Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_133_2_202240_qel84M.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.41 T-atoms per nm^3
Material density = 1.937 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5895 Angstrom
T1  -- O2  = 1.5903 Angstrom
T1  -- O3  = 1.5694 Angstrom
T1  -- O4  = 1.6108 Angstrom
      mean = 1.5900 Angstrom
        t1 = 0.104549  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.082599  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6107 Angstrom
T2  -- O5  = 1.6584 Angstrom
T2  -- O6  = 1.6458 Angstrom
T2  -- O6  = 1.6433 Angstrom
      mean = 1.6395 Angstrom
        t1 = 0.027070  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017595  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5694 A <--> 1.6584 A
          Mean   = 1.6148 A
          StdDev = 0.0297 A

       t1 Range  = 0.0271 <-- 0.0658 --> 0.1045
       t2 Range  = 0.0176 <-- 0.0501 --> 0.0826

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 122.607 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 118.766 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  89.751 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 118.627 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  89.757 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  =  90.512 deg; O3  -- O4  = 2 A
       89.751 deg <-- 105.003 deg --> 122.607 deg

O4  -- T2  -- O5  = 107.475 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.386 deg; O4  -- O6  = 3 A
O4  -- T2  -- O6  = 106.959 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 112.388 deg; O5  -- O6  = 3 A
O5  -- T2  -- O6  = 111.913 deg; O5  -- O6  = 3 A
O6  -- T2  -- O6  = 110.420 deg; O6  -- O6  = 3 A
       106.959 deg <-- 109.423 deg --> 112.388 deg

        O-T-O SUMMARY
          Range  = 89.7513 deg <--> 122.6073 deg
          Mean   = 105.3867 deg
          StdDev = 10.5567 deg

        O--O SUMMARY
          Range  = 2.2580 A <--> 2.7893 A
          Mean   = 2.5663 A
          StdDev = 0.2010 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.200 deg; T1  -- T2  = 4.5045 A
T1  - O1  - T1  - O3  - T1  = 134.989 deg; T1  -- T1  = 5.7198 A
T1  - O1  - T1  - O4  - T1  = 135.011 deg; T1  -- T1  = 5.7195 A
T2  - O2  - T1  - O3  - T1  =  88.636 deg; T2  -- T1  = 4.3837 A
T2  - O2  - T1  - O4  - T1  =  91.081 deg; T2  -- T1  = 4.4777 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3161 A

T1  - O4  - T2  - O5  - T2  = 106.985 deg; T1  -- T2  = 5.2482 A
T1  - O4  - T2  - O6  - T2  = 106.696 deg; T1  -- T2  = 5.1447 A
T1  - O4  - T2  - O6  - T2  = 109.152 deg; T1  -- T2  = 5.2255 A
T2  - O5  - T2  - O6  - T2  = 121.522 deg; T2  -- T2  = 5.6738 A
T2  - O5  - T2  - O6  - T2  = 125.505 deg; T2  -- T2  = 5.7807 A
T2  - O6  - T2  - O6  - T2  =  84.614 deg; T2  -- T2  = 4.2980 A

        T-T-T SUMMARY
          Range  = 84.6136 deg <--> 135.0109 deg
          Mean   = 107.3788 deg
          StdDev = 17.1954 deg

        T--T SUMMARY
          Range  = 4.2980 A <--> 5.7807 A
          Mean   = 5.0655 A
          StdDev = 0.5770 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.554 deg ; T1  -- T1   3.0524 A

T1  -- O2  -- T1  = 147.232 deg ; T1  -- T1   3.0515 A

T1  -- O3  -- T1  = 180.000 deg ; T1  -- T1   3.1388 A

T1  -- O4  -- T2  = 176.492 deg ; T1  -- T2   3.2199 A

T2  -- O5  -- T2  = 172.303 deg ; T2  -- T2   3.3092 A

T2  -- O6  -- T2  = 152.180 deg ; T2  -- T2   3.1927 A


        T-O-T SUMMARY
          Range  = 147.2316° <--> 180.0000 deg
          Mean   = 162.6268 deg
          StdDev = 13.9837 deg

        T--T SUMMARY
          Range  = 3.0515 A <--> 3.3092 A
          Mean   = 3.1608 A
          StdDev = 0.0924 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2580 A
O1  -- O4  = 2.2580 A
O2  -- O4  = 2.2588 A
O2  -- O4  = 2.2588 A
O3  -- O4  = 2.2589 A
O3  -- O4  = 2.2589 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 915.000
Average ring size = 5.7391