Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_133_1_9_c4RTFT.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 29.04 T-atoms per nm^3
Material density = 2.897 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6631 Angstrom
T1  -- O2  = 1.6557 Angstrom
T1  -- O3  = 1.6631 Angstrom
T1  -- O4  = 1.5800 Angstrom
      mean = 1.6405 Angstrom
        t1 = 0.134061  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.085358  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5800 A <--> 1.6631 A
          Mean   = 1.6405 A
          StdDev = 0.0353 A

       t1 Range  = 0.1341 <-- 0.1341 --> 0.1341
       t2 Range  = 0.0854 <-- 0.0854 --> 0.0854

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.439 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.841 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 127.508 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 134.705 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  75.101 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  =  98.110 deg; O3  -- O4  = 2 A
       75.101 deg <-- 109.117 deg --> 134.705 deg

        O-T-O SUMMARY
          Range  = 75.1006 deg <--> 134.7049 deg
          Mean   = 109.1172 deg
          StdDev = 19.6923 deg

        O--O SUMMARY
          Range  = 1.9730 A <--> 3.0629 A
          Mean   = 2.6376 A
          StdDev = 0.3561 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 124.091 deg; T1  -- T1  = 5.7217 A
T1  - O1  - T1  - O3  - T1  =  83.048 deg; T1  -- T1  = 3.8530 A
T1  - O1  - T1  - O4  - T1  = 121.838 deg; T1  -- T1  = 5.3203 A
T1  - O2  - T1  - O3  - T1  =  73.772 deg; T1  -- T1  = 3.6068 A
T1  - O2  - T1  - O4  - T1  =  84.455 deg; T1  -- T1  = 4.2059 A
T1  - O3  - T1  - O4  - T1  = 153.865 deg; T1  -- T1  = 5.4032 A

        T-T-T SUMMARY
          Range  = 73.7716 deg <--> 153.8650 deg
          Mean   = 106.8449 deg
          StdDev = 28.8637 deg

        T--T SUMMARY
          Range  = 3.6068 A <--> 5.7217 A
          Mean   = 4.6852 A
          StdDev = 0.8332 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.406 deg ; T1  -- T1   3.3169 A

T1  -- O2  -- T1  = 104.595 deg ; T1  -- T1   2.6200 A

T1  -- O3  -- T1  = 123.237 deg ; T1  -- T1   2.9264 A

T1  -- O4  -- T1  = 180.000 deg ; T1  -- T1   3.1600 A


        T-O-T SUMMARY
          Range  = 104.5945° <--> 180.0000 deg
          Mean   = 144.8094 deg
          StdDev = 31.9856 deg

        T--T SUMMARY
          Range  = 2.6200 A <--> 3.3169 A
          Mean   = 3.0058 A
          StdDev = 0.2646 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O4  = 1.9730 A
O2  -- O4  = 1.9730 A
T1  -- T1  = 2.6200 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 24 44 78 111 158 209 269 334 407 481 570 661 762 870
TD10 = 1242
Circuit symbol = 4.7_{3}.4.7_{4}.6.7
Weight = 19
Vertex symbol  = 4.7_{3}.4.7_{4}.7.7_{3}
Weight = 25

<TD10> = 1242.000
Average ring size = 6.2759