Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_134_2_6710_CB2WL1.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 17.81 T-atoms per nm^3
Material density = 1.777 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6138 Angstrom
T1  -- O3  = 1.6229 Angstrom
T1  -- O4  = 1.6090 Angstrom
T1  -- O2  = 1.6232 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.005564  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004681  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6103 Angstrom
T2  -- O5  = 1.6175 Angstrom
T2  -- O6  = 1.6185 Angstrom
T2  -- O7  = 1.6184 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.004617  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002493  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6090 A <--> 1.6232 A
          Mean   = 1.6167 A
          StdDev = 0.0050 A

       t1 Range  = 0.0046 <-- 0.0051 --> 0.0056
       t2 Range  = 0.0025 <-- 0.0036 --> 0.0047

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.289 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.977 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.293 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.873 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.497 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.895 deg; O4  -- O2  = 3 A
       108.977 deg <-- 109.471 deg --> 109.895 deg

O4  -- T2  -- O5  = 109.547 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.162 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.155 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.562 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.554 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.846 deg; O6  -- O7  = 3 A
       109.155 deg <-- 109.471 deg --> 109.846 deg

        O-T-O SUMMARY
          Range  = 108.9771 deg <--> 109.8948 deg
          Mean   = 109.4587 deg
          StdDev = 0.3165 deg

        O--O SUMMARY
          Range  = 2.6234 A <--> 2.6508 A
          Mean   = 2.6386 A
          StdDev = 0.0082 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.2020 A
T1  - O1  - T1  - O4  - T1  =  90.004 deg; T1  -- T1  = 4.3868 A
T1  - O1  - T1  - O2  - T2  = 131.741 deg; T1  -- T2  = 5.6504 A
T1  - O3  - T1  - O4  - T1  =  89.996 deg; T1  -- T1  = 4.3868 A
T1  - O3  - T1  - O2  - T2  = 131.731 deg; T1  -- T2  = 5.6506 A
T1  - O4  - T1  - O2  - T2  = 109.705 deg; T1  -- T2  = 5.2712 A

T1  - O4  - T2  - O5  - T2  = 120.571 deg; T1  -- T2  = 5.5194 A
T1  - O4  - T2  - O6  - T2  = 120.564 deg; T1  -- T2  = 5.5195 A
T1  - O4  - T2  - O7  - T2  = 109.705 deg; T1  -- T2  = 5.2776 A
T2  - O5  - T2  - O6  - T2  =  83.167 deg; T2  -- T2  = 4.1625 A
T2  - O5  - T2  - O7  - T2  = 110.182 deg; T2  -- T2  = 5.2246 A
T2  - O6  - T2  - O7  - T2  = 110.172 deg; T2  -- T2  = 5.2246 A

        T-T-T SUMMARY
          Range  = 83.1675 deg <--> 131.7409 deg
          Mean   = 107.6712 deg
          StdDev = 14.9860 deg

        T--T SUMMARY
          Range  = 4.1625 A <--> 5.6506 A
          Mean   = 5.0465 A
          StdDev = 0.5358 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.381 deg ; T1  -- T1   3.2273 A

T1  -- O2  -- T1  = 132.505 deg ; T1  -- T1   2.9715 A

T1  -- O3  -- T1  = 132.521 deg ; T1  -- T1   2.9711 A

T1  -- O4  -- T2  = 179.832 deg ; T1  -- T2   3.2193 A

T2  -- O5  -- T2  = 179.847 deg ; T2  -- T2   3.2351 A

T2  -- O6  -- T2  = 151.229 deg ; T2  -- T2   3.1356 A

T2  -- O7  -- T2  = 151.316 deg ; T2  -- T2   3.1360 A


        T-O-T SUMMARY
          Range  = 132.5046° <--> 179.8467 deg
          Mean   = 157.9473 deg
          StdDev = 19.9422 deg

        T--T SUMMARY
          Range  = 2.9711 A <--> 3.2351 A
          Mean   = 3.1280 A
          StdDev = 0.1066 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 37 59 82 110 143 179 221 268 318 374 437 502 567
TD10 = 864
Circuit symbol = 4.6_{2}.4.8_{4}.4.8_{4}
Weight = 27
Vertex symbol  = 4.6_{2}.4.8_{2}.4.8_{2}
Weight = 27

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 37 57 80 109 143 181 225 270 320 375 433 498 567
TD10 = 870
Circuit symbol = 4.8_{2}.6.6_{3}.6.6_{3}
Weight = 26
Vertex symbol  = 4.8_{2}.6.6_{3}.6.6_{3}
Weight = 26

<TD10> = 867.000
Average ring size = 5.8537