHIwq.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 16.86 T-atoms per nm^3
Material density = 1.682 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6191 Angstrom
T1  -- O2  = 1.6109 Angstrom
T1  -- O4  = 1.6188 Angstrom
T1  -- O3  = 1.6201 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.005820  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002531  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6195 Angstrom
T2  -- O5  = 1.6201 Angstrom
T2  -- O6  = 1.6157 Angstrom
T2  -- O4  = 1.6196 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.005521  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001104  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6203 Angstrom
T3  -- O6  = 1.6203 Angstrom
T3  -- O6  = 1.6203 Angstrom
T3  -- O6  = 1.6203 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.010433  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006372  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6109 A <--> 1.6203 A
          Mean   = 1.6182 A
          StdDev = 0.0029 A

       t1 Range  = 0.0055 <-- 0.0073 --> 0.0104
       t2 Range  = 0.0011 <-- 0.0033 --> 0.0064

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.294 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.541 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.977 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.165 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 108.880 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.963 deg; O4  -- O3  = 3 A
       108.880 deg <-- 109.470 deg --> 109.977 deg

O3  -- T2  -- O5  = 109.351 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.813 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.535 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.388 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.410 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.330 deg; O6  -- O4  = 3 A
       109.330 deg <-- 109.471 deg --> 109.813 deg

O6  -- T3  -- O6  = 108.529 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.529 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 111.373 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 111.373 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.529 deg; O6  -- O6  = 3 A
O6  -- T3  -- O6  = 108.529 deg; O6  -- O6  = 3 A
       108.529 deg <-- 109.477 deg --> 111.373 deg

        O-T-O SUMMARY
          Range  = 108.5286 deg <--> 111.3734 deg
          Mean   = 109.4778 deg
          StdDev = 0.8267 deg

        O--O SUMMARY
          Range  = 2.6284 A <--> 2.6766 A
          Mean   = 2.6436 A
          StdDev = 0.0142 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4630 A
T1  - O1  - T1  - O4  - T2  = 119.958 deg; T1  -- T2  = 5.2931 A
T1  - O1  - T1  - O3  - T2  = 119.388 deg; T1  -- T2  = 5.3210 A
T1  - O2  - T1  - O4  - T2  = 127.442 deg; T1  -- T2  = 5.5947 A
T1  - O2  - T1  - O3  - T2  = 128.619 deg; T1  -- T2  = 5.6677 A
T2  - O4  - T1  - O3  - T2  =  75.569 deg; T2  -- T2  = 3.7326 A

T2  - O3  - T2  - O5  - T3  = 127.411 deg; T2  -- T3  = 5.6582 A
T2  - O3  - T2  - O6  - T1  = 128.131 deg; T2  -- T1  = 5.6307 A
T2  - O3  - T2  - O4  - T1  = 127.430 deg; T2  -- T1  = 5.6585 A
T3  - O5  - T2  - O6  - T1  =  91.673 deg; T3  -- T1  = 4.3703 A
T3  - O5  - T2  - O4  - T1  =  90.718 deg; T3  -- T1  = 4.3703 A
T1  - O6  - T2  - O4  - T1  =  76.061 deg; T1  -- T1  = 3.7532 A

T2  - O6  - T3  - O6  - T2  = 129.105 deg; T2  -- T2  = 5.5465 A
T2  - O6  - T3  - O6  - T2  = 129.105 deg; T2  -- T2  = 5.5465 A
T2  - O6  - T3  - O6  - T2  =  74.842 deg; T2  -- T2  = 3.7326 A
T2  - O6  - T3  - O6  - T2  =  74.842 deg; T2  -- T2  = 3.7326 A
T2  - O6  - T3  - O6  - T2  = 129.105 deg; T2  -- T2  = 5.5465 A
T2  - O6  - T3  - O6  - T2  = 129.105 deg; T2  -- T2  = 5.5465 A

        T-T-T SUMMARY
          Range  = 74.8423 deg <--> 129.1046 deg
          Mean   = 109.9145 deg
          StdDev = 22.6563 deg

        T--T SUMMARY
          Range  = 3.7326 A <--> 5.6677 A
          Mean   = 4.9676 A
          StdDev = 0.7848 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.471 deg ; T1  -- T1   3.0924 A

T1  -- O2  -- T1  = 174.474 deg ; T1  -- T1   3.2181 A

T1  -- O3  -- T2  = 142.861 deg ; T1  -- T2   3.0709 A

T1  -- O4  -- T2  = 137.753 deg ; T1  -- T2   3.0208 A

T2  -- O5  -- T2  = 177.504 deg ; T2  -- T2   3.2395 A

T2  -- O6  -- T3  = 143.274 deg ; T2  -- T3   3.0712 A


        T-O-T SUMMARY
          Range  = 137.7534° <--> 177.5039 deg
          Mean   = 153.5562 deg
          StdDev = 16.1376 deg

        T--T SUMMARY
          Range  = 3.0208 A <--> 3.2395 A
          Mean   = 3.1188 A
          StdDev = 0.0814 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 35 53 77 108 134 161 204 254 303 355 408 464 526
TD10 = 805
Circuit symbol = 4.4_{2}.6_{2}.8_{5}.6_{2}.8_{5}
Weight = 24
Vertex symbol  = 4.4_{2}.6_{2}.8_{3}.6_{2}.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 20 35 55 75 99 135 174 209 249 298 351 406 465 532
TD10 = 817
Circuit symbol = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29
Vertex symbol  = 4.8_{3}.4.8_{3}.4.8_{4}
Weight = 29

T3 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 20 36 50 72 104 132 168 218 256 288 340 408 474 536
TD10 = 813
Circuit symbol = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29
Vertex symbol  = 4_{2}.4_{2}.8_{4}.8_{4}.8_{4}.8_{4}
Weight = 29

<TD10> = 811.222
Average ring size = 6.3051