Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_138_2_30857_yThIbK.cif"

There are 20 T-atoms per unit cell
There are 40 O-atoms per unit cell

Framework density = 19.88 T-atoms per nm^3
Material density = 1.984 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6233 Angstrom
T1  -- O2  = 1.6226 Angstrom
T1  -- O3  = 1.6262 Angstrom
T1  -- O1  = 1.6226 Angstrom
      mean = 1.6236 Angstrom
        t1 = 0.008793  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001552  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O3  = 1.6218 Angstrom
T2  -- O3  = 1.6218 Angstrom
      mean = 1.6218 Angstrom
        t1 = 0.007898  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001962  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6218 A <--> 1.6262 A
          Mean   = 1.6233 A
          StdDev = 0.0015 A

       t1 Range  = 0.0079 <-- 0.0083 --> 0.0088
       t2 Range  = 0.0016 <-- 0.0018 --> 0.0020

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.705 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.472 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 108.851 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.833 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.858 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.101 deg; O3  -- O1  = 3 A
       108.851 deg <-- 109.470 deg --> 109.858 deg

O3  -- T2  -- O3  = 108.996 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.301 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.118 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.118 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 109.301 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 108.996 deg; O3  -- O3  = 3 A
       108.996 deg <-- 109.472 deg --> 110.118 deg

        O-T-O SUMMARY
          Range  = 108.8515 deg <--> 110.1185 deg
          Mean   = 109.4710 deg
          StdDev = 0.4296 deg

        O--O SUMMARY
          Range  = 2.6400 A <--> 2.6589 A
          Mean   = 2.6499 A
          StdDev = 0.0072 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 122.774 deg; T1  -- T2  = 5.3115 A
T1  - O1  - T1  - O3  - T1  = 144.392 deg; T1  -- T1  = 5.7361 A
T1  - O1  - T1  - O1  - T1  = 106.198 deg; T1  -- T1  = 4.8178 A
T2  - O2  - T1  - O3  - T1  =  92.384 deg; T2  -- T1  = 4.3314 A
T2  - O2  - T1  - O1  - T1  =  92.384 deg; T2  -- T1  = 4.3314 A
T1  - O3  - T1  - O1  - T1  =  74.860 deg; T1  -- T1  = 3.6322 A

T1  - O3  - T2  - O3  - T1  = 114.453 deg; T1  -- T1  = 5.0681 A
T1  - O3  - T2  - O3  - T1  =  74.112 deg; T1  -- T1  = 3.6322 A
T1  - O3  - T2  - O3  - T1  = 149.296 deg; T1  -- T1  = 5.8125 A
T1  - O3  - T2  - O3  - T1  = 149.296 deg; T1  -- T1  = 5.8125 A
T1  - O3  - T2  - O3  - T1  =  74.112 deg; T1  -- T1  = 3.6322 A
T1  - O3  - T2  - O3  - T1  = 114.453 deg; T1  -- T1  = 5.0681 A

        T-T-T SUMMARY
          Range  = 74.1116 deg <--> 149.2964 deg
          Mean   = 109.0595 deg
          StdDev = 27.3190 deg

        T--T SUMMARY
          Range  = 3.6322 A <--> 5.8125 A
          Mean   = 4.7655 A
          StdDev = 0.8109 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.021 deg ; T1  -- T1   2.9880 A

T1  -- O2  -- T1  = 138.687 deg ; T1  -- T1   3.0366 A

T1  -- O3  -- T2  = 136.222 deg ; T1  -- T2   3.0138 A


        T-O-T SUMMARY
          Range  = 134.0213° <--> 138.6871 deg
          Mean   = 136.3103 deg
          StdDev = 1.9260 deg

        T--T SUMMARY
          Range  = 2.9880 A <--> 3.0366 A
          Mean   = 3.0128 A
          StdDev = 0.0200 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 18 32 50 73 100 130 164 201 242 288 338 393 452 514
TD10 = 782
Circuit symbol = 4.8_{2}.4.8_{2}.4_{2}.6
Weight = 20
Vertex symbol  = 4.8.4.8.4_{2}.6
Weight = 20

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 8 16 32 54 72 96 130 164 200 242 288 340 394 448 512
TD10 = 777
Circuit symbol = 4_{2}.4_{2}.6.6.8_{4}.8_{4}
Weight = 15
Vertex symbol  = 4_{2}.4_{2}.6.6.10_{8}.10_{8}
Weight = 29

<TD10> = 781.000
Average ring size = 5.8140