Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_131_5_6280783_NLRw6r.cif"

There are 80 T-atoms per unit cell
There are 160 O-atoms per unit cell

Framework density = 24.38 T-atoms per nm^3
Material density = 2.433 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6223 Angstrom
T1  -- O2  = 1.7278 Angstrom
T1  -- O3  = 1.5620 Angstrom
T1  -- O4  = 1.8071 Angstrom
      mean = 1.6798 Angstrom
        t1 = 0.094981  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.072633  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.7829 Angstrom
T2  -- O5  = 1.7351 Angstrom
T2  -- O6  = 1.5988 Angstrom
T2  -- O7  = 1.6208 Angstrom
      mean = 1.6844 Angstrom
        t1 = 0.082630  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050215  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6029 Angstrom
T3  -- O8  = 1.6296 Angstrom
T3  -- O9  = 1.5463 Angstrom
T3  -- O10 = 1.6387 Angstrom
      mean = 1.6043 Angstrom
        t1 = 0.050826  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.054990  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6186 Angstrom
T4  -- O11 = 1.6339 Angstrom
T4  -- O12 = 1.5785 Angstrom
T4  -- O13 = 1.6385 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.029466  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028879  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O13 = 1.6204 Angstrom
T5  -- O14 = 1.6233 Angstrom
T5  -- O15 = 1.5649 Angstrom
T5  -- O16 = 1.6073 Angstrom
      mean = 1.6040 Angstrom
        t1 = 0.041111  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039580  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5463 A <--> 1.8071 A
          Mean   = 1.6380 A
          StdDev = 0.0692 A

       t1 Range  = 0.0295 <-- 0.0598 --> 0.0950
       t2 Range  = 0.0289 <-- 0.0493 --> 0.0726

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.074 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.306 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.057 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  99.717 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 128.553 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 101.600 deg; O3  -- O4  = 3 A
       99.717 deg <-- 108.885 deg --> 128.553 deg

O4  -- T2  -- O5  = 126.925 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 101.861 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 103.848 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 107.223 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.064 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 107.663 deg; O6  -- O7  = 3 A
       101.861 deg <-- 109.264 deg --> 126.925 deg

O6  -- T3  -- O8  = 116.154 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 100.812 deg; O6  -- O9  = 2 A
O6  -- T3  -- O10 = 113.989 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 101.889 deg; O8  -- O9  = 2 A
O8  -- T3  -- O10 = 114.538 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 107.144 deg; O9  -- O10 = 3 A
       100.812 deg <-- 109.088 deg --> 116.154 deg

O7  -- T4  -- O11 = 112.239 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 105.551 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 112.617 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 107.016 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 113.224 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 105.477 deg; O12 -- O13 = 3 A
       105.477 deg <-- 109.354 deg --> 113.224 deg

O13 -- T5  -- O14 = 119.429 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 102.858 deg; O13 -- O15 = 2 A
O13 -- T5  -- O16 = 110.792 deg; O13 -- O16 = 3 A
O14 -- T5  -- O15 = 102.832 deg; O14 -- O15 = 2 A
O14 -- T5  -- O16 = 110.415 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 109.593 deg; O15 -- O16 = 3 A
       102.832 deg <-- 109.320 deg --> 119.429 deg

        O-T-O SUMMARY
          Range  = 99.7167 deg <--> 128.5532 deg
          Mean   = 109.6280 deg
          StdDev = 7.2685 deg

        O--O SUMMARY
          Range  = 2.4270 A <--> 3.1847 A
          Mean   = 2.6824 A
          StdDev = 0.1724 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 155.148 deg ; T1  -- T1   3.1685 A

T1  -- O2  -- T1  = 129.800 deg ; T1  -- T1   3.1293 A

T1  -- O3  -- T1  = 163.796 deg ; T1  -- T1   3.0928 A

T1  -- O4  -- T2  = 132.967 deg ; T1  -- T2   3.2918 A

T2  -- O5  -- T2  = 133.147 deg ; T2  -- T2   3.1842 A

T2  -- O6  -- T3  = 141.154 deg ; T2  -- T3   3.0195 A

T2  -- O7  -- T4  = 134.196 deg ; T2  -- T4   2.9840 A

T3  -- O8  -- T3  = 117.361 deg ; T3  -- T3   2.7842 A

T3  -- O9  -- T3  = 162.182 deg ; T3  -- T3   3.0552 A

T3  -- O10 -- T3  = 127.820 deg ; T3  -- T3   2.9434 A

T4  -- O11 -- T4  = 128.178 deg ; T4  -- T4   2.9393 A

T4  -- O12 -- T4  = 161.199 deg ; T4  -- T4   3.1147 A

T4  -- O13 -- T5  = 122.632 deg ; T4  -- T5   2.8590 A

T5  -- O14 -- T5  = 115.969 deg ; T5  -- T5   2.7528 A

T5  -- O15 -- T5  = 134.751 deg ; T5  -- T5   2.8889 A

T5  -- O16 -- T5  = 173.785 deg ; T5  -- T5   3.2099 A


        T-O-T SUMMARY
          Range  = 115.9691° <--> 173.7851 deg
          Mean   = 139.6303 deg
          StdDev = 17.3892 deg

        T--T SUMMARY
          Range  = 2.7528 A <--> 3.2918 A
          Mean   = 3.0261 A
          StdDev = 0.1523 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.1685 Angstrom
  T1  -- T2  = 3.2918 Angstrom
  T1  -- T4  = 3.2614 Angstrom
  T1  -- T1  = 3.0928 Angstrom
  T1  -- T1  = 3.1293 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T2  = 3.0195 Angstrom
  T3  -- T3  = 3.0552 Angstrom
  T3  -- T3  = 2.9434 Angstrom
  T3  -- T5  = 3.3290 Angstrom
  T3  -- T3  = 2.7842 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 3.2614 Angstrom
  T4  -- T2  = 2.9840 Angstrom
  T4  -- T4  = 3.1147 Angstrom
  T4  -- T5  = 2.8590 Angstrom
  T4  -- T4  = 2.9393 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T3  = 3.3290 Angstrom
  T5  -- T4  = 2.8590 Angstrom
  T5  -- T5  = 3.2099 Angstrom
  T5  -- T5  = 2.8889 Angstrom
  T5  -- T5  = 2.7528 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 37 59 83 119 173 229 270 315 399 505 584 653 765
TD10 = 1003
Circuit symbol = 4.6.4.8.4.8
Weight = 11
Vertex symbol  = 4.6.4.10_{2}.4.12_{3}
Weight = 38

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 18 29 54 91 124 156 206 279 352 404 462 565 682 758
TD10 = 972
Circuit symbol = 4.6.4.10_{5}.6.8_{4}
Weight = 21
Vertex symbol  = 4.6.4.10.8_{2}.12_{2}
Weight = 30

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 15 30 53 83 123 172 222 272 339 431 518 575 635 745
TD10 = 983
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.10.4.12_{5}
Weight = 34

T4 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 13 20 33 62 105 144 179 234 313 386 444 526 643 741
TD10 = 803
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.14
Weight = 22

T5 (Si): multiplicity = 16
Coordination Sequence =
    1 4 7 9 14 25 44 80 135 187 223 271 355 446 511 583 706
TD10 = 729
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.14
Weight = 21

<TD10> = 898.000
Average ring size = 5.8857